A kind of wear-resistant UV light curing wood coating composition

A technology of wood coatings and compositions, applied in the direction of epoxy resin coatings, coatings, etc., can solve the problems of high wear resistance of paint films, and achieve the effects of ensuring sanding resistance, sanding performance, and convenient sanding

Inactive Publication Date: 2016-03-23
江苏大象东亚制漆有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This creates a contradiction. On the one hand, the paint film requires high wear resistance, and on the other hand, it needs to be easily polished during UV paint construction. This contradiction has not been effectively resolved so far.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of wear-resistant UV light curing wood coating composition
  • A kind of wear-resistant UV light curing wood coating composition
  • A kind of wear-resistant UV light curing wood coating composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] This example provides a kind of wear-resisting UV photocuring wood coating composition, and its raw material formula is as follows in terms of mass percentage:

[0029]

[0030] The preparation method of the composition is as follows: according to the formula ratio, put the resin, diluent, and photoinitiator into the material bucket, start stirring, and put in 200 mesh transparent micropowder, 400 mesh transparent micropowder, and 800 mesh talc in sequence at a speed of 500r / min. powder, 1250 mesh talc powder, keep the rotation speed of 500r / min for 30 minutes, then increase the rotation speed to 1200r / min, disperse for 30 minutes, stop the machine, filter and pack with 80 mesh nylon filter, and the whole production process should be protected from light.

[0031] The main technical index of gained composition is as follows:

[0032] 1. Viscosity, cp / s4500

[0033] 2. Abrasion, 750g / 500r0.008

[0034] 3. Grinding property, easy to grind with 400# sandpaper

Embodiment 2

[0036] This example provides a kind of wear-resisting UV photocuring wood coating composition, and its raw material formula is as follows in terms of mass percentage:

[0037]

[0038] The preparation method of the composition is as follows: according to the formula ratio, put the resin and diluent into the material tank, start stirring, and put in 200 mesh transparent micropowder, 400 mesh transparent micropowder, 800 mesh talcum powder, 1250 mesh For talcum powder, keep the rotating speed of 400r / min for 35 minutes, then increase the rotating speed to 1100r / min, disperse for 35 minutes, stop the machine, filter and pack with 80-mesh nylon filter, and the whole production process should be protected from light.

[0039] The main technical index of gained composition is as follows:

[0040]1. Viscosity, cp / s4800

[0041] 2. Abrasion, 750g / 500r0.007

[0042] 3. Grinding property, easy to grind with 400# sandpaper

Embodiment 3

[0044] This example provides a kind of wear-resisting UV photocuring wood coating composition, and its raw material formula is as follows in terms of mass percentage:

[0045]

[0046] The preparation method of the composition is as follows: according to the formula ratio, put the resin and diluent into the material tank, start stirring, and put in 200 mesh transparent micropowder, 400 mesh transparent micropowder, 800 mesh talcum powder, 1250 mesh For talcum powder, keep the rotating speed of 400r / min for 25 minutes, then increase the rotating speed to 1100r / min, disperse for 35 minutes, stop the machine, filter and pack with 80-mesh nylon filter, and the whole production process should be protected from light.

[0047] The main technical index of gained composition is as follows:

[0048] 1. Viscosity, cp / s4650

[0049] 2. Abrasion, 750g / 500r0.008

[0050] 3. Grinding property, easy to grind with 400# sandpaper

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a wear-resistant UV (ultraviolet) photocuring woodware paint composition which comprises base resin, reactive diluent, photoinitiator and wear-resistant micro powder, wherein the wear-resistant micro powder is one or a combination of both of silicon oxide powder and aluminum oxide powder, the powder composing the wear-resistant micro powder has at least two particle sizes, the difference between the at least two particle sizes is at least 100 meshes, and the mass percent of the wear-resistant micro powder in the composition is 6-13%; and the composition further comprises talcum powder, the talcum powder also has at least two particle sizes, the difference between the two particle sizes is at least 100 meshes, the mass percent of the talcum powder in the composition is 8-18%, the particle size of the talcum powder is smaller than that of the wear-resistant micro powder, and the difference between the particle sizes of the talcum powder and the wear-resistant micro powder is at least 300 meshes. The paint composition disclosed by the invention ensures sanding performance in application, and also ensures wear resistance of a paint film.

Description

technical field [0001] The invention relates to a coating composition, in particular to a UV light curing wood coating composition. Background technique [0002] In 1946, Inmout Company of the United States obtained the first patent of UP / styrene UV curing ink. In the early 1950s, a large number of theoretical research articles were published. In the early 1960s, it entered commercial application (Germany first produced unsaturated polyester-based wood filler, the UV lamp power density was 30w / cm, and the line speed was 10 m / min (more than 3 lamps irradiated at the same time). At present The line speed of UV curing in the printing industry reaches 50-400 m / min. In the early 1970s, the acrylate curing system entered industrial application, the UV lamp power was increased to 80w / cm and effective reflectors were used to overcome the limitation of oxygen inhibition. Problem; In the 1980s, it was only developed and applied in developed countries and regions (in 1986, the United...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/10C09D7/12C09D5/00
Inventor 刘祥艾小芳
Owner 江苏大象东亚制漆有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com