Al-Fe-Cu-Zn aluminum alloy for automobile wire and wire harness thereof

A technology of al-fe-cu-zn and automotive wiring harness, which is applied in the field of aluminum alloy, can solve problems such as shedding, and achieve the effect of overcoming the problem of processing performance and realizing light weight

Pending Publication Date: 2014-04-30
ANHUI JOY SENSE CABLE
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the wires of the electric wiring body of the mobile body are riveted to the terminals, and if creep occurs, there is a risk of falling off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Al-Fe-Cu-Zn aluminum alloy for automobile wire and wire harness thereof
  • Al-Fe-Cu-Zn aluminum alloy for automobile wire and wire harness thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] An aluminum alloy for automotive wires, the components and weight percentages of each component are as follows (total weight: 1T):

[0040] components

Fe

Cu

Zn

Si

RE

Al

Weight (Kg)

2

0.1

0.01

/

/

997.89

Weight percentage (%)

0.2

0.01

0.001

/

/

99.789

[0041] In the above-mentioned aluminum alloy materials, it is preferable to add a certain amount of Zn. The addition of Zn will slightly reduce the electrical conductivity of the aluminum alloy, but can effectively improve the strength to a certain extent, and at the same time improve the creep rate of the conductor.

[0042] The method for preparing an aluminum alloy wire core by using the above-mentioned aluminum alloy material, the specific steps are as follows:

[0043] a. Melting and casting: add aluminum alloy components according to the above ratio, melt at 730°C, cast ingots at 670°C, and then roll into alloy rods...

Embodiment 2

[0048] An aluminum alloy for automotive wires, the components and weight percentages of each component are as follows (total weight: 1T):

[0049]

[0050] Among the above-mentioned aluminum alloy materials, the content of Si was compared. An appropriate amount of Si can increase the recrystallization temperature and refine the grains, while exceeding a certain content will reduce its electrical conductivity. In the process of implementation, it was found that the Si content Excessive samples are prone to breakage during the wire drawing process.

[0051] The method for preparing an aluminum alloy wire core by using the above-mentioned aluminum alloy material, the specific steps are as follows:

[0052] a. Melting and casting: add aluminum alloy components according to the above ratio, melt at 730°C, cast ingots at 670°C, and then roll into alloy rods after solution treatment and aging treatment. The aging treatment here is preferably at 140°C or at higher temperatures,

...

Embodiment 3

[0057] An aluminum alloy for automotive wires, the components and weight percentages of each component are as follows (total weight: 1T):

[0058]

[0059] In the above-mentioned aluminum alloy materials, it is preferable to add a certain amount of RE elements, wherein Ce and La account for 56% of the total RE content, and rare earths can significantly improve the electrical properties of the alloy. In the present invention, rare earths are added to the aluminum alloy to make the aluminum alloy melt and cast Increase the supercooling of the composition, refine the grain, reduce the secondary grain distance, reduce the gas and inclusions in the alloy, and make the inclusion phase tend to be spheroidized. It can also reduce the surface tension of the melt, increase the fluidity, and is conducive to casting into ingots. It has a significant impact on the process performance, and can also improve the fatigue resistance of the alloy and prolong the service life of the cable. Ce a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Conductivityaaaaaaaaaa
Average creep speedaaaaaaaaaa
Conductivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an Al-Fe-Cu-Zn aluminum alloy for an automobile wire, a preparation method thereof and an automobile wire harness prepared by using the Al-Fe-Cu-Zn aluminum alloy. The Al-Fe-Cu-Zn aluminum alloy for the automobile wire comprises the following components: 0.2-1.4wt% of Fe, 0.01-0.5wt% of Cu, 0.001-0.2wt% of Zn and the balance of Al and inevitable impurities. According to the Al-Fe-Cu-Zn aluminum alloy disclosed by the invention, by adding Fe, the mechanical strength and tensile properties of the alloy can be improved, and Fe can also obviously improve the high-temperature creep resistance and improve the anti-fatigue performance of the alloy; by adding Cu, the strength and high-temperature creep property of the alloy can be improved, and the anti-fatigue performance can be improved; by adding Zn, the electrical conductivity of the aluminum alloy can be slightly reduced, the strength can be effectively improved to a certain extent, and the creep rate of a conductor is simultaneously improved.

Description

technical field [0001] The invention relates to a wire harness that can be used as a storage battery cable in a mobile carrier, a wire harness or a cable for an engine, and belongs to the field of aluminum alloys. Background technique [0002] At present, the automobile industry is developing rapidly in the world. The automobile industry has not only become the pillar industry of developed countries such as the United States and Japan, but also some developing countries including China. As one of the important supporting products of automobiles, the automobile line, no matter It has a good market prospect in terms of scale output and variety demand. [0003] At the same time, automobiles are developing in the direction of miniaturization and light weight, the control circuits of various electronic devices are increasing, and the wiring positions in motor vehicles are increasing. Therefore, in order to reduce weight, attempts have been made to use aluminum electric wires who...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C21/00H01B1/02
Inventor 林泽民
Owner ANHUI JOY SENSE CABLE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com