A kind of asphalt mixture for suppressing reflective cracks of pavement and its preparation method and application

A technology of asphalt mixture and reflective cracks, which is applied in the field of building materials, can solve the problems of increasing the cost of renovation projects in purchase prices, restricting urban road renovation projects, etc., achieving good economic and environmental benefits, and suppressing reflective cracks

Active Publication Date: 2018-02-13
SHANGHAI PUDONG ROAD & BRIDGE GRP CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to regional differences, higher purchase prices of aggregates and 90# heavy traffic asphalt increase the cost of "white plus black" renovation projects, which restricts the progress of urban road renovation projects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of asphalt mixture for suppressing reflective cracks of pavement and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] This example provides an asphalt mixture for suppressing reflective cracks on the road surface. The raw materials used are as follows:

[0031] Aggregate: Coarse aggregate and fine aggregate are limestone, the nominal maximum particle size is 19mm, coarse aggregate and fine aggregate account for 76.2% and 12.5% ​​of the mass of the mixture respectively;

[0032] Filler: limestone powder, accounting for 4.2% of the mass of the mixture;

[0033] Fiber stabilizer: lignin fiber, with an average length of about 4mm, accounting for 0.3% of the mass of the mixture;

[0034] The ore grading is:

[0035] Sieve hole (mm)

26.5

19

16

13.2

9.5

4.75

2.36

1.18

0.6

0.3

0.15

0.075

Passing rate(%)

100.0

95.1

81.6

65.5

45.1

19.7

14.6

11.4

8.9

7.5

6.7

5.9

[0036] High-viscosity asphalt binder: accounting for 6.5% of the mass of the mixture, modified from Tepco 70# asphalt 77.3%, 60-80 mesh waste...

Embodiment 2

[0042] Aggregate: Coarse aggregate and fine aggregate are limestone, the nominal maximum particle size is 19mm, coarse aggregate and fine aggregate account for 72.9% and 14.9% of the mass of the mixture respectively;

[0043] Filler: limestone powder, accounting for 5.1% of the mass of the mixture;

[0044] Fiber stabilizer: lignin fiber, with an average length of about 5mm, accounting for 0.4% of the mass of the mixture;

[0045] The ore grading is:

[0046] Sieve hole (mm)

26.5

19

16

13.2

9.5

4.75

2.36

1.18

0.6

0.3

0.15

0.075

Passing rate(%)

100.0

95.2

82.1

66.4

46.1

21.6

16.1

12.4

9.4

7.9

6.9

6.0

[0047] High-viscosity asphalt binder: accounting for 6.7% of the mass of the mixture, composed of 77.1% of Korean SK70# asphalt, 14.9% of 60-80 mesh waste rubber powder, 2‰ of industrial grade sulfur, 3.8% of warm mixing agent and high-viscosity asphalt modifier 4% composition, among wh...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
voidageaaaaaaaaaa
voidageaaaaaaaaaa
Login to View More

Abstract

The invention relates to an asphalt mixture for suppressing reflective cracks on road surfaces and its preparation method and application. The mixture includes aggregates, fillers, fiber stabilizers and high-viscosity asphalt binders. The aggregates include coarse aggregates and fine aggregates. The nominal maximum particle size of the asphalt mixture is 19mm, and both the coarse and fine aggregates are made of limestone; in terms of weight percentage, the amount of high-viscosity asphalt binder is 5.5% to 6.9% of the mass of the asphalt mixture, ranging from 60 to 80 mesh 12%~19% of rubber powder, 1‰~3‰ of crosslinking agent, 4.0%~8.0% of modifier, 3.8%~7.6% of viscosity reducer, and the balance is 70# matrix asphalt, and the asphalt mixture is intermittent half Open gradation, porosity 8% to 12%. The asphalt mixture provided by the invention can effectively suppress reflection cracks on the road surface, has low preparation cost, and has good economic and environmental benefits.

Description

technical field [0001] The invention belongs to the technical field of building materials used in road engineering, and in particular relates to an asphalt mixture for suppressing reflective cracks on road surfaces, a preparation method and application thereof. Background technique [0002] With the development of society, urban roads have higher requirements for functionality and comfort while satisfying traffic travel. The reconstruction of a large number of existing cement concrete pavements has become a difficult point in the development of urban roads. Years of engineering practice experience shows that "white plus black" is an economical and effective engineering transformation method, that is, adding a layer of asphalt mixture to suppress reflection cracks on the original cement road slab. [0003] This layer of asphalt mixture for suppressing reflective cracks is the key to the "white plus black" reconstruction project. Discontinuously graded, high-viscosity asphalt ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/26
Inventor 李桥林刘钢赫振华王腾飞李军代陆风云马利志李交袁月邱轶徐韵淳邓国民夏庆宇吴月琴李俊
Owner SHANGHAI PUDONG ROAD & BRIDGE GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com