High-strength thick steel plate for large heat input welding

A technology for high-intensity welding and thick steel plates, which is applied to the thick steel plate for high-intensity welding and its manufacturing field, and can solve the problem that the adverse effect is not obvious, the weldability of high-intensity energy is unfavorable, and no welding thermal simulation or physical welding is given. Process conditions, etc.

Active Publication Date: 2012-11-07
BAOSHAN IRON & STEEL CO LTD
View PDF13 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In fact, the addition of Nb is detrimental to the large input energy weldability of steel, but this adverse effect is not obvious when the welding input energy is small (<100kJ / cm).
[0006] Although CN101050504A and CN101407893A claimed that HAZ has excellent low-temperature toughness after high-energy input welding, they did not provide welding thermal simulation or physical welding process conditions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength thick steel plate for large heat input welding
  • High-strength thick steel plate for large heat input welding
  • High-strength thick steel plate for large heat input welding

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0043] Table 1 The chemical composition of the steel plate of the embodiment of the present invention, % by weight

[0044] serial number

C

Si

P

S

mn

Al

N

Ti

Cr

B

1

0.07

0.15

0.0080

0.0031

1.70

0.06

0.009

0.013

0.10

0.0016

2

0.08

0.13

0.0077

0.0042

1.78

0.02

0.006

0.011

0.18

0.0015

[0045] 3

0.08

0.14

0.0075

0.0035

1.51

0.08

0.020

0.012

0.21

0.0023

4

0.09

0.11

0.0076

0.0041

1.55

0.05

0.015

0.009

0.16

0.0018

5

0.10

0.05

0.0085

0.0038

1.61

0.03

0.018

0.006

0.24

0.0024

6

0.08

0.12

0.0084

0.0032

1.79

0.10

0.007

0.005

0....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a high-strength thick steel plate for large heat input welding. The high-strength thick steel plate comprises, by weight percent, 0.07-0.10% of C, 0.05-0.15% of Si, 1.5-1.8% of Mn, not more than 0.01% of P, not more than 0.005% of S, 0.02-0.10% of Al, 0.006-0.02% of N, 0.005-0.015% of Ti, 0.10-0.25% of Cr, 0.0015-0.0025% of B, not more than 0.0030% of O, and the balance Fe and other inevitable impurity. A manufacture method of the high-strength thick steel plate includes: smelting in a converter or an electric furnace, secondary refining in a vacuum furnace, casting ingots, reheating the ingots, and performing TMCP (thermal mechanical control processing) and fast cooling to obtain the steel plate. The thick steel plate with a high strength of 600MPa is low in cost, and has excellent low-temperature toughness in the large heat input welding.

Description

technical field [0001] The invention relates to a thick steel plate for high heat input welding and a manufacturing method thereof, in particular to a thick steel plate for 600MPa grade high strength and low cost large heat input welding and a manufacturing method thereof. Background technique [0002] Low-alloy high-strength steel is one of the most widely used structural materials in engineering applications, and is widely used in oil and gas pipelines, shipbuilding, bridges, high-rise buildings, pressure vessels, oil storage tanks and other industries. In order to improve production efficiency, the above-mentioned industries have higher and higher requirements on the weldability of steel plates, especially the weldability of large heat input, but high heat input welding can easily cause the toughness of the weld seam and its surrounding welding heat-affected zone (HAZ) Severe deterioration makes welded joints prone to brittle fracture. For traditional steel plates such a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/38C22C38/32C21D8/02
Inventor 王巍王焕荣刘刚
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products