Plastic binder and preparation method thereof

A technology of adhesives and plastics, which is applied in the direction of adhesive types, hydrocarbon copolymer adhesives, non-polymer adhesive additives, etc., and can solve problems such as poor storage performance, low bonding strength, and narrow application range, etc. Problems, to achieve the effect of fast bonding, high bonding strength and wide application

Inactive Publication Date: 2013-10-16
QUZHOU DONGKAI GLUE IND CO LTD
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims at the disadvantages of existing plastic adhesives, such as poor storage performance, easy color change, high production cost, narrow application range, and low bonding strength, and aims to provide a plastic adhesive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Plastic binder and preparation method thereof
  • Plastic binder and preparation method thereof
  • Plastic binder and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A plastic adhesive, based on the number of raw materials, the content of each component is:

[0027]

[0028] The base material is commercially pure acrylonitrile-styrene resin copolymer.

[0029] The antioxidant is tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester and silane coupling agent. The quality of tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid]pentaerythritol ester is 50% of the antioxidant quality. The mass of the silane coupling agent is 50% of the mass of the antioxidant.

[0030] The preparation method comprises the following steps:

[0031] A. Take dichloroethane, dichloroethylene, methyl acetate, ethyl acetate, acetone, tetrahydrofuran and cyclohexanone by weight respectively and join in the reactor, drop into 15 parts of meteorological method white carbon black, stir, Obtain solution one;

[0032] B. In solution one, drop into 10 parts of industrial pure acrylonitrile-styrene resin copolymer, stir, obta...

Embodiment 2

[0036] A plastic adhesive, based on the number of raw materials, the content of each component is:

[0037]

[0038] The base material is commercially pure acrylonitrile-styrene resin copolymer.

[0039] The antioxidant is tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester and silane coupling agent. The quality of tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid]pentaerythritol ester is 50% of the antioxidant quality. The mass of the silane coupling agent is 50% of the mass of the antioxidant.

[0040] The preparation method comprises the following steps:

[0041] A. Take dichloroethane, dichloroethylene, methyl acetate, ethyl acetate, acetone, tetrahydrofuran and cyclohexanone by weight respectively and join in the reactor, drop into 20 parts of meteorological white carbon black, stir, Obtain solution one;

[0042] B. In solution one, drop into 50 parts of industrial pure acrylonitrile-styrene resin copolymers, stir, obtain sol...

Embodiment 3

[0046] A plastic adhesive, based on the number of raw materials, the content of each component is:

[0047]

[0048] The base material is commercially pure acrylonitrile-styrene resin copolymer.

[0049]The antioxidant is tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester and silane coupling agent. The quality of tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid]pentaerythritol ester is 50% of the antioxidant quality. The mass of the silane coupling agent is 50% of the mass of the antioxidant.

[0050] The preparation method comprises the following steps:

[0051] A. Take dichloroethane, dichloroethylene, methyl acetate, ethyl acetate, acetone, tetrahydrofuran and cyclohexanone by weight respectively and join in the reactor, drop into 5 parts of meteorological method white carbon black, stir, Obtain solution one;

[0052] B. In solution one, drop into 10 parts of industrial pure acrylonitrile-styrene resin copolymer, stir, obtain...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of binders and particularly relates to a plastic binder. A base material of the plastic binder disclosed by the invention is an acrylonitrile-styrene resin copolymer, a plasticizer is a dibutyl ester type compound, and an antioxidant, gas phase process white carbon black and a solvent are additionally added. The invention further relates to a preparation method of the plastic binder, and the preparation method comprises the following steps of: adding the solvent into a reaction kettle, putting in the gas phase process white carbon black and stirring till complete dissolution; putting in the acrylonitrile-styrene resin copolymer and stirring till complete dissolution of the acrylonitrile-styrene resin copolymer; and adding the antioxidant and the dibutyl ester type compound and stirring to obtain the plastic binder. The plastic binder disclosed by the invention has the advantages of environmental friendliness, good storage performance, low production cost and wide range of application, and the binding strength achieves the national standard. The plastic binder disclosed by the invention is convenient to prepare, simple in conditions, safe and reliable, and the base material can select waste plastic of SAN (styrene-acrylonitrile) resin so as to realize recycling of the waste of the base material, avoid the waste of resources and be suitable for industrial production.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to a plastic adhesive and a preparation method thereof. Background technique [0002] At present, the existing plastic adhesives have the following disadvantages: short shelf life, poor storage performance, and yellowish product color; the product is packaged in an iron can, which will rust the iron can and turn the color black; and the adhesive strength is low, Production costs are high. The scope of use is narrow, and it can only be applied to the bonding of PVC pipes and fittings; the toxicity is high, and mass production and sales are restricted. For example: currently on the market, the base material is a plastic adhesive made of high-chlorinated polyvinyl chloride, which has dark color, high toxicity, heavy odor, poor oxygen resistance, and poor storage performance; the normal shelf life is generally 5-7 months. When the temperature is low, it will thicken, deteriorate, or...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J125/12C09J11/04C09J11/06
Inventor 钱小东钱凯李元
Owner QUZHOU DONGKAI GLUE IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com