Transformation induced plasticity steel and preparation method thereof

A transformation-induced plasticity, strip technology, applied in metal material coating process, hot dipping process, coating, etc.

Inactive Publication Date: 2012-10-24
SHOUGANG CORPORATION
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But for the jet hot-dip galvanizing annealing production line that is generally used at present, this problem cannot be solved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Transformation induced plasticity steel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A kind of phase transformation induced plasticity steel, its chemical composition weight percent is respectively:

[0029] C: 0.19%, Si: 0.5%, Mn: 1.9%, P: 0.008%, S: 0.005%, Alt: 0.9%, N: 0.005%, Nb: 0.03%, and the balance is Fe and impurities.

[0030] The preparation method of phase transformation induced plasticity steel in this embodiment specifically includes the following steps:

[0031] 1) Smelting: Add steel scrap to the converter for smelting. The end temperature of the first furnace during the smelting process is 1670-1690°C; the target temperature of the continuous pouring during the smelting process is 1660-1680°C; during the smelting process, Al-Fe alloy is used to resist Chemical powder deoxidation, the addition of Al-Fe alloy anti-chemical powder is 4kg / t; during the smelting process, slag is added during the tapping process, and the slag is added with the steel flow in the early stage of tapping, and the tapping amount reaches the total steel amount Be...

Embodiment 2

[0046] A kind of phase transformation induced plasticity steel, its chemical composition weight percent is respectively:

[0047] C: 0.21%, Si: 0.6%, Mn: 2.0%, P: 0.01%, S: 0.01%, Alt: 0.8%, N: 0.0008%, Nb: 0.04%, and the balance is Fe and impurities.

[0048] The preparation method of phase transformation induced plasticity steel in this embodiment specifically includes the following steps:

[0049] 1) Smelting: Add steel scrap to the converter for smelting. The end point temperature of the first furnace during the smelting process is 1690°C; the target temperature at the end point of continuous casting during the smelting process is 1660°C; during the smelting process, Al-Fe is used for deoxidation. The addition amount is 4kg / t; during the smelting process, slag is added during the tapping process, and the slag is added along with the steel flow in the early stage of tapping, and all the slag is added before the tapping amount reaches 1 / 5 of the total steel amount, and every...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses transformation induced plasticity steel and a preparation method thereof and belongs to the technical field of cold rolling hot galvanizing. The transformation induced plasticity steel comprises by mass, 0.18%-0.21% of carbon, 0.6%-10.5% of silicon, 1.8%-2.0% of manganese, 0.03%-0.04% of niobium, no more than 0.01% of phosphorus, no more than 0.01% of sulphur, 0.8%-1.0% of all aluminum, no more than 0.005% of nitrogen and the balance ferrum. Based on a producing method of conventional jet cooling hot galvanizing, the transformation induced plasticity steel and the preparation method are used in 780 MPa automobile cold rolling hot galvanizing, and the transformation induced plasticity steel not only can meet design strength and has good welding and plastic performances.

Description

technical field [0001] The invention belongs to the technical field of cold-rolling and hot-dip galvanizing, and relates to a phase transformation-induced plasticity steel and a preparation method thereof. Background technique [0002] In order to reduce fuel consumption and emission reduction, it is necessary to reduce the weight of automobiles. On the contrary, in order to improve automobile safety, it will be necessary to increase the quality of automobiles. An effective means to solve this contradiction is to use high-strength steel and advanced high-strength steel. On the other hand, the corrosion resistance of automobiles has also become an increasing requirement for high-end automobiles. [0003] The microstructure of Transformation Induced Plasticity Steel (TRIP) consists of ferrite, bainite, retained austenite and a small amount of martensite. TRIP steels have well-matched strength and ductility due to the TRIP effect. The TRIP effect is that the retained austenit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/12C21D8/02C23C2/40
Inventor 姜英花邝霜尉冬王海全滕华湘刘光明
Owner SHOUGANG CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com