Shrinkable film and method for manufacturing same

A shrink film, degradable film technology, used in chemical instruments and methods, synthetic resin layered products, transportation and packaging, etc., can solve problems such as increased film opacity, aluminum delamination or separation, and reduced productivity, to achieve uniform shrinkage sexual effect

Active Publication Date: 2013-05-08
KOLON IND INC
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the usability of the film deteriorates, causing an increase in opacity of the film, resulting in limited use, and the thermal properties of the blend resin itself lead to a decrease in productivity, and the shrinkage of the final product is difficult to control, resulting in limited use
[0004] In addition, aluminum deposited after the aluminum deposition process for use in food packaging, etc., may delaminate or separate because no other processes are performed during the manufacture of the final film, resulting in limited use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Shrinkable film and method for manufacturing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] 60% of polylactic acid resin as a raw material resin, polylactone (DAICELL Chemical Company, Celgreen), and silica having an average particle size of 2.7 μm so as to be 450 ppm in the final film were added and then blended to prepare a masterbatch. The masterbatch was dried at 110°C for 2 hours using a hot air dryer, melted and extruded at 200°C, and then rapidly cooled and solidified by a cooling roll at 25°C, thereby preparing an unstretched film.

[0044] The water-dispersed polyurethane coating composition was coated on one surface of the unstretched film by an in-line coating (ILC) process so that the coating thickness after drying thereof was 0.04 μm. The water-dispersible polyurethane coating composition contained 0.8 wt% polyurethane resin solids (DKC, Superflex 210), 0.1 wt% silicon-based wetting agent (DowCorning, Q2-5212) and the balance water.

[0045] The unstretched film coated with the water-dispersed polyurethane coating composition was passed through a ...

Embodiment 2

[0048] A film was produced in the same manner as in Example 1 except that 45 wt % of polylactone was used to prepare the masterbatch, and the physical properties of the film are shown in Table 1.

Embodiment 3

[0050] A film was produced in the same manner as in Example 1 except that 30 wt% of polylactone was used to prepare the masterbatch, and the physical properties of the film are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a film for packaging food and to a method for manufacturing same. More particularly, the present invention relates to a film for packaging food and to a method for manufacturing same, wherein the film has superior flexibility, transparency, and biodegradability, and has excellent adhesion to a metal coating layer to achieve improved moisture barrier properties.

Description

technical field [0001] The following disclosure relates to a food packaging film and its manufacturing method, and more specifically, to a film capable of excellent adhesion to a metal deposition layer and thereby maintaining excellent moisture resistance while having high flexibility, transparency A food packaging film with high performance and biodegradability and a method for manufacturing the same. Background technique [0002] Petroleum-derived polyethylene, polypropylene, polyvinyl chloride, polystyrene, polyester, etc. are used to make conventional plastic shrinkable films. Since these shrinkable films are chemically and biologically stable, they take a very long time to decompose, which causes serious environmental problems. [0003] Currently, conventionally used biodegradable shrinkable films are mainly made of polylactic acid, but their use is limited because of their low shrinkage and brittleness due to a crystallization phenomenon during film manufacturing. In...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B15/08B32B15/20B32B27/04C08J7/043
CPCC08J2367/04C08J7/04C08J2475/04B32B27/08C08J7/045Y10T428/265Y10T428/31565Y10T428/31605C08J7/0423C08J7/043C08L67/04C23C14/20B29C55/08B32B15/09
Inventor 金东珍金时敏金允照宋起相
Owner KOLON IND INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com