Pouring material for slag stopping wall and slag stopping wall

A slag retaining wall and castable technology, which is applied to casting molten material containers, manufacturing tools, metal processing equipment, etc., can solve the problems of not achieving the best thermal strength, affecting the use of tundish, and low strength of the slag retaining wall, etc. Achieve the effect of low cost, good absorption, good thermal shock resistance

Active Publication Date: 2014-05-07
ANHUI SAFE ELECTRONICS
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is that the slag retaining wall formed by mixing magnesia and corundum sand has low strength, cannot achieve the best thermal strength, and has a low service life, which affects the use of the tundish, thereby providing the slag retaining wall castable and slag retaining wall

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pouring material for slag stopping wall and slag stopping wall
  • Pouring material for slag stopping wall and slag stopping wall

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The castable for the slag retaining wall is composed of the following components in weight percentage: 12.7% of 8-20mm bauxite, 12.9% of 5-8mm bauxite, 14.5% of 3-5mm bauxite, 15.8% of 1-3mm bauxite, 0~ 12.8% of 1mm bauxite, 13.6% of bauxite with a particle size of 200 mesh, 3.3% of 0-1mm magnesia, 8.35% of magnesia with a particle size of 200 mesh, 4.35% of silicon micropowder, 1.5% of steel fiber, 0.1% of sodium hexametaphosphate, explosion-proof Fiber 0.1%.

Embodiment 2

[0021] The castable for the slag retaining wall is composed of the following components in weight percentage: 12% of 8-20mm bauxite, 12% of 5-8mm bauxite, 20% of 3-5mm bauxite, 15% of 1-3mm bauxite, 0-3mm bauxite 12% 1mm bauxite, 12.5% ​​bauxite with a particle size of 200 mesh, 3% magnesia with a particle size of 200 mesh, 8% magnesia with a particle size of 200 mesh, 4% silicon powder, 1.4% steel fiber, 0.06% sodium hexametaphosphate, explosion-proof Fiber 0.04%.

Embodiment 3

[0023] The castable for the slag retaining wall is composed of the following components in weight percentage: 11.2% of 8-20mm bauxite, 11.3% of 5-8mm bauxite, 25.5% of 3-5mm bauxite, 14.4% of 1-3mm bauxite, 0~ 10.9% 1mm bauxite, 11.7% bauxite with a particle size of 200 mesh, 2.7% magnesia with a particle size of 0-1mm, 7.65% magnesia with a particle size of 200 mesh, 3.65% silicon micropowder, and 1% steel fiber.

[0024] Al in the 8-20mm bauxite 2 o 3 content, Al in 5 ~ 8mm bauxite 2 o 3 content, Al in 3~5mm bauxite 2 o 3 content, Al in 1 ~ 3mm bauxite 2 o 3 content, Al in 0~1mm bauxite 2 o 3 content, Al in bauxite with a particle size of 200 mesh 2 o 3 The content of MgO in the 0-1mm magnesia and the MgO content in the magnesia with a particle size of 200 mesh are all equal to 88%. 95%, so that the magnesia has the characteristics of bending resistance, pressure resistance, high strength, etc., and improves the strength and bending resistance of the slag retainin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a pouring material for a slag stopping wall. The pouring material consists of the following components: 8mm to 20mm alumina, 5mm to 8mm alumina, 3mm to 5mm alumina, 1mm to 3mm alumina, 0 to 1mm alumina, alumina with the granularity of 200 meshes, 0 to 1mm magnesium sand, magnesium sand with the granularity of 200 meshes, silicon micro powder, steel fiber, sodium hexametaphosphate and explosion-proof fibers. The slag stopping wall which is prepared by mixing the components comprises a plane wall body and slope wall bodies which are arranged on two sides of the plane wall body, wherein the bottom end of the plane wall body is provided with at least one flow steel hole, the top end of each slope wall body is provided with at least one suspension ring, and an arc chamfer angle is arranged on the junction of the plane wall body and the slope wall body. The slag stopping wall has the advantages that the slag stopping wall which is prepared by mixing the components is good in thermal shock resistance, optimal in hot strength under the working temperature, effective for absorbing Al2O3 in impurities, low in cost and good in service life.

Description

technical field [0001] The invention relates to a pouring material for a slag retaining wall and a slag retaining wall. Background technique [0002] In the process of iron and steel smelting, due to the uneven flow of molten steel in the tundish, some places are fast and some places are slow, especially there is an inactive stagnant zone of molten steel in the bottom area of ​​the tundish, which makes it difficult for inclusions to float up, and molten steel in the tundish The actual average residence time is shorter than the theoretical average residence time. In order to fully and effectively utilize the volume of the tundish and promote the floating of debris, a slag retaining wall is added to the tundish. Most of the existing castables for slag retaining walls use magnesia It is mixed with corundum sand, so that the strength of the slag retaining wall after the manufacture is low, the best thermal strength cannot be achieved, the service life is low, and the dead zone a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66B22D41/00
Inventor 李开胜
Owner ANHUI SAFE ELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com