Flame-retardant reinforced ABS (Acrylonitrile Butadiene Styrene) material and preparation method thereof

A technology of ABS material and brominated flame retardant, which is applied in the field of flame retardant reinforced ABS material and its preparation, can solve the problems of not having high strength and high flame retardant performance at the same time, and high cost, so as to improve the surface bonding force and ensure the strength Performance requirements, the effect of improving overall performance

Inactive Publication Date: 2013-09-18
QINGDAO GON TECHNOLOGY CO LTD
View PDF9 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The invention provides a flame-retardant reinforced ABS material and a preparation method thereof, which can solve the problems of high cost and inability to simultaneously possess high strength and high flame-retardant performance in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant reinforced ABS (Acrylonitrile Butadiene Styrene) material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Embodiment 1, unit: kg

[0039] 40 parts of acrylonitrile-styrene (SAN), 10 parts of ABS high rubber powder, 29 parts of glass fiber, 5 parts of styrene-maleic anhydride (SMA), 12 parts of decabromodiphenylethane as brominated flame retardant, 3 parts of antimony trioxide, 0.10 part of polytetrafluoroethylene as anti-dripping agent, 0.3 part of antioxidant 1010, 0.4 part of vinyl bisstearamide (EBS) as lubricant, and 0.2 part of coupling agent KH550.

Embodiment 2

[0040] Embodiment 2, unit: kg

[0041]Acrylonitrile-styrene (SAN) 35 parts, ABS high rubber powder 14 parts, glass fiber 30 parts, styrene-maleic anhydride (SMA) 5 parts, brominated flame retardant 12 parts, antimony trioxide 3 parts, The anti-dripping agent is 0.15 parts of polytetrafluoroethylene, 0.3 parts of antioxidant 168, 0.40 parts of lubricant zinc stearate, and 0.15 parts of coupling agent KH560.

Embodiment 3

[0042] Embodiment 3, unit: kg

[0043] Acrylonitrile-styrene (SAN) 45 parts, ABS high rubber powder 12 parts, glass fiber 20 parts, styrene-maleic anhydride (SMA) 5 parts, brominated flame retardant 15 parts, antimony trioxide 3, antimony The dripping agent is 0.15 parts of polytetrafluoroethylene, 0.3 parts of antioxidant, 0.5 parts of lubricant calcium stearate, and 0.2 parts of coupling agent KH550.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a flame-retardant reinforced ABS (Acrylonitrile Butadiene Styrene) material and a preparation method thereof. The problems of high cost and incapability of having high strength and high flame retardancy at the same time in the prior art can be solved. The technical scheme is as follows: the flame-retardant reinforced ABS material comprises the following components inparts by weight: 35-50 parts of acrylonitrile-styrene, 8-15 parts of ABS high glue powder, 20-40 parts of glass fiber, 3-6 parts of styrene-maleic anhydride,10-15 parts of brominated flame retardant, 2-4 parts of antimonous oxide, 0.10-0.20 part of anti-dripping agent, 0.3-0.6 part of antioxidant, 0.3-0.8 part of lubricant and 0.1-0.3 part of coupling agent. The formulation system of the invention contains a reinforcement system, a capacity increasing system and a flame retardant system to meet the design demands and simultaneously meets the high strength and flame retardancy demands.

Description

technical field [0001] The invention belongs to a composite material, in particular to a flame-retardant reinforced ABS material and a preparation method thereof. Background technique [0002] ABS resin is one of the five major synthetic resins. ABS is a terpolymer of acrylonitrile, butadiene and styrene. It has excellent impact resistance, heat resistance, low temperature resistance, chemical resistance and electrical properties. It also has Easy to process, stable product size, good surface gloss, etc., easy to paint and color, and can also carry out secondary processing such as surface metal spraying, electroplating, welding, hot pressing and bonding, etc., widely used in machinery, automobiles, electronics It is a thermoplastic engineering plastic with a wide range of uses in industrial fields such as electrical appliances, instrumentation, textiles, and construction. [0003] ABS resin is easy to process, has good dimensional stability and surface gloss, is easy to pai...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L25/12C08L55/02C08L35/06C08K3/22C08K7/14B29C47/92B29C48/92
CPCB29C48/022B29C48/04B29C48/40B29C48/919B29C48/92B29C2948/92704B29C2948/92895
Inventor 王龙王爱国
Owner QINGDAO GON TECHNOLOGY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com