Niobium-containing high-strength fine-grain 700MPa-level hot-rolled dual-phase steel and production method thereof

A technology of hot-rolled dual-phase steel and production method, which is applied in the field of niobium-containing high-strength and fine-grained 700MPa-grade hot-rolled dual-phase steel, can solve the problem of increasing difficulty in surface quality control of hot-rolled sheets, high cooling process requirements, industrial production restrictions, etc. problem, to achieve the effect of ensuring coating performance, low yield ratio and low cost

Inactive Publication Date: 2013-12-18
UNIV OF SCI & TECH LIAONING
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When the Si content is high, it is more difficult to control the surface quality of the hot-rolled sheet, adding alloy elements such as Cr and Mo, and the cost is high; (2) a three-stage cooling process is adopted, such as: Chinese Patent Publication (Announcement) No. A kind of 600MPa grade hot-rolled dual-phase steel and its preparation method
Due to its high requirements on the cooling process, the three-stage cooling process is used, and the industrial production is limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Niobium-containing high-strength fine-grain 700MPa-level hot-rolled dual-phase steel and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] The present invention will be specifically described below through embodiments in conjunction with the accompanying drawings.

[0027] A niobium-containing high-strength fine-grained 700MPa grade hot-rolled dual-phase steel and its production method. The prepared alloy is smelted into a steel ingot in a 50kg vacuum induction heating furnace, and its chemical composition weight percentage is C: 0.08%; Si: 0.40%; Mn: 1.40%; P: ≤0.03%; S: ≤0.03%; Nb: 0.10%, the rest is Fe and unavoidable impurities. Hot rolling is done on a laboratory 450 rolling mill. The rolling process is as follows: heat the steel ingot to 1200~1250°C, and start rolling after holding it for 1 hour; the rolling temperature range in the austenite recrystallization zone is 1100~1150°C, and the deformation in the austenite recrystallization zone is controlled at 50% ; The rolling temperature range of the austenite non-recrystallization zone is 880~980℃, and the deformation of the austenite non-recrystalli...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a niobium-containing high-strength fine-grain 700MPa-level hot-rolled dual-phase steel and a production method thereof. A steel plate with a polygonal ferrite and martensite dual-phase structure is obtained by a hot rolling and sectional control cooling process. The dual-phase steel comprises the following chemical components in percentage by weight: 0.07-0.10% of C, 0.20-0.50% of Si, 1.20-1.50% of Mn, less than or equal to 0.03% of P, less than or equal to 0.03% of S, 0.08-0.11% of Nb and the balance of Fe and unavoidable impurities. The production method of the dual-phase steel comprises the following steps: preparing materials according to the chemical components of the dual-phase steel; smelting in a vacuum induction furnace, and pouring the molten steel to obtain a steel ingot; heating the steel ingot and starting rolling; controlling the rolling at two stages; after the rolling, performing sectional cooling; and finally conveying the product to a coil storehouse. The dual-phase steel disclosed by the invention has the advantages of good strength-toughness match of steel plate, high tensile strength of steel plate, low yield ratio and good stamping property.

Description

Technical field: [0001] The invention relates to a high-strength fine-grain hot-rolled dual-phase steel and a production method thereof, in particular to a niobium-containing high-strength fine-grain 700MPa hot-rolled dual-phase steel and a production method thereof. Background technique: [0002] Iron and steel materials are still the main structural materials in the 21st century. High performance and low cost are the development direction of steel materials in the future and a necessary prerequisite for sustainable economic development. With the development of modern automobiles in the direction of high safety, economical and environmental protection, and long life, higher and higher requirements are put forward for the strength, formability, and corrosion resistance of automobile sheets. Due to its high strength and high formability, hot-rolled dual-phase steel has been widely used in the manufacture of automobile reinforcement plates, wheels, chassis, bumpers, various fr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/12C21D8/04
Inventor 张红梅周国十刘英义李胜利胡晓东应传涛
Owner UNIV OF SCI & TECH LIAONING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com