High-strength and high-toughness heat treatment method of medium-carbon silicon-manganese-chromium-nickel series low alloy steel

A medium-carbon silicon-manganese-chromium-nickel and carbon-silicon-manganese-chromium-nickel technology is applied in the field of high-strength and toughening heat treatment of low-alloy steels, which can solve the problem that medium-carbon silicon-manganese-chromium-nickel low-alloy steels cannot have both strength and plasticity. problems, to achieve the effect of increasing yield strength, increasing tensile strength, and improving plasticity and toughness

Active Publication Date: 2013-09-04
HARBIN INST OF TECH
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims to solve the problem that the medium-carbon silicon-manganese-chromium-nickel low-alloy steel obtained after the traditional heat treatment process cannot have good strength and ductility at the same time, and provides a medium-carbon silicon-manganese-chromium-nickel low-alloy steel High strength and toughness heat treatment method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength and high-toughness heat treatment method of medium-carbon silicon-manganese-chromium-nickel series low alloy steel
  • High-strength and high-toughness heat treatment method of medium-carbon silicon-manganese-chromium-nickel series low alloy steel

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0010] Specific embodiment one: In this embodiment, a method for high-strength and toughening heat treatment of medium-carbon silicon-manganese-chromium-nickel low-alloy steel is carried out according to the following steps:

[0011] 1. The first heat treatment: Austenitize the medium-carbon silicon-manganese-chromium-nickel low-alloy steel, and then lower the martensitic transformation starting point Ms of the medium-carbon silicon-manganese-chromium-nickel low-alloy steel at 90°C to 10°C. ℃ for isothermal quenching, holding time is 120s, complete the first heat treatment; wherein said isothermal quenching is isothermal oil quenching or isothermal gas quenching;

[0012] 2. The second heat treatment: put the medium-carbon silicon-manganese-chromium-nickel low-alloy steel after the first heat treatment in step 1 above the martensitic transformation starting point Ms of the medium-carbon silicon-manganese-chromium-nickel low-alloy steel at 80°C to 200°C ℃ for isothermal quenchi...

specific Embodiment approach 2

[0015] Embodiment 2: The difference between this embodiment and Embodiment 1 is that the specific operation process of the austenitization treatment described in step 1 is as follows: the medium-carbon silicon-manganese-chromium-nickel low-alloy steel is placed at a temperature of medium carbon silicon Manganese-chromium-nickel low-alloy steel A c3 Insulation under the above conditions of 30°C to 50°C, the holding time is 600s to 1800s, that is, the austenitization treatment is completed; the A c3 It is the final temperature when ferrite is completely transformed into austenite when heated. Others are the same as in the first embodiment.

specific Embodiment approach 3

[0016] Embodiment 3: This embodiment is different from Embodiment 1 or 2 in that the medium-carbon silicon-manganese-chromium-nickel low-alloy steel described in step 1 is 40SiMnCrNiMoV steel, 37SiMnCrNiMoV steel, 30Si2MnCrMoVE steel or 35SiMnCrMoVA steel. Others are the same as in the first or second embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Yield strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-strength and high-toughness heat treatment method of medium-carbon silicon-manganese-chromium-nickel series low alloy steel, relating to a high-strength and high-strength heat treatment method of low alloy steel and aiming at solving the problem that the medium-carbon silicon-manganese-chromium-nickel series low alloy steel treated by a traditional heat treatment process cannot simultaneously obtain excellent strength, ductility and toughness. The high-strength and high-toughness heat treatment method comprises the following steps of: 1, carrying out austenitizing treatment on the medium-carbon silicon-manganese-chromium-nickel series low alloy steel, and then carrying out isothermal quenching to finish primary heat treatment; and 2, carrying out isothermal quenching on the medium-carbon silicon-manganese-chromium-nickel series low alloy steel subjected to the primary heat treatment in the step 1, and finally quenching to room temperature. The medium-carbon silicon-manganese-chromium-nickel series low alloy steel treated by using the method disclosed by the invention has the tensile strength of 1580MPa-2000MPa, the yield strength of 1340MPa-1870MPa, the ductility of 9.0-22.9 percent and the percentage reduction of area of 16.0-43.2 percent. The high-strength and high-toughness heat treatment method can be used for heat treatment of the medium-carbon silicon-manganese-chromium-nickel series low alloy steel.

Description

technical field [0001] The invention relates to a heat treatment method for high strength and toughness of low alloy steel. Background technique [0002] Medium-carbon silicon-manganese-chromium-nickel low-alloy steel is a low-alloy high-strength steel. Based on its high strength, it is mainly used in aircraft landing gear, rocket shell materials and engine pump cross shafts. The carbon content of medium-carbon silicon-manganese-chromium-nickel low-alloy steel is generally between 0.25% and 0.5%, and the total content of alloy elements is not higher than 5%, among which Cr, Ni and Mn elements can improve the hardenability of steel The addition of Mo and V elements can refine grains, improve the microstructure of steel, and improve the tempering ability of steel. One of the traditional heat treatment processes for medium-carbon silicon-manganese-chromium-nickel low-alloy steel is low-temperature tempering heat treatment after quenching. Through this process, the tensile stre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21D1/20C21D1/22
Inventor 朱景川崔玉玲来忠红刘勇王慧
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap