High definition print processing method for surface of cementum plate and cementum plate with prints

A processing method and a quality board technology are applied in the field of building decoration materials to achieve the effects of low preparation cost, high simulation degree and relatively low preparation cost

Inactive Publication Date: 2014-04-02
FOSHAN ARTECH PANEL
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a high-definition spray painting treatment method on the surface of cementitious boards and cementitious boards with spray painting. And UV ink can be well attached to the surface of the cement board to form a high-definition inkjet color pattern, and the pattern has many advantages such as not easy to fall off, wear-resistant, non-combustible, easy to clean, high simulation, non-toxic, acid and alkali resistance, etc. Solve the problem that the cement board in the prior art cannot be used for high-definition inkjet to form high-definition color patterns

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High definition print processing method for surface of cementum plate and cementum plate with prints
  • High definition print processing method for surface of cementum plate and cementum plate with prints

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] Take a calcium silicate board, sand its surface, and apply a layer of back primer 20g / m on the back of the calcium silicate board 2 , dry and solidify; then apply a layer of penetrating primer 75g / m on the front 2 , dry and solidify; putty treatment again; and then a layer of sealing primer 50g / m 2 , drying and curing; sanding treatment; and then a layer of white primer 100 g / m 2 , drying and curing; sanding treatment; and then a layer of super white paint 20mg / m 2 , dry and solidify. Spray a coat of UV color paint on top of the super white paint layer and let it dry.

[0055] Take a calcium silicate board with inkjet painting, and put a layer of UV high-gloss varnish 90 g / m on the inkjet layer 2 , dry and solidify.

[0056] Take another calcium silicate board with spray painting, and put a layer of UV matte varnish 15 g / m on the spray painting layer 2 , dry and solidify.

[0057] The hardness, color parameters, etc. were tested respectively, and the results are ...

Embodiment 2

[0059] Take a fiber cement board, sand its surface, and apply a layer of back primer 30g / m on the back of the fiber cement board 2 , dry and solidify; then apply a layer of penetrating primer 60g / m on the front 2 , dry and solidify; putty treatment again; and then a layer of sealing primer 55g / m 2 , drying and curing; sanding treatment; and then a layer of white primer 90 g / m 2 , drying and curing; sanding treatment; and then a layer of super white paint 25mg / m 2 , dry and solidify. On the ultra-white paint layer, apply UV flat-panel printing equipment, use UV ink to spray-paint it, and wait for it to dry.

[0060] Take a piece of fiber cement board with inkjet painting, and put a layer of UV high-gloss varnish 100g / m on the inkjet layer 2 , dry and solidify.

[0061] On another piece of fiber cement with inkjet painting, put a layer of UV matte varnish 15g / m on the inkjet layer 2 , dry and solidify.

[0062] The hardness, color parameters, etc. were tested respectively...

Embodiment 3

[0064] Take a fiber cement pressure board, sand its surface, and apply a layer of back primer 25g / m on the back of the fiber cement pressure board 2 , dry and solidify; then apply a layer of penetrating primer 80g / m on the front 2 , dry and solidify; putty treatment again; and then a layer of sealing primer 60g / m 2 , drying and curing; sanding treatment; and then a layer of white primer 80 g / m 2 , drying and curing; sanding treatment; and then a layer of super white paint 30mg / m 2 , dry and solidify. On the ultra-white paint layer, apply UV flat-panel printing equipment, use UV ink to spray-paint it, and wait for it to dry and solidify.

[0065] Take a fiber cement pressure plate with inkjet painting, and put a layer of UV high-gloss varnish 95g / m on the inkjet layer 2 , dry and solidify.

[0066] On another piece of fiber cement with inkjet painting, apply a layer of UV matte varnish 20g / m on the inkjet layer 2 , dry and solidify.

[0067] The hardness, color parameter...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high definition print processing method for the surface of a cementum plate and the cementum plate with prints. The processing method comprises the following steps: sanding the cementum plate: a layer of permeable primer is painted on the front of the cementum plate; processing putty; painting a layer of seal undercoat; sanding processing; painting a layer of white primer; sanding processing; painting a layer of super-white paint. The surface of the cementum plate is subjected to special pretreatment, thus colored paint and ink can be stuck on the surface of the cementum plate, and the surface of the cementum plate is provided with a variety of colors, figures or patterns, and the patterns are not easy to fall off. Therefore the cementum plate with the prints is wear-resisting, ageing resistant, not susceptible to pollution and waterproof, and has good fire prevention performance. The cementum plate with the prints is suitable for decorating the indoor wall face. The cementum plate is provided with the fire-prevention, tough, impact resistant and environment-friendly performances of the cementum plate as well as the decoration effects of high imitation wood grain, marbling, personalized patterns, and the preparation cost is lower.

Description

technical field [0001] The invention relates to the field of building decoration materials, in particular to a high-definition inkjet treatment method on the surface of a cement board and a cement board with inkjet. Background technique [0002] Nowadays, people's material living standards are gradually improving, and the requirements for architectural decoration are getting higher and higher. At present, the building boards used for indoor and outdoor decoration of buildings are generally wood boards, marble boards, ceramic tiles, melamine boards and the like. However, wood boards are processed from natural materials, and a large amount of use will inevitably cause damage to forest resources. Moreover, noble wood is becoming more and more scarce, and the natural formation of wood grains cannot be selected. Infestation and many other problems. Marble is also processed from natural materials. Extensive use will also cause scarcity of resources, and marble has problems such ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04F13/14B41M5/00B41M1/26
Inventor 周良剑
Owner FOSHAN ARTECH PANEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com