Laser-transmission welded connection method

A technology of laser transmission welding and connection method, which is applied in the field of improving the connection strength of metal and polymer laser transmission welding, can solve problems such as welding seam damage, and achieve the effect of firm local connection and improved connection strength

Inactive Publication Date: 2013-04-03
JIANGSU UNIV
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The document "The Effect of Laser Shock Surface Strengthening on the Mechanical Properties of Welded Joints" describes a method for surface strengthening treatment of welded joints to improve tensile strength. This method is to improve the strength of welded connections after welding. In transmission welding Inevitably cause damage to the weld seam after welding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Laser-transmission welded connection method
  • Laser-transmission welded connection method
  • Laser-transmission welded connection method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] Below in conjunction with specific embodiment the present invention is further described, weld transparent nylon and 304 stainless steel metals with the present invention.

[0017] Welding preparation: The selected welding transparent light-transmitting material nylon 13 has a size of 10x10x2mm, and the light-absorbing material 304 stainless steel 15 has a size of 10x10x0.6mm. The laser transmission welding laser adopts a continuous energy semiconductor laser generator 7 with a maximum power of 130w and a wavelength of 980nm±10nm.

[0018] Surface treatment of weldment: Ultrasonic cleaning of sample 304 stainless steel 15 with ethanol to remove surface impurities, after drying, place it on the workbench of precision machining machine tool, select Φ0.5mm round micro-shaft tool electrode, apply electrolysis The liquid is 5% sodium nitrate aqueous solution, the static pressure between the selected workpiece and the tool is 2.0N, the processing time is 2min, the abrasive is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
depthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a laser-transmission welded connection method, which belongs to the technical field of laser transmission welding, and particularly relates to laser transmission welding between metals and polymers. The laser-transmission welded connection method comprises the following steps of: firstly, carrying out micro-ultrasonic electrolysis combined machining process on the to-be-welded surface of a metal material so as to form concave pits in the surface of the metal material; connecting a lower-layer light absorption material which is the metal the surface of which is subjected to the micro-ultrasonic electrolysis combined machining process, and an upper-layer light absorption material which is a polymer in an overlapping manner, clamping the two light absorption materials by a restraint layer, and applying a welding pressure to the light absorption materials; and carrying out laser transmission welding on the light absorption materials by a semiconductor laser so as to enable a surface temperature to fast reach a melting point of the upper-layer polymer and the surface of the polymer to be melted, thus forming an holding-on interface with a riveted structure at a weld joint and improving the connecting strength of laser-transmission welding since the concave pits are formed in the surface subjected to the micro-ultrasonic electrolysis combined machining process of the lower-layer metal, and the polymer with the melted surface layer flows into the concave pits under the action of the welding pressure.

Description

technical field [0001] The invention belongs to the technical field of laser transmission welding, in particular to a method capable of improving the connection strength of metal and polymer laser transmission welding. The micro-ultrasonic electrolytic composite processing method is used to form pits on the metal surface. During laser transmission welding, the molten polymer flows into the pits under the action of welding pressure, forming a riveting interface at the weld, increasing the metal and The connection contact area of ​​the polymer is improved, thereby achieving an increase in the connection strength of the laser transmission welding. Background technique [0002] At present, laser transmission welding technology is widely used in the field of welding processing of the same and dissimilar materials such as polymers and polymers, and polymers and metals. Its characteristics are: fast, non-contact, accurate, small heat-affected zone, etc. With the development of las...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C65/16B29C65/64B23H5/08
CPCB29C65/1616B29C65/1635B29C65/1654B29C65/44B29C66/02B29C66/1122B29C66/30325B29C66/41B29C66/43B29C66/71B29C66/742B29C66/74283B29C66/8122B29C66/81267B29C66/8322B29C66/836B29C66/9221B29C66/929B29C66/939B29K2077/00B29K2909/08
Inventor 刘会霞赵振关陈浩黄创严长顾宇轩张迪马友娟邱唐标李品王霄
Owner JIANGSU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com