Aerated concrete wall material containing river silt and preparation method thereof

A technology of aerated concrete and sand, applied in ceramic products, manufacturing tools, other household appliances, etc., can solve the problems of reduced profit of aerated concrete, impact on ecological environment, high material cost, light weight and protection of ecological environment. , the effect of improving production efficiency

Active Publication Date: 2013-02-06
HUAHONG GROUP YIXING HUAHONG NEW WALL BUILDING MATERIALS
View PDF6 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the main component of processing and manufacturing air-entrained concrete is fly ash or sand. Due to the high cost of fly ash or sand itself, and because the country needs macro-economic regulation and control, the construction industry has entered a low tide, which has greatly reduced the profit of air-entrained concrete manufacturing. In particular, sand is used to make air-entrained concrete wall materials. Due to excessive sand mining, it is not advisable to greatly affect the ecological environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] This embodiment is an aerated concrete wall material containing river silt and sand, which is composed of mixture A and mixture B, and the weight ratio of mixture A and mixture B is 5:1.

[0034] The weight percentage components of the mixture A are: river silt: 60%, cement: 5%, lime: 13%, gypsum powder: 1%, aluminum powder: 10%, foam stabilizer 11%.

[0035] The weight percentage components of the mixture B are: base material: 40%, magnesium chloride solution: 15%, magnesium oxide: 5%, binder: 2%, additive: 4%, cement: 26%, gypsum powder: 3%, Water reducing agent: 1%, coagulant: 1%, lithium carbonate: 1%, fiber: 1%, stable masterbatch: 1%; the weight percentage concentration of magnesium chloride solution is 39%; the water reducing agent is lignosulfonic acid Sodium salt superplasticizer, naphthalene superplasticizer, aliphatic superplasticizer or polycarboxylate superplasticizer; coagulant water glass or aluminum sulfate.

[0036] The weight percentage components of ...

Embodiment 2

[0053] This embodiment is an aerated concrete wall material containing river silt and sand, which is composed of mixture A and mixture B, and the weight ratio of mixture A and mixture B is 3:1.

[0054] The weight percentage components of the mixture A are: river silt: 75%, cement: 1%, lime: 14%, gypsum powder: 2%, aluminum powder: 6%, foam stabilizer 2%.

[0055] The weight percentage components of the mixture B are: base material: 41%, magnesium chloride solution: 10%, magnesium oxide: 6%, binder: 3%, additive: 4%, cement: 25%, gypsum powder: 4%, Water reducing agent: 1%, coagulant: 1%, lithium carbonate: 2%, fiber: 1%, stable masterbatch: 2%; the weight percentage concentration of magnesium chloride solution is 40%; the water reducing agent is lignosulfonic acid Sodium salt superplasticizer, naphthalene superplasticizer, aliphatic superplasticizer or polycarboxylate superplasticizer; coagulant water glass or aluminum sulfate.

[0056] The weight percentage components of th...

Embodiment 3

[0073] This embodiment is an aerated concrete wall material containing river silt and sand, which is composed of mixture A and mixture B, and the weight ratio of mixture A and mixture B is 1:1.

[0074] The weight percentage components of the mixture A are: river silt: 65%, cement: 10%, lime: 15%, gypsum powder: 1%, aluminum powder: 7%, foam stabilizer 2%.

[0075] The weight percentage components of the mixture B are: base material: 40%, magnesium chloride solution: 10%, magnesium oxide: 5%, binder: 5%, additive: 5%, cement: 25%, gypsum powder: 5%, Water reducing agent: 1%, coagulant: 1%, lithium carbonate: 1%, fiber: 1%, stable masterbatch: 1%; the weight percentage concentration of magnesium chloride solution is 42%; the water reducing agent is lignosulfonic acid Sodium salt superplasticizer, naphthalene superplasticizer, aliphatic superplasticizer or polycarboxylate superplasticizer; coagulant water glass or aluminum sulfate.

[0076] The weight percentage components of t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to an aerated concrete wall material and a preparation method thereof, in particular to an aerated concrete wall material containing river silt and a preparation method thereof. The aerated concrete wall material comprises the following main components in percentage by weight: 60-75% of river silt, 1-10% of cement, 13-28% of lime, 1-2% of gypsum powder, 6-10% of aluminum powder and 2-11% of foam stabilizing agent, and the sum of weight percentages of the components is 100%. In the invention, river silt dug out by regulating the Yangtze River can be effectively utilized, energy is saved, emission is reduced, the ecological environment is protected, and the processed aerated concrete wall material also has high compressive strength and high bending strength.

Description

technical field [0001] The invention relates to an aerated concrete wall material and a preparation method thereof, in particular to an aerated concrete wall material containing river silt and sand and a preparation method thereof. Background technique [0002] The traditional bricks used in construction generally use solid clay bricks as sintered ordinary bricks (commonly known as red bricks). Most of these bricks are made of cultivated land clay, which seriously damages the cultivated land and causes the loss of a large amount of land resources. Simultaneously in its burning process, also can waste a large amount of fuel and cause air pollution. In addition, the current red bricks have many disadvantages such as heavy weight, poor processing performance, and poor sound insulation performance. With the progress of society and the rapid development of construction and decoration industries, more and more attention is paid to the requirements for aerated concrete wall materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/32C04B38/00B28B11/24
Inventor 王博王毓春
Owner HUAHONG GROUP YIXING HUAHONG NEW WALL BUILDING MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com