Preparation method of fluorine-containing acrylate terpolymer emulsion

An acrylate terpolymer and acrylate technology, applied in fiber processing, textiles and papermaking, etc., can solve the problems of high cost of initiators and emulsifiers, unfavorable for large-scale popularization and application, and achieve the effect of improving adhesion

Active Publication Date: 2013-06-05
SHANDONG UNIV
View PDF8 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above-mentioned fluorine-containing polyacrylate emulsion method mainly has two problems: one is that most of the perfluorocarbon side chains of the prepared fluorine-containing polyacrylate emulsion contain fluorine carbon atoms ≥ 8, which has a certain bioaccumulation and biological toxicity, the relevant bills have restricted or banned the use; the second is that the cost of initiators and emulsifiers used is relatively high, which is not conducive to large-scale promotion and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of fluorine-containing acrylate terpolymer emulsion
  • Preparation method of fluorine-containing acrylate terpolymer emulsion
  • Preparation method of fluorine-containing acrylate terpolymer emulsion

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] (1) Add 35ml of deionized water, 10ml of acetone, 4.55g of perfluorohexyl ethyl acrylate, 9.30g of stearyl acrylate, 2-((2-hydroxyethyl)sulfonyl)ethyl acrylate into a 100ml reaction bottle Esters 1.20g, OP-10 (non-ionic surfactant) 0.46g, anionic surfactant sodium dodecyl sulfate 0.25g, dodecyl mercaptan 0.10g, high-speed shearing at 40°C for 1h, then ultrasonic emulsification After 0.5h, a milky white pre-emulsion was obtained.

[0048] Take 0.11 g of the initiator ammonium persulfate, dissolve it in 10 ml of deionized water, and prepare a solution for later use.

[0049] (2) In a 100ml reaction vessel equipped with stirring, reflux condenser, thermometer, and constant pressure dropping funnel, pass nitrogen protection, add 1 / 2 mass of pre-emulsion prepared in step (1) and 1 / 3 mass The initiator was heated to 80°C to react, and blue fluorescence appeared after 1 hour of reaction, then the remaining pre-emulsion and initiator were added dropwise, and the addition was c...

Embodiment 2

[0051] (1) Add 35ml of deionized water, 10ml of acetone, 6.07g of perfluorohexyl ethyl acrylate, 7.67g of lauryl acrylate, and 2-((2-hydroxyethyl)sulfonyl)ethyl acrylate into a 100ml reaction bottle in sequence 1.36g, OP-100.46g, anionic surfactant sodium lauryl sulfate 0.26g, dodecyl mercaptan 0.072g, high-speed shearing at 40°C for 1h, and ultrasonic emulsification for 30min to obtain a milky white pre-emulsion.

[0052] Take 0.11 g of the initiator ammonium persulfate, dissolve it in 10 ml of deionized water, and prepare a solution for later use.

[0053] (2) The heating reaction temperature is 83° C., and other conditions are the same as (2) in Example 1.

Embodiment 3

[0055] (1) Add 35ml of deionized water, 10ml of acetone, 4.55g of perfluorohexyl ethyl acrylate, 9.35g of stearyl acrylate, 2-((2-hydroxyethyl)sulfonyl) ethyl acrylate into a 100ml reaction bottle 1.44g of ester, 0.49g of NP-400, 0.30g of cationic surfactant cetyltrimethylammonium bromide, 0.062g of dodecyl mercaptan, high-speed shearing at 40°C for 1h, and ultrasonic emulsification for 35min to obtain milky white pre-emulsion.

[0056] Take 0.090 g of initiator ammonium persulfate, dissolve it in 10 ml of deionized water, and prepare a solution for later use.

[0057] (2) The reaction device, operation steps and other conditions are the same as (2) in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of a fluorine-containing acrylate terpolymer emulsion, which comprises the following steps: by taking perfluorohexyl ethyl (methyl) acrylate, high fatty alcohol (methyl) acrylate and a crosslinking monomer as main raw materials, taking persulfate as initiator and using composite emulsifier and a proper amount of co-emulsifier, chain transfer agent and deionized water, performing high-speed shearing at 40 DEG C for 0.5-2 hours, and then performing ultrasonic emulsification for 20-60 minutes to obtain a stable pre-emulsion; and taking part of the pre-emulsion, adding part of the initiator, heating to 50-90 DEG C, reacting for 0.5-1 hours, dropwisely adding the residual pre-emulsion and residual initiator, reacting for 3-6 hours while keeping the temperature, cooling, and regulating the pH value. The prepared emulsion is uniform and stable in particle size and does not contain harmful ingredients such as PFOS / PFOA and the like; and a coated film formed by the emulsion has favorable water repellency and oil repellency.

Description

technical field [0001] The invention relates to a method for preparing a fluorine-containing acrylate terpolymer emulsion, and belongs to the technical field of fluorine-containing acrylate polymer preparation. Background technique [0002] Fluorine is the most electronegative element in the periodic table. After the hydrogen in the carbon chain is replaced by a fluorine atom, the bond energy increases and the polarity increases. Fluorocarbon polymers have strong stability and extremely low surface energy. Fluorine-containing acrylate polymers are mainly used in water and oil repellent finishing of fabrics. [0003] At present, the fluorine-containing acrylate polymers used for fabric finishing are mainly composed of fluorine-containing (meth)acrylates, non-fluorine-containing (meth)acrylates and cross-linking monomers, and are mainly prepared by emulsion polymerization. Fluorine-containing (meth)acrylates provide water and oil repellency, non-fluorine-containing monomers c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F220/24C08F220/18C08F220/38C08F2/30C08F2/26D06M15/277
Inventor 王明刚孔胜男谭业邦刘舒
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com