Waterborne epoxy antirust paint and preparation method

A water-based epoxy and anti-rust paint technology, applied in the field of anti-rust paint, can solve the problems of poor low-temperature curing, endangering human health, polluting the environment, etc., and achieve the effects of excellent water resistance, excellent anti-rust, and good adhesion

Active Publication Date: 2013-03-27
ANHUI KAILIN ADVANCED MATERIAL CO LTD
View PDF7 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Defects of solvent-based epoxy resin antirust paint: 1. Poor outdoor weather resistance; 2. Poor low-temperature curing; 3. Release a small amount of toxic and harmful substances, endangering human health and polluting the environment
[0007] Although the existing water-based anti-rust paint can avoid the defects of solvent-based epoxy resin anti-rust paint to a certain extent, there are limitations in stability, acid and alkali resistance and other comprehensive properties, which cannot meet market demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterborne epoxy antirust paint and preparation method
  • Waterborne epoxy antirust paint and preparation method
  • Waterborne epoxy antirust paint and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0083] A kind of water-based epoxy antirust paint, described antirust paint mainly is made up of A component and B component by mass ratio 2.5:1:

[0084] 1) The component A includes the following components by mass percentage:

[0085]

[0086] The sum of the above components is 100%;

[0087] Wherein, the millbase mixture comprises the following components by mass percentage:

[0088]

[0089] 2) The B component is water-based epoxy curing agent AB-HGF.

[0090] The preparation method of described waterborne epoxy antirust paint, comprises the following steps:

[0091] 1) First prepare the millbase mixture according to the formula quantity, and the millbase mixture is obtained by pre-dispersing each component and then grinding;

[0092] 2) Mix, stir, and filter the millbase mixture, epoxy resin emulsion, and additives obtained in step 1) according to the formula to obtain the component A;

[0093] 3) Pack the components A and B obtained in step 2) according to the ...

Embodiment 2

[0095] A kind of water-based epoxy antirust paint, described antirust paint mainly is made up of A component and B component by mass ratio 7.5:1:

[0096] 1) The component A includes the following components by mass percentage:

[0097]

[0098] The sum of the above components is 100%;

[0099] Wherein, the millbase mixture comprises the following components by mass percentage:

[0100]

[0101]

[0102] 2) The B component is water-based epoxy curing agent AB-HGT.

[0103] The preparation method is the same as in Example 1.

Embodiment 3

[0105] A kind of waterborne epoxy antirust paint, described antirust paint is made up of A component and B component by mass ratio 2:1:

[0106] 1) The component A includes the following components by mass percentage:

[0107]

[0108] The sum of the above components is 100%;

[0109] Wherein, the millbase mixture comprises the following components by mass percentage:

[0110]

[0111] 2) The B component is water-based epoxy curing agent AB-HGA.

[0112] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thermal resistanceaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a waterborne epoxy antirust paint and a preparation method. The antirust paint mainly comprises a component A and a component B; the component A comprises the following constituents in percentage by mass: 40-55% of paint paste mixture, 43-58% of epoxy resin emulsion and 1.2-8% of auxiliary II, wherein the total of the constituents aforementioned is 100% by weight; the paint paste mixture comprises the following constituents in percentage by mass: 40-85% of pigments and fillers, 0.3-6% of auxiliary I and the balance of water; and the component B is a curing agent. The preparation method comprises the following steps of: preparing the paint paste mixture according to prescription amounts, and mixing and stirring the paint paste mixture, the epoxy resin emulsion and the auxiliary II according to prescription amounts to obtain the component A; and packaging the component A and the component in a ratio by mass. The waterborne epoxy antirust paint obtained by the prescription disclosed by the invention is excellent in water-resistant, oil-resistant, acid-base-resistant, salt-mist-resistant performances and the like, excellent in anti-rust and anti-corrosion performances, and good in mechanical performances of adhesion force, flexibility, impact resistance and the like.

Description

technical field [0001] The invention relates to the technical field of antirust paint, in particular to a water-based epoxy antirust paint and a preparation method thereof. Background technique [0002] As people pay more and more attention to environmental protection, safe production, etc., as well as awareness of sustainable and healthy development, countries all over the world have higher and higher environmental protection requirements for coatings. The level of VOC content has become a measure of whether a coating is It is the standard of environmental protection paint. Driven by national environmental protection laws and regulations, the development of my country's coatings industry is moving towards the direction of convenient construction, resource saving, health and environmental protection. Safe, non-toxic and efficient water-based coatings are growing rapidly by leaps and bounds. Therefore, promoting the development, production and use of water-based coatings has...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D5/08
Inventor 王和山
Owner ANHUI KAILIN ADVANCED MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com