Hydrothermal preparation method of TiO2-rGO composite photochemical catalyst

A catalyst and composite light technology, applied in chemical instruments and methods, physical/chemical process catalysts, chemical/physical processes, etc., to achieve the effect of simple operation, low equipment requirements, and easy mass synthesis

Inactive Publication Date: 2012-10-31
WUHAN UNIV OF TECH
View PDF2 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As far as we know, there is no information about the one-step preparation of TiO by hydrothermal method using pure water as solvent without any admixture as reducing agent. 2 Composite with reduced graphene (TiO 2 -rGO) as a highly active photocatalyst

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrothermal preparation method of TiO2-rGO composite photochemical catalyst
  • Hydrothermal preparation method of TiO2-rGO composite photochemical catalyst
  • Hydrothermal preparation method of TiO2-rGO composite photochemical catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] TiO 2 -rGO composite photocatalyst was prepared as follows: (1) 0.5 g commercial P25 TiO 2 After pretreatment at 550°C for 2 h; (2) dissolving graphene oxide in deionized water and ultrasonic treatment to form a uniform graphene oxide (GO) solution, in which the concentration of graphene oxide was 0.05 wt %; (3) adding 0.5 g pretreated TiO 2 Disperse into 10 ml graphene oxide solution and stir for 2 h to form stable TiO 2 -GO suspension; (4) TiO prepared above 2 -GO suspension was hydrothermally treated at 150°C for 5 h; the obtained product was washed three times and then dried in vacuum at 60°C for 6 h to obtain TiO 2 -rGO composite photocatalyst.

[0030] figure 1 is TiO 2 -Schematic diagram of the synthesis of rGO composites. As we all know, since graphene oxide contains many oxygen-containing functional groups, such as -OH, C=O, C-O-C and -COOH, it can be well dispersed in water to form a uniform and stable solution. figure 1 a is a schematic diagram of the s...

Embodiment 2

[0038] In order to test TiO 2 Effect of powder pretreatment temperature on TiO 2 - Influence of rGO nanocomposites, in addition to different pretreatment temperature, other reaction conditions are as follows: TiO 2 Powder pretreatment time (2 h), TiO 2 Powder mass (0.5 g), graphene oxide concentration (0.05 %) and volume (10 ml), stirring time (2 h), hydrothermal temperature (150 °C), hydrothermal time (5 h), drying temperature (60 °C ), drying time (6 h) etc. are all identical with embodiment 1. The results show that when the pretreatment temperature is 200 °C, TiO 2 The impurities adsorbed on the surface of the powder cannot be effectively removed, and the uniformity and suspension performance are not good after mixing with the graphene solution, which affects the TiO 2 Combination with graphene; when the pretreatment temperature is 350-600°C, TiO 2 The powder is mixed with the graphene solution to obtain a solution with good uniformity and suspension performance; when ...

Embodiment 3

[0040] In order to test TiO 2 Powder pretreatment time on TiO 2 - Influence of rGO nanocomposites, in addition to different pretreatment time, other reaction conditions are as follows: TiO 2 Powder pretreatment temperature (550°C), TiO 2 Powder mass (0.5 g), graphene oxide concentration (0.05 %) and volume (10 ml), stirring time (2 h), hydrothermal temperature (150 °C), hydrothermal time (5 h), drying temperature (60 °C ), drying time (6 h) etc. are all identical with embodiment 1. The results show that when the pretreatment time is 0.5 h, TiO 2 The impurities adsorbed on the powder surface were not effectively removed, which affected the formation of composite materials and the TiO 2 and graphene; when the pretreatment time is 1-3 h, TiO 2 The impurities adsorbed on the powder surface are effectively removed, forming a fresh interface, making TiO 2 It is easy to combine with the graphene surface; when the pretreatment time reaches 5 h, TiO 2 Too large powder particles ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a hydrothermal preparation method of a TiO2-rGO composite photochemical catalyst, sequentially comprising the following steps of: dispersing pretreated TiO2 into 10mL of graphene oxide solution prepared by step 2), and evenly stirring, so as to obtain stable TiO2-GO suspending liquid; and carrying out hydrothermal treatment under the temperature of 100-200DEG C for 0.5-10 hours, washing a product by three times, and carrying out vacuum drying, so as to obtain the TiO2-rGO composite photochemical catalyst. The hydrothermal preparation method has the benefit effects of taking purified water as a solvent, being simple to operate, and free from adding various reducing agents such as an organic surface active agent and an additive, thereby being a green and environment-friendly graphene oxide reduction method. The photoproduction-electron hole effective separation efficiency can be improved due to the high electronic mobility of reduced graphene, so that the photocatalysed performance of the TiO2 can be improved, and the hydrothermal preparation method has the advantages of being very simple to operate, low in equipment requirement, free from expressive reaction devices, easy to synthesize on a large scale, etc.

Description

Technical field [0001] The invention involves TIO 2 -Rgo composite optical catalyst's water heat system. technical background [0002] Due to the increasingly serious air and water pollution, the application of photocatalytic degradation organic pollutants has attracted more and more attention.Titanium dioxide is one of the most widely studied photocatalysts with optical catalytic activity, which can effectively degrade various organic matter.However, titanium dioxide photocatalysts are not widely used. The main reason is that titanium dioxide in ultraviolet light can produce photochemical electron-grounded pairs, while photocopy electronics-cave acupoints have a chemical effect on composite titanium dioxide and adsorbing pollutants.Lay the photocatalytic efficiency.Therefore, how the current challenge is to effectively prevent the compound of electronics-ground acupoints and increase TIO 2 Light catalytic activity.A series of modified strategies are applied to TIO 2 In the base ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J21/18
Inventor 王苹王进余火根杨小利段华军蔡浩鹏
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap