Nano titanium dioxide-type damping grease composition

A technology of nano-titanium dioxide and grease composition, which is applied in the field of damping and lubricating materials, can solve the problems of limited application occasions, different damping structure performance, poor adaptability, etc., and achieve high shear stability, high plastic compatibility, and prevent moisture Effect

Inactive Publication Date: 2012-05-02
SHENZHEN EUBO NEW MATERIAL TECH
View PDF13 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing damping structures (damping materials) have different performances, poor adaptability, and limited application occasions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] 1. Material composition and ratio measurement formula: see Table 1,

[0027] Table 1

[0028] Material composition

Specific material composition

Measuring formula

(A)

Polysiloxane Synthetic Base Oil, 500,000 cSt

100.0

(B)

Nano titanium dioxide, 10nm

20.0

(C)

A silane coupling agent

2.0

(D)

Ethylene Propylene Silicone Rubber Copolymer

10.0

(E)

PTFE

5.0

(F)

Zinc dialkyldithiocarbamate

1.0

[0029] 2. Process steps for making finished damping grease:

[0030] (1) Surface modification treatment of nano-titanium dioxide: Feed according to the formula, stir evenly and let it stand for 20 minutes; heat for 30 minutes, heat through a heat-conducting oil furnace, and control the temperature at 125°C; then cool for standby;

[0031] (2) Making the base grease: Feed according to the formula, stir evenly and let it stand for 30 minutes; then gr...

Embodiment 2

[0034] 1. Material composition and ratio measurement formula: see Table 2,

[0035] Table 2

[0036] Material composition

Specific material composition

Measuring formula

(A)

Polysiloxane Synthetic Base Oil, 1 million cSt

100.0

(B)

Nano titanium dioxide, 20nm

30.0

(C)

Methoxypolysiloxane

3.0

(D)

Polyisobutylene

7.0

(E)

Melamine cyanurate

8.0

(F)

Benzotriazole

1.5

[0037] 2. Process steps for making finished damping grease:

[0038] (1) Surface modification treatment of nano-titanium dioxide: feeding according to the formula, stirring evenly and then standing for 30 minutes; then heating for 30 minutes, heating through a heat-conducting oil furnace, and controlling the temperature at 135°C; then cooling for later use;

[0039] (2) Making base grease: Feed according to the formula, stir evenly and let it stand for 20 minutes; then grind, incl...

Embodiment 3

[0042] 1. Material composition and ratio measurement formula: see Table 3,

[0043] table 3

[0044] Material composition

Specific material composition

Measuring formula

(A)

Polysiloxane synthetic base oil, 1.5 million cSt

100.0

(B)

Nano titanium dioxide, 30nm

50.0

(C)

Titanate

5.0

(D)

Ethylene Propylene Silicone Rubber Copolymer

5.0

(E)

PTFE

5.0

(F)

2,6-di-tert-butyl-p-cresol

1.0

[0045] 2. Process steps for making finished damping grease:

[0046] (1) Surface modification treatment of nano-titanium dioxide: Feed according to the formula, stir evenly and let stand for 20 minutes; heat for 30 minutes, heat through a heat-conducting oil furnace, and control the temperature at 135°C; then cool for later use;

[0047] (2) Make the base grease; feed according to the formula amount, stir evenly and let it stand for 30 minutes; regrind, includin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of damping materials, and more particularly, provides a nano titanium dioxide-type damping grease composition, which comprises, in parts by weight: (A) 100.0 parts of polysiloxane synthetic base oil, (B) 5.0 to 50.0 parts of nano titanium dioxide, (C) 0.5 to 5.0 parts of modified surface treatment agent, (D) 1.0 to 10.0 parts of torsional force intensifier, (E) 3.0 to 10.0 parts of solid lubricant, and (F) 0.2 to 2.0 parts of antioxidant corrosion inhibitor. The finished damping grease prepared by these materials in the above proportions has excellent high / low temperature performance, wide applicable temperature range and high shear stability, is capable of controlling motion accurately and reducing noise, and can be widely applied to any part of a variety of optical instruments, electronic instruments, measurement instruments and the like, which requires the control for free motion. Meanwhile, the production process is simple and easily implementable, so the nano titanium dioxide-type damping grease composition is suitable for large-scale batch production.

Description

technical field [0001] The invention belongs to the field of damping lubricating materials, and in particular provides a nano-titanium dioxide type damping grease composition. Background technique [0002] The damping structure refers to the structure that combines the damping material and the component to consume the vibration. 目前,有关阻尼结构的文献报道较多,如中国专利CN201110104841.3、CN201020180385.1、CN200920183597.2、CN200920181534.3、CN200920135526.5、CN200920021859.5、CN200710200751.8、CN200610049632.2、CN200510010111.1、 CN200420048936.3, CN94215977.2, CN201010596292.1, etc. However, there are few reports on the development of damping materials, but in many fields, there is a great demand for high-quality damping structures (damping materials). In some occasions, it is necessary to use a damping structure to reduce the hazards caused by mechanical vibration and noise, and in some occasions it is necessary to use a damping structure to precisely control the action, and some electronic products ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M169/04C10M177/00C10N50/10C10N40/06
Inventor 杨发达李士成童蓉王虹岳风树
Owner SHENZHEN EUBO NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com