Polyvinyl chloride powdery plastic dipping composition

A polyvinyl chloride and polyvinyl chloride resin technology is applied in the field of polymer material processing and application, which can solve the problems of complex dipping process, unspecified resin polymerization degree, unspecified resin powder polymerization degree and resin powder particle size, etc. Short melting and plasticizing time, enhanced waterproof and corrosion resistance, no pollution effect

Active Publication Date: 2014-01-22
CHINA PETROLEUM & CHEM CORP
View PDF5 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the dipping process of this method is relatively complicated, and the degree of polymerization of the resin used and whether to use composite resin are not clearly specified; the degree of polymerization of the resin powder used and the particle size of the resin powder are not clearly specified, and the two have a great impact on the melting time of the material and Leveling has a great influence

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The formula of a polyvinyl chloride powder dipping composition of the present invention is: polyvinyl chloride resin (polymerization degree 700), 100 parts, polyvinyl chloride paste resin (polymerization degree 1000), 3 parts, dioctyl phthalate , 50 parts, dioctyl sebacate, 6 parts, organotin stabilizer, 2.5 parts, epoxy soybean oil, 4.5 parts, stearic acid, 5 parts, glyceryl monostearate, 2 parts, titanium dioxide ( 10μm), 5 parts, superfine activated calcium carbonate (10μm), 2 parts, titanium blue green, 0.02 parts.

Embodiment 2

[0027] The formula of a polyvinyl chloride powder dipping composition of the present invention is: polyvinyl chloride resin (polymerization degree 600), 100 parts, polyvinyl chloride paste resin (polymerization degree 1000), 2 parts, dioctyl phthalate , 31 parts, dioctyl sebacate, 4 parts, organotin stabilizer, 1 part, epoxy soybean oil, 1 part, stearic acid, 1 part, glyceryl monostearate, 1 part.

Embodiment 3

[0029] The formula of a polyvinyl chloride powder dipping composition of the present invention is: polyvinyl chloride resin (polymerization degree 550), 100 parts, polyvinyl chloride paste resin (polymerization degree 1000), 15 parts, diisodecyl phthalate Ester, 60 parts, dioctyl sebacate, 5 parts, organotin stabilizer, 7 parts, epoxy soybean oil, 6 parts, stearic acid, 6 parts, oxidized polyethylene wax, 4 parts, superfine activated carbonic acid Calcium (15 μm), 5 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a polyvinyl chloride powdery plastic dipping composition, and belongs to the technical field of processing and application of high-molecular materials. The polyvinyl chloride powdery plastic dipping composition is characterized by comprising the following components (in parts by weight): 100 parts of polyvinyl chloride, 2-15 parts of polyvinyl chloride paste resin, 35-65 parts of plasticizing agent, 1-7 parts of stabilizing agent, 1-6 parts of epoxidized soybean oil, 2-10 parts of lubricating agent and 0-10 parts of filler, wherein polyvinyl chloride is suspension method polyvinyl chloride resin, the polymerization degree is 500-800, and the grain diameter is 50-200 micrometers; the polymerization degree of the polyvinyl chloride paste resin is 1000, and the grain diameter is 5-20 micrometers. Compared with the prior art, the polyvinyl chloride powdery plastic dipping composition disclosed by the invention achieves shorter melting and plasticizing time and better leveling property of a plastic dipping product by requiring the polymerization degree of polyvinyl chloride resin powder and the granular size of the composition.

Description

technical field [0001] The invention discloses a polyvinyl chloride powder dipping composition, which belongs to the technical field of polymer material processing and application. Background technique [0002] Plastic dipping is a processing method in which the surface-treated metal products are dipped into resin powder or resin paste in a preheated state, and the resin on the surface of the metal layer is heated and plasticized to obtain a plastic coating on the surface. Plastic-dipped products are suitable for various metal guardrails, frames, tools, the outer coating of metal cages for aquatic product breeding, and the coating of wire mesh, etc., and have broad markets in industry, agriculture and daily necessities. [0003] At present, domestic plastic dipping mainly uses PVC paste resin, which is soaked in a plasticizer for a long time and mixed to form a slurry or paste shape, then dipped in plastic, and then heated, plasticized and shaped to make PVC products. In or...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/02C08K13/06C08K5/1515C08K5/12C08K5/11C08K3/22C08K3/26
Inventor 桂俊杰王晶张新华李静刘荣德张桦贾小波刘浩孙培培孙丽朋
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com