Method for preparing cigarette flaky carbonaceous heat source materials by calcium salt

Abstract

The invention discloses a method for preparing cigarette flaky carbonaceous heat source materials by calcium salt. The method includes the steps of mixing sodium alginate, ammonium alginate or potassium alginate with carbon powder and water according to a mass ratio of the sodium alginate, ammonium alginate or potassium alginate to the carbon powder of 1:5-45, stirring to colloids, then extruding the colloid into flakes, and enabling the flakes to fully contact with calcium salt solution to obtain cured substances; and subjecting the cured substances to rinsing and drying to enable moisture content to reach 10-20% so as to obtain the cigarette flaky carbonaceous heat source materials. Harm caused by the fact that fiberglass is inhaled into a human body is reduced, and combustibility of carbonaceous heat sources is improved; and the method has the advantages of simplicity, short production cycle, low cost and the like.

Description

technical field [0001] The invention belongs to the field of cigarettes, and in particular relates to a method for preparing sheet-shaped carbonaceous heat source materials for cigarettes used in low-temperature cigarettes by using calcium salts. Background technique [0002] Studies have shown that nicotine and most tobacco flavor components can be transferred to smoke at lower temperatures (300-500°C). If the temperature of the cigarette is lowered to below 600°C (the ignition point of tobacco is about 700°C), various harmful components of the smoke can be greatly reduced, while the aroma components are relatively less affected. Therefore, a cigarette that uses a carbonaceous heat source for dry distillation of tobacco components was invented. Among them, the carbonaceous heat source of R.J. Reynolds Tobacco’s Eclipse cigarette uses glass fiber wrapped carbon rods. However, the carbon rods are formed by extrusion. , the interior is dense, and in order to form hot air flow...

AI Technical Summary

Problems solved by technology

Therefore, a cigarette that uses a carbonaceous heat source for dry distillation of tobacco components was invented. Among them, the carbonaceous heat source of R.J. Reynolds Tobacco’s Eclipse cigarette uses glass fiber wrapped carbon rods. However, the carbon rods are formed by extrusion. , the interior is dense, and in order to form hot air flow, the outer layer needs to be wrapped with breathable glass fiber. Some studies believe that even if such particles can be trapped by the filter material, they will inevitably be adsorbed on the filter during packaging and other processes, resulting in inhalation and harm. Healthy, dense carbon rods are also harder to ignite than thinner carbon filaments