A technology for cable sheathing and wind power generation, applied in the direction of insulated cables, cables, circuits, etc., can solve the problems of large permanent deformation and limited use range, etc., and achieve the goals of reducing consumption, highlighting durability, increasing elongation and tear strength Effect

Active Publication Date: 2014-10-22
南通特美特工具有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to its large permanent deformation, its scope of use is also limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Cable sheathing materials for wind power generation are calculated by mass fraction and include the following components:

[0037] 90 parts of chlorosulfonated polyethylene, the vulcanizing agent magnesium oxide and N, N'-m-phenylene bismaleimide, the mass ratio is 2:6, 3 parts; the vulcanization accelerator is 2-mercaptobenzothiazole and Antimony dithiocarbamate, its mass ratio is 0.4:2, 1 part of vulcanization accelerator; 1 part of zinc oxide as vulcanization accelerator; antiscorch agent N-cyclohexylsulfurized phthalimide and N-nitrosoaniline The mass ratio is 2:1, 0.8 part; The mass ratio of antioxidant N-phenyl-2-naphthylamine, N-phenyl-N'-isopropyl p-phenylenediamine and 2-mercaptobenzimidazole is 1 :1:8, 1 part; the flame retardant is triphenyl phosphate and melamine, the mass ratio of triphenyl phosphate and melamine is 1:1, 10 parts; the plasticizer is dioctyl phthalate and chlorinated The mass ratio of paraffin, dioctyl phthalate and chlorinated paraffin is ...

Embodiment 2

[0039] Cable sheathing materials for wind power generation are calculated by mass fraction and include the following components:

[0040] 100 parts of chlorosulfonated polyethylene, the vulcanizing agent magnesium oxide and N, N'-m-phenylene bismaleimide, the mass ratio is 4:6, 13 parts; the vulcanization accelerator is 2-mercaptobenzothiazole and Molybdenum dithiocarbamate, its mass ratio is 1:2, 5 parts of vulcanization accelerator; 4 parts of zinc oxide as vulcanization accelerator; anti-scorch agent N-cyclohexylsulfurized phthalimide and N-nitrosoaniline The mass ratio of 2:1, 3 parts; :1:8, 3 parts; the flame retardant is triphenyl phosphate and melamine, the mass ratio of triphenyl phosphate and melamine is 1:4, 20 parts; the plasticizer is dioctyl phthalate and chlorinated The mass ratio of paraffin wax, dioctyl phthalate and chlorinated paraffin is 2:1, 18 parts; 40 parts of high-dispersion white carbon black reinforcing agent; coupling agent bis(dioctyl phosphite) te...

Embodiment 3

[0042] Cable sheathing materials for wind power generation are calculated by mass fraction and include the following components:

[0043] 98 parts of chlorosulfonated polyethylene, the vulcanizing agent magnesium oxide and N, N'-m-phenylene bismaleimide, the mass ratio is 3:6, 10 parts; the vulcanization accelerator is 2-mercaptobenzothiazole and Bismuth dithiocarbamate, its mass ratio is 0.8:2, 3 parts of vulcanization accelerator; 2 parts of zinc oxide as vulcanization accelerator assistant; anti-scorch agent N-cyclohexylsulfurized phthalimide and N-nitrosoaniline The mass ratio is 2:1, 2 parts; the mass ratio of anti-ageing agent N-phenyl-2-naphthylamine, N-phenyl-N'-isopropyl-p-phenylenediamine and 2-mercaptobenzimidazole is 1 :1:8,,2 parts; the flame retardant is triphenyl phosphate and melamine, the mass ratio of triphenyl phosphate and melamine is 1:3, 16 parts; the plasticizer is dioctyl phthalate and chlorine The mass ratio of chemical paraffin, dioctyl phthalate and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a cable sheath material for wind power generation, which is characterized by comprising the following components in parts by mass: 90-100 parts of unvulcanized rubber base, 3-13 parts of vulcanizing agent, 1-5 parts of vulcanization accelerator, 1-4 parts of vulcanization acceleration assistant, 0.5-3 parts of anti-scorching agent, 1-3 parts of anti-aging agent, 10-20 parts of flame retardant, 8-18 parts of plasticizer, 20-40 parts of reinforcing agent and 0.5-2 parts of coupling agent. The preparation method comprises the following steps: carrying out multistep compounding to prepare compounded rubber; carrying out thin passing on the compounded rubber with an open mill 3-4 times, standing the output sheet; and cutting the output sheet into strips with a three-roller calender, and cooling the output rubber page through cooling rollers to obtain the finished product. The cable sheath material for wind power generation has the advantages of scientific proportioning of selected raw materials, simple preparation method, better corrosion resistance, better oxidation resistance, better weather resistance, higher mechanical properties (stretching resistance and torsion resistance) and high shock resistance, and is low-pollution environment-friendly product.

Description

technical field [0001] The invention belongs to the field of rubber material preparation, in particular to a cable sheath material for wind power generation. Background technique [0002] In recent years, due to the shortage of resources such as oil and coal at home and abroad, countries have vigorously developed new energy sources. Wind energy, as a clean energy source, is energy-saving and environmentally friendly, and has an inexhaustible source. However, the cable accessories for wind power generation cannot keep up with the requirements of wind power generation. Due to difficult maintenance and harsh service conditions, the cables for wind power generation have high requirements for cable performance and life, and the cables are constantly twisted during operation. At present, natural rubber and styrene-butadiene rubber are mostly used for cable sheath rubber. This kind of cable sheath rubber has good elasticity, but its weather resistance is poor, and it is easy to age...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/34C08K13/02C08K3/22C08K5/3415C08K5/47C08K5/39C08K5/523C08K5/3492C08K3/36C08K5/18C08K5/37H01B7/17
Inventor 张民
Owner 南通特美特工具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap