PVDC copolymer emulsion for wear-resistant water-based floor paint as well as preparation method and application thereof

A technology of copolymerization emulsion and floor paint, applied in the direction of coating, etc., can solve the problems of environmental and human health hazards, insufficient wear resistance, no flame retardancy, etc., and achieve good environmental protection, quality improvement, and good safety. Effect

Active Publication Date: 2013-04-17
海南聚能创新服务有限公司
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the floor paints used in the market are mainly solvent-based. Solvent-based floor paints have the advantages of low film-forming temperature, strong adhesion, high wear resistance, and good water resistance. However, they will release a large amount during production and use. Volatile organic compounds, which bring certain harm to the environment and human health; with the enhancement of people's awareness of environmental protection and safety, the use of water-based floor paint instead of solvent-based floor paint has become a future development trend
At present, relevant research has also made some progress, such as the patent application of CN200810030503, which discloses a water-based paint that can be used for floors. Its components include acrylic acid emulsion, glycerin, xylitol, sodium pyrophosphate, water, and have good environmental protection. property, but this water-based paint has insufficient abrasion resistance when it is used for flooring; the patent application of CN201010163994 discloses a kind of water-based acrylic polyurethane topcoat, which is prepared by adding auxiliary agents such as titanium dioxide and talcum powder with water-based acrylic resin as base material, Good water resistance, weather resistance, chemical resistance and high abrasion resistance, but not flame retardant

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PVDC copolymer emulsion for wear-resistant water-based floor paint as well as preparation method and application thereof
  • PVDC copolymer emulsion for wear-resistant water-based floor paint as well as preparation method and application thereof
  • PVDC copolymer emulsion for wear-resistant water-based floor paint as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012]

[0013] The specific preparation process is: add 280g of potassium superphosphate to 8kg of water to obtain an aqueous solution of potassium superphosphate initiator; mix 80kg of water, 40kg of vinylidene chloride, 50kg of vinyl chloride, 7kg of acrylonitrile, 3kg of butyl acrylate, and dodecylbenzenesulfonate Add sodium phosphate 1.2kg, OP-10200g, and ammonium hydrogen phosphate 20g into the reactor and mix evenly, add potassium superphosphate initiator aqueous solution, when the reaction pressure drops to zero, the reaction ends, and adding potassium hydroxide to adjust the pH value is 2 to obtain PVDC copolymer emulsion with 50% solid content.

[0014] The physical index of the obtained wear-resistant water-based floor paint with PVDC copolymer emulsion is:

[0015]

[0016]

Embodiment 2

[0018]

[0019] The specific preparation process is: add 350g of potassium superphosphate to 8kg of water to obtain an aqueous solution of potassium superphosphate initiator; mix 60kg of water, 48kg of vinylidene chloride, 60kg of vinyl chloride, 8.4kg of acrylonitrile, 3.6kg of butyl acrylate, and Add 1.4kg of sodium benzenesulfonate, 300g of OP-10, and 20g of ammonium hydrogen phosphate into the reaction kettle and mix evenly, add an aqueous solution of potassium superphosphate initiator, when the reaction pressure drops to zero, the reaction ends, and then add potassium hydroxide to adjust the pH value to 2.2 , to obtain a PVDC copolymer emulsion with a solid content of 60%.

Embodiment 3

[0021]

[0022] The specific preparation process is: add 280g of potassium superphosphate to 8kg of water to obtain an aqueous solution of potassium superphosphate initiator; mix 80kg of water, 40kg of vinylidene chloride, 50kg of vinyl chloride, 7kg of acrylonitrile, 3kg of ethyl acrylate, and dodecylbenzenesulfonate Add 1.2kg of sodium phosphate, OP-4200g, and 20g of ammonium hydrogen phosphate into the reaction kettle and mix evenly, add potassium superphosphate initiator aqueous solution, when the reaction pressure drops to zero, the reaction ends, and adding triethylamine to adjust the pH value is 2 to obtain PVDC copolymer emulsion with 50% solid content.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a PVDC (polyvinyl dichloride) copolymer emulsion for a wear-resistant water-based floor paint, as well as a preparation method and an application thereof, and solves the problems of poor wear resistance, no flame resistance and the like. The wear-resistant water-based floor paint is prepared by taking a certain amount of vinylidene chloride, vinyl chloride, vinyl cyanide and acrylic ester as mixed monomers and carrying out emulsion polymerization. Due to the existence of chloride atoms, the water-based floor paint prepared with the PVDC copolymer emulsion is good in environmental friendliness, high in wear resistance and excellent in flame resistance; and a floor coated with the floor paint is better in safety, the product quality is improved and the product is popular with consumers.

Description

technical field [0001] The invention relates to a PVDC copolymer emulsion, in particular to a PVDC copolymer emulsion for wear-resistant water-based floor paint and its preparation method and application. Background technique [0002] At present, the floor paints used in the market are mainly solvent-based. Solvent-based floor paints have the advantages of low film-forming temperature, strong adhesion, high wear resistance, and good water resistance. However, they will release a large amount during production and use. The volatile organic compounds in the floor will bring certain harm to the environment and human health; with the enhancement of people's awareness of environmental protection and safety, the use of water-based floor paint instead of solvent-based floor paint will become a future development trend. At present, relevant research has also made some progress, such as the patent application of CN200810030503, which discloses a water-based paint that can be used for...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F214/10C08F214/06C08F220/14C08F220/18C08F2/26C08F2/30C09D127/08C09D127/06
Inventor 方勇邢青涛
Owner 海南聚能创新服务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap