Super high temperature resistant anti-corrosion coating and preparation method thereof

A technology for anti-corrosion coatings and high temperature resistance, applied in the direction of anti-corrosion coatings, coatings, etc., to solve the problem of coating compactness and ensure durability

Active Publication Date: 2016-01-20
JIANGSU RONGCHANG NEW MATERIAL TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The ultra-high temperature resistant coating not only has high temperature resistance and corrosion resistance but also has good storage stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Super high temperature resistant anti-corrosion coating and preparation method thereof
  • Super high temperature resistant anti-corrosion coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] 1. Raw materials

[0026] Siloxane Monomer Industrial Products Wacker Chemie

[0027] 1053 Silicone resin industrial products Zhonghao Chenguang Chemical Co., Ltd.

[0028] 840 organic resin industrial products Dow Corning Chemical

[0029] Acrylamide Monomer Industrial Products Shanghai Chemical Reagent Co., Ltd.

[0030] Silicone coupling agent industrial products Nanjing Shuguang Chemical Co., Ltd.

[0031] Cetyl Ammonium Bromide Chemicals Jiangsu Jincheng Reagent Co., Ltd.

[0032] Heat Stabilizer Industrial Products Nantong Advan Chemical Co., Ltd.

[0033] 2441 Glass black industrial products Shanghai Tianguang Chemical Factory

[0034] 2451 Glass White Industrial Products Shanghai Tianguang Chemical Factory

[0035] Enamel Black Industrial Products Shanghai Tianguang Chemical Factory

[0036] Aluminum Powder Industrial Products Jinan Metal Pigment Co., Ltd.

[0037] Zinc Phosphate Industrial Products Shanghai Hengzhan Chemical Co., Ltd.

[0038] Mica Pow...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of a superhigh-temperature-resisting and anti-corrosion coating. An amide group is introduced by a silane coupling agent containing double bonds and then the silane coupling agent is copolymerized with silicone resin containing methoxyl active groups to prepare modified organic silicon resin containing amide groups, and the modified organic silicon resin has extremely strong compatibility with alkaline pigments and consequently no longer react with alkaline glass powder filler, so that the coating has excellent storage stability; besides, the coating can resist high temperature of 800 DEG C and has strong anti-corrosion capability.

Description

technical field [0001] The invention belongs to the technical field of chemical coatings, and relates to a super-high-temperature-resistant anti-corrosion coating and a preparation method thereof. The coating is suitable for various high-temperature-resistant fields, especially for high-temperature-resistant anti-corrosion fields under an environment of 800°C. Background technique [0002] As we all know, metal materials are prone to oxidation reaction with oxygen in the air in high temperature environment, resulting in corrosion phenomenon, so that the metal materials gradually lose their strength and lead to the loss of structural performance, which has become a hidden danger of various accidents. Super high temperature resistant coating refers to the temperature exceeding 800 ℃. Under the impact of high temperature and strength, the paint film will not fall off and peel off, and can still maintain appropriate physical and mechanical properties to effectively protect the su...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D183/10C09D7/12C09D5/10C08G77/442C08F230/08C08F220/58C08F220/54
Inventor 陈群祝红良马金才陆朝军黄顺道
Owner JIANGSU RONGCHANG NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com