Preparation method of high-performance composite gypsum cementing slurry

A cementing slurry, high-performance technology, applied in the field of building materials, can solve the problems of unfavorable gypsum strength, non-adjustable setting time, and low compressive strength

Active Publication Date: 2013-12-11
四川吉浦森建材有限公司
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The journal "Nonmetallic Minerals" Issue 2, 2008 "Research on the Modification and Mechanism of Building Gypsum by Mineral Admixtures" introduced the composite gypsum cementitious material prepared with building gypsum, fly ash, mineral powder, cement, etc. as the main materials. , although it has good pouring performance, but the setting time is not adjustable; the compressive strength is low, so it cannot meet the needs of many occasions
In addition, previous studies believed that the amount of cement in gypsum should not be too large, such as "slag powder and cement modified gypsum cementitious material" introduced in "Gypsum Building Materials" published by China Building Materials Industry Press in 2012 on page 296. The large amount of cement will lead to too high alkalinity, which is not good for the strength of gypsum

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of high-performance composite gypsum cementing slurry
  • Preparation method of high-performance composite gypsum cementing slurry

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] See Table 1, ①, get 50kg of phosphorus building plaster, P.O42.5 cement 20kg, fly ash 30kg and stir under the rotating speed of 100 rpm to obtain the mixed powder for subsequent use; ②, get citric acid 0.005kg, potassium sulfate Mix 0.2kg evenly and grind together, pass through a 0.2mm sieve to obtain the activator for later use; ③, take 0.25kg of powdered polycarboxylate superplasticizer, 36kg of water and the activator obtained in step ② and pour it into a stirring container, at 150 rpm Stir at a rotating speed of 1 / min to obtain a mixed liquid; 4., under stirring at a rotating speed of 250 rev / min, add the mixed powder obtained in step 1. into a stirring container filled with a mixed liquid, and after the addition is completed, it will be mixed at 1800 The composite gypsum cemented slurry referred to in the present invention is obtained by stirring until the slurry is stirred at a rotating speed of rpm.

[0018] The content of other embodiments is basically the same ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A preparation method of high-performance composite gypsum cementing slurry belongs to the technical field of building materials. The composite gypsum cementing slurry comprises the components of one of building gypsum powder, coal ash or slag powder, a mixed powder comprising cementing, a water reducer and water as well as the components of an exciting agent formed by mixing a retarder and a sulphate, wherein the water, the water reducer and the exciting agent are proportionally weighed out according to the total mass of the mixed powder, and then poured into a stirring container, and uniformly stirred to obtain a mixed solution, the mixed powder are blended into the stirring container filled with the mixed solution in a stirring state, the mixed powder and the mixed solution are stirred into a slurry at a high speed after being blended so as to obtain the composite gypsum cementing slurry. The composite gypsum cementing slurry has the advantages of excellent pouring performance, adjustable settling time and high compressive strength. The preparation method can be used for producing building material products with different sizes and performances.

Description

technical field [0001] The invention relates to a composite gypsum cementing slurry and a manufacturing method thereof. It belongs to the technical field of building materials. Background technique [0002] Building gypsum refers to calcium sulfate dihydrate (CaSO 4 2H 2 O) prepared by dehydration, with β-calcium sulfate hemihydrate (β-CaSO 4 1 / 2H 2 O) Powdered gelling material as the main component. Natural gypsum, phosphogypsum, and desulfurized gypsum are three types of gypsum that are currently widely used in construction. [0003] The treatment and utilization of fly ash, slag, phosphogypsum and desulfurized gypsum solid waste have long been concerned by countries all over the world, and the cumulative stockpiles in my country alone have exceeded 500 million tons. At present, the composite gypsum cementing materials used in industrial production are mainly made of dihydrate gypsum, fly ash, slag, lime, phosphorus slag, etc. For example, in the Chinese journal "Br...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00
Inventor 黄滔庄瑞文邱峰秦钢
Owner 四川吉浦森建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap