A kind of protective coating for single crystal superalloy and preparation method thereof

A technology of superalloy and protective coating, applied in the direction of metal material coating process, coating, metal layered products, etc., can solve the problems of limited application, easy peeling and failure of coating, thermal-mechanical fatigue, etc., to improve strain tolerance , Solve the problem of poor interface bonding force and improve the effect of interface bonding force

Active Publication Date: 2015-08-05
SHENYANG LIMING AERO-ENGINE GROUP CORPORATION
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During service, the surface of MCrAlY coating cannot rapidly form continuous and dense Al 2 o 3 film, and the YSZ ceramic surface layer prepared by the atmospheric plasma spraying method has a lamellar structure, which is easy to cause thermal fatigue under the condition of cold and hot cycles, and makes the coating easy to peel off and fail, which limits its application on high-speed rotating turbine blades

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of protective coating for single crystal superalloy and preparation method thereof
  • A kind of protective coating for single crystal superalloy and preparation method thereof
  • A kind of protective coating for single crystal superalloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] A protective coating for single crystal superalloy, the protective coating is composed of a PtAl metal bottom layer and a columnar crystal structure YSZ ceramic surface layer. Wherein the PtAl metal bottom layer is a platinum-modified aluminide coating, and the columnar crystal structure YSZ ceramic surface layer is 6-8%Y 2 o 3 Partially stabilized ZrO 2 Columnar crystal structure ceramic surface layer.

[0033] A method for preparing the protective coating for the above-mentioned single crystal superalloy, the preparation method comprises the steps of:

[0034] (1) Preparation steps of the PtAl metal bottom layer

[0035] The preparation steps of the PtAl metal bottom layer are as follows: first, a 10 μm Pt layer is prepared on the surface of the single crystal superalloy blade substrate by electroplating, and then aluminized to the Pt layer by an embedding method, and the thickness of the prepared PtAl metal bottom layer is 50μm;

[0036] (2) Post-treatment steps...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a protective coating of a single crystal high-temperature alloy as well as a preparation method thereof. The technical scheme is as follows: the protective coating of the single crystal high-temperature alloy consists of a PtAl metal bottom layer and an YSZ (Yttria Stabilized Zirconia) ceramic surface layer in a columnar crystal structure. The preparation method of the protective coating of the single crystal high-temperature alloy comprises the following steps: a preparation step of the PtAl metal bottom layer, a post-treatment step of the PtAl metal bottom layer, a preparation step of the YSZ ceramic surface layer in the columnar crystal structure, and a post-treatment step of the YSZ ceramic surface layer in the columnar crystal structure. The invention can provide the protective coating of the single crystal high-temperature alloy, which is good in interface bonding, excellent in oxidation resistance and high in stress tolerance, as well as the preparation method thereof.

Description

technical field [0001] The invention relates to a protective coating and a preparation method thereof, in particular to a protective coating for a single crystal superalloy and a preparation method thereof. Background technique [0002] In order to continuously improve the performance of aero-engines (high thrust-to-weight ratio, low fuel consumption), it is required to continuously increase the gas temperature at the turbine inlet. The turbine blades, the core components of the engine, serve in very harsh environments. In addition to bearing aerodynamic loads and centrifugal loads, they are also subjected to the impact and erosion of high-temperature gas for a long time. Although single crystal superalloy blades have excellent high-temperature mechanical properties, their high-temperature oxidation resistance cannot meet the needs of use. The surfaces of advanced aero-engine turbine blades at home and abroad are coated with protective coatings without exception to improve ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B15/04B32B18/00C23C14/06C23C14/30
Inventor 程玉贤袁福河王璐张春刚刘艳
Owner SHENYANG LIMING AERO-ENGINE GROUP CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com