Preparation method of PETG (polyethylene terephthalate glycol) encapsulated wire
A technology of coating wire and coating, which is applied to the device, coating, pretreatment surface and other directions of coating liquid on the surface. Strong focus, not easy to scratch off, smooth surface effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0026] Weigh 75kg of PET and 25kg of PEG400, add them into the reactor, start stirring when the temperature reaches 150°C, stop heating when the temperature reaches 200°C, and continue stirring for 45 minutes; when the liquid in the reactor cools to 15°C, add 25g of Basonat HB195 into it, Stir for 50 minutes to obtain PETG glue.
[0027] Use the prepared PETG glue solution to wrap the metal wire.
[0028] Put the prepared PETG glue into the stuffing box of the extruder, let it out, and the released metal wire penetrates into the mold, and the glue is squeezed into the glue coating chamber by the pressure of the extruder screw for encapsulation. The temperature of the glue room is 40°C; the glue-covering stage adopts a horizontal extruder, and the extrusion speed is 350-400 m / min; The length of the oven is 3m, the temperature is 780°C, the time for the metal wire to stay in the oven is 0.1-0.2 seconds; the baked wire is sent into the cooling cabin for cooling, and the temperat...
Embodiment 2
[0031] Weigh 75kg of PET and 25kg of PEG1000, add them into the reactor, start stirring when the temperature reaches 150°C, stop heating when the temperature reaches 200°C, and continue stirring for 45 minutes; when the liquid in the reactor cools to 15°C, add 30g of Basonat HB195 into it, Stir for 50 minutes to obtain PETG glue.
[0032] The PETG glue solution was used to encapsulate the metal wire according to the method in Example 1.
Embodiment 3
[0034] Weigh 80kgPET and 20kgPEG1000, put them into the reactor, start stirring when the temperature rises to 150°C, stop heating when the temperature reaches 200°C, and continue stirring for 45min; Stir for 50 minutes to obtain the bottom material; add 10kg of titanium dioxide to the bottom material, stir for 40 minutes, and set aside for later use.
[0035] The PETG glue solution was used to encapsulate the metal wire according to the method in Example 1.
[0036] The technical indicators that the metal wire covered wire can achieve:
[0037] Test items index standard Adhesion (scraping and peeling) ≤0.5cm GB9286-98 Film thickness (μm) ≥6 GB1764-89 Impact resistance(cm) 50 GB1732-93 Water resistance (25℃,h) ≥120 GB1733-93 Salt spray resistance (h) ≥200 GB1771-91 Fineness(mm) ≤20 GB1724-89 Hardness (Pencil) ≥2H GB6739-96 Viscosity (Tu-4 cups) (s) ≥120 GB1723-93 Flow drying temperature 120°C ≦1...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com