Soft tinning raw steel plate and manufacture method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A manufacturing method and steel plate technology, which is applied in the field of steel plate production, can solve problems such as excessive inclusions of Al2O3, achieve the effects of reducing inclusion content and improving formability
Inactive Publication Date: 2013-02-06
ANGANG STEEL CO LTD
View PDF8 Cites 16 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0008] The purpose of the present invention is to solve the problem of excessive aluminum oxide inclusions in the prior art steel, and to provide a soft tin-plated original steel plate that can meet the requirements of the continuous annealing production method and its manufacturing method
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0028] The chemical composition of steel is: C 0.01%, Si 0.01%, Mn 0.30%, P 0.01%, S 0.008%, Al 0.02%, N 0.002%, O 0.001%, Ti 0.07%, the rest is Fe and some inevitable Impurity elements; the oxygen activity at the end of the converter is controlled below 0.04%; the maximum continuous annealing temperature is 720℃, the over-aging temperature is 450℃, and the leveling elongation is 1.0%.
[0029] The surface Rockwell hardness (HR30Tm) value of the cold rolled tin plate after annealing is 56, the inclusion grade is D0, and there is no yield platform.
Embodiment 2
[0031] The chemical composition of steel is: C 0.002%, Si 0.01%, Mn 0.15%, P 0.007%, S 0.004%, Al 0.00%, N 0.001%, O 0.0008%, Ti 0.04%, Ca 0.001%, and the rest are Fe and Some unavoidable impurity elements; the oxygen activity at the end of the converter is controlled below 0.03%; the maximum continuous annealing temperature is 780℃, the over-aging temperature is 410℃, and the flat elongation is 1.7%.
[0032] The surface Rockwell hardness (HR30Tm) of the cold rolled tin plate after annealing is 52, the inclusion grade is D0, and there is no yield platform.
Embodiment 3
[0034] The chemical composition of steel is: C 0.002%, Si 0.01%, Mn 0.13%, P 0.012%, S 0.006%, Al 0.001%, N 0.001%, O 0.0008%, Ti 0.02%, Nb 0.02%, Mg 0.001%, The rest are Fe and some unavoidable impurity elements; the end-point oxygen activity of the converter is controlled below 0.03%; the maximum continuous annealing temperature is 800℃, the over-aging temperature is 430℃, and the flat elongation is 2.2%.
[0035] The surface Rockwell hardness (HR30Tm) of the cold rolled tin plate after annealing is 50, the inclusion grade is D0, and there is no yield platform.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides a soft tinning raw steel plate and a manufacture method of the soft tinning raw steel plate. The steel plate is prepared from the following chemical components in percentage by weight: 0.0001 to 0.010% of C, not greater than 0.02% of Si, 0.10 to 060% of Mn, not greater than 0.02% of P, not greater than 0.02% of S, not greater than 0.02% of Al, not greater than 0.002% of N, not greater than 0.005% of O, 0.005 to 0.05% of Nb, and/or 0.005 to 0.07% of Ti, and the balance of Fe. The manufacture method comprises the technical processes as follows: preprocessing molten iron-melting through a converter-refining outside the converter-protectively casting-performing hot rolling-pickling and performing cold rolling-annealing- inspecting-packaging; activity of end-point oxygen of a molten iron is controlled to reach a value of 0.02 to 0.06% during melting by the converter; the molten iron is processed in vacuum during being refined outside the furnace; contents of alloy elements such as C and Mn are precisely controlled; and the contents of gases such as oxygen and nitrogen in the molten iron can be reduced. By adopting the manufacture method provided by the invention, a problem that the soft tinning raw steel plate is relatively hardly produced by a continuous annealing method can be solved, content of inclusion in steel can be decreased, and a forming performance of the steel plate can be improved.
Description
Technical field [0001] The invention belongs to the technical field of steel plate production, and particularly relates to a soft tinned raw steel plate and a manufacturing method thereof. Background technique [0002] Tin plate is a symbolic and basic product of a large modern steel company. It is the most direct manifestation of the company's smelting, rolling and coating level. The production of tin plate is a systematic project, and each process will affect the final performance of the material. Among them, the steel purity control and inclusion control in the steelmaking process are the basis for obtaining high-quality cold-rolled tin plate. [0003] Generally, the tin plate materials used for beverage cans and food cans are distinguished by the degree of quenching and tempering. The Rockwell hardness HR30Tm of the quenching and tempering degree indicates that the primary cold-rolled product is divided into T1-5 according to the hardness of the material, and the secondary col...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.