A window film that adheres to the outside of the window pane

A technology of window glass and window film, which is applied in the direction of synthetic resin layered products, layered products, chemical instruments and methods, etc., can solve problems such as embrittlement and short service life, and achieve aging resistance, reduce damage, and guarantee The effect of service life

Active Publication Date: 2016-05-11
乐凯胶片股份有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing known window films are generally used on the inside of the glass window film. If it is adhered to the outside of the glass window, there are disadvantages such as short service life (generally only 3 to 5 years), embrittlement, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A window film that adheres to the outside of the window pane
  • A window film that adheres to the outside of the window pane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Preparation of anti-scratch and weather-resistant layer coating solution:

[0036] Multifunctional urethane acrylate prepolymer (EBECRYL294 / 25HD) 30 parts by weight

[0037] 10 parts by weight of fluorine-containing ethylene glycol diacrylate

[0038] 14 parts by weight of 2-fluoroacrylate

[0039] Photoinitiator (184) 3 parts by weight

[0040] 40 parts by weight of ethyl acetate

[0041] BYK-3071 parts by weight

[0042] 2,4,6-tris(2'-butoxyphenyl)-1,3,5-triazine 2 parts by weight

[0043] Add the above-mentioned substances into a container, and stir evenly to obtain a coating solution for an anti-scratch and weather-resistant layer.

[0044] The parts by weight in each embodiment of the present invention may be g or kg.

[0045] Preparation of window film:

[0046] Gravure coating heat insulation layer on one side of polyester film (PET film), wet coating weight 15g / m 2 , cured by ultraviolet light after drying to obtain a heat-insulating layer with a dry fil...

Embodiment 2

[0048] Preparation of anti-scratch and weather-resistant layer coating solution:

[0049] Multifunctional urethane acrylate prepolymer (BASF LR-8987 prepolymer) 20 parts by weight

[0050] 30 parts by weight of fluorine-containing polyurethane acrylate

[0051] 25 parts by weight of 2-fluoroacrylate

[0052] 11734 parts by weight

[0053] 40 parts by weight of ethyl acetate

[0054] BYK-3070.5 parts by weight

[0055] 0.5 parts by weight of 2,4,6-tris(2'-butoxyphenyl)-1,3,5-triazine

[0056] Add the above-mentioned substances into a container, and stir evenly to obtain a coating solution for an anti-scratch and weather-resistant layer.

[0057] Preparation of window film:

[0058] Gravure coating heat insulation layer on one side of polyester film (PET film), wet coating weight 15g / m 2 , UV curing after drying to obtain a heat insulation layer with a dry film thickness of about 10um; apply the above-mentioned anti-scratch and weather-resistant layer coating liquid on th...

Embodiment 3

[0060] Preparation of anti-scratch and weather-resistant layer coating solution:

[0061] Pure acrylate prepolymer (6530B-40 from Changxing Company, etc.) prepolymer 60 parts by weight

[0062] 5 parts by weight of fluorine-containing polyurethane acrylate

[0063] TPO3 parts by weight

[0064] 30 parts by weight of butyl acetate

[0065] BYK-3061 parts by weight

[0066] 1 part by weight of phenyl o-hydroxybenzoate

[0067] Add the above-mentioned substances into a container, and stir evenly to obtain a coating solution for an anti-scratch and weather-resistant layer.

[0068] Preparation of window film:

[0069] Gravure coating heat insulation layer on one side of polyester film (PET film), wet coating weight 15g / m 2 , cured by ultraviolet light after drying to obtain a heat-insulating layer with a dry film thickness of about 10um; coat the above-mentioned anti-scratch and weather-resistant layer coating liquid on the heat-insulating layer, and the wet coating amount i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a window film adhered onto the outer side of a window glass. According to the invention, a thermal insulation layer is arranged on the surface of a transparent substrate, and a scratch-resistant and weather-resistant layer is arranged on the surface of the thermal insulation layer; the other surface of the transparent substrate is provided with a pressure-sensitive adhesive layer, and a release film layer is arranged on the surface of the pressure-sensitive adhesive layer. The window film provided by the invention has a simple structure, excellent aging resistance, a high ultraviolet light rejection rate and high thermal insulation efficiency and can be widely applied to window glass of a building or an automobile.

Description

technical field [0001] The invention relates to a window film, in particular to a window film adhered to the outside of the window glass. Background technique [0002] Window film is an energy-saving and environmentally friendly film product with broad market development prospects. It is mainly used in automobile windows and building windows. [0003] In many cases, due to the limitation of construction location or site, it is impossible to attach window film to the inner side of the glass window, such as ceiling glass, glass curtain wall, multi-layer glass, and hollow glass structures that require higher energy-saving effects, etc. Window film is attached on the outside. Because it is used on the outside of glass windows, it is required to be used for a long time and has excellent aging resistance, that is, it will not be embrittled within a certain period of time (more than 8 years). However, the existing known window films are generally used on the inside of the glass w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B9/04B32B27/08B32B27/18B32B33/00
Inventor 秦长喜牛娟妮许亮高超
Owner 乐凯胶片股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products