Wet production process of sprinkled glass fiber canopy

A glass fiber and production process technology, applied in the field of wet production process, can solve the problems of affecting product odor, product appearance quality decline, high cost, and achieve the effect of satisfying lightweight design, weight reduction, and good rigidity

Active Publication Date: 2015-08-19
WUXI GISSING AUTO ACOUSTIC PARTS TECH CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing wet-process canopy is usually directly formed by superimposing glass fiber mat and PU. This molding process mainly has the following problems: 1. The glass fiber mat has already undergone a processing procedure in the glass fiber mat manufacturer, so it will produce The cost is higher than that of glass fiber of the same weight. Glue and rubber powder will be added in the processing of glass fiber mat manufacturers. Such substances will affect the odor and VOC of the product; 2. The glass fiber mat may be damaged during the molding process The complexity of the product shape leads to the appearance of the product with glass fiber marks, which leads to a decrease in the quality of the product appearance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Example 1 GAC Toyota 635A with sunroof roof

[0024] Canopy specification: L1644×W1182×H204

[0025] Wet production process of sprinkled glass fiber canopy, the steps are as follows:

[0026] (1) PU sheet rolling: put the PU sheet into the rubber rolling machine for double-sided rubber rolling, the speed of the rubber rolling machine is 35 rpm, the horizontal distance between the upper and lower rollers of the rubber rolling machine is 0.3mm; Glue amount single side 40g / m 2 ;

[0027] (2) Laying: Lay the impregnated non-woven base fabric and PE / PA composite film on the laying table on the feeding mechanism;

[0028] (3) The first glass fiber sprinkler: use a glass fiber cutter to cut the glass fiber to a length of 18mm, and use a glass fiber sprinkler to evenly sprinkle the cut glass fiber on the material laid in step (2) Above, the falling amount is 110g / m 2 ;

[0029] (4) PU placement: use machine grippers to place the PU sheet completed in step (1) on top of th...

Embodiment 2

[0043] Wet production process of sprinkled glass fiber canopy, the steps are as follows:

[0044] (1) PU sheet rolling: put the PU sheet into the rubber rolling machine for double-sided rubber rolling, the speed of the rubber rolling machine is 40 rpm, the horizontal distance between the upper and lower rollers of the rubber rolling machine is 0.5mm; Glue amount single side 50g / m 2 ;

[0045] (2) Laying: Lay the impregnated non-woven base fabric and PE / PA composite film on the laying table on the feeding mechanism;

[0046] (3) The first glass fiber spilling: Use a glass fiber cutter to cut the glass fiber to a length of 22mm, and use a glass fiber sprinkler to evenly sprinkle the cut glass fiber on the material laid in step (2) Above, the falling amount is 130g / m 2 ;

[0047] (4) PU placement: use machine grippers to place the PU sheet completed in step (1) on top of the evenly scattered glass fibers in step (3);

[0048] (5) The second glass fiber spraying: Use a glass ...

Embodiment 3

[0061] Wet production process of sprinkled glass fiber canopy, the steps are as follows:

[0062] (1) PU sheet rolling: put the PU sheet into the rubber rolling machine for double-sided rubber rolling, the speed of the rubber rolling machine is 38 rpm, the horizontal distance between the upper and lower rollers of the rubber rolling machine is 0.4mm; Glue amount single side 45g / m 2 ;

[0063] (2) Laying: Lay the impregnated non-woven base fabric and PE / PA composite film on the laying table on the feeding mechanism;

[0064] (3) The first glass fiber sprinkler: use a glass fiber cutter to cut the glass fiber to a length of 20mm, and use a glass fiber sprinkler to evenly sprinkle the cut glass fiber on the material laid in step (2) Above, the falling amount is 120g / m 2 ;

[0065] (4) PU placement: use machine grippers to place the PU sheet completed in step (1) on top of the evenly scattered glass fiber in step (3);

[0066] (5) The second glass fiber spraying: Use a glass ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Basis weightaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a wet-process production process of a sprinkled glass fiber roof, specifically for installation on the top of a car to play the roles of heat insulation, sound absorption and beautification, and belongs to the technical field of car interior parts. It obtains the finished glass fiber canopy through PU sheet rolling, laying, first glass fiber spilling, PU placement, second glass fiber spilling, fabric laying, pressing molding, cooling and setting, water jet cutting and inspection . The invention solves performance indicators such as low odor and low VOC of the roof, greatly reduces the weight of the roof, and meets the requirements of the lightweight design of the whole vehicle; when the glass fiber is scattered, the double-sided scattering process is adopted without any chemical composition Adding, forming flow operation, stable process, and good product appearance; the product has good rigidity, not easy to break and sag; there is no accumulation of semi-finished products on the way, which saves manufacturing costs; no harmful substances are produced in the entire production process of the product, which is an environmentally friendly product.

Description

technical field [0001] The invention relates to a wet-process production process of a sprinkled glass fiber roof, specifically for installation on the top of a car to play the roles of heat insulation, sound absorption and beautification, and belongs to the technical field of car interior parts. Background technique [0002] The car roof is generally installed on the top of the car to play the role of heat insulation, sound absorption and beautification. In the era of more and more pursuit of high performance, environmental protection, energy saving, lightweight, and individualization, the interior of a car, like the shape of a car, has become an important factor for people to choose a car. Therefore, the requirements for automotive interior parts are getting higher and higher. In the prior art, performance indicators such as high sound absorption, low weight, high strength, odor, and VOC of the canopy have become bottlenecks, restricting the development of the canopy. The...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B37/12B32B37/06B32B37/10B32B37/24B32B38/04
Inventor 王俊东
Owner WUXI GISSING AUTO ACOUSTIC PARTS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com