Nonmetal electrode material of vanadium redox battery and preparation method thereof

An electrode material, non-metal technology, applied in the field of vanadium batteries, to achieve the effects of compact structure, simple preparation process and low price

Inactive Publication Date: 2012-02-01
陶淞祥
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a non-metallic electrode material for a vanadium battery and a preparation method thereof, aiming at solving the problems existing when graphite felt or carbon felt is used as an electrode material of a vanadium battery, and improving the performance of a vanadium battery electrode

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Embodiment 1: A kind of raw material formulation and preparation method of vanadium battery non-metallic electrode material

[0039] The raw material formula is composed of the following substances in mass percentage:

[0040] (1) High-density polyethylene 10%

[0041] Among them, the melt index of high-density polyethylene is 2~4;

[0042] (2) Low-density polyethylene 35%

[0043] Among them, the melt index of low density polyethylene is 4~8;

[0044] (3) Mixture of calcium stearate and zinc stearate 2%

[0045] Among them, the mass mixing ratio of calcium stearate and zinc stearate is 1:0.25~1:0.5;

[0046] (4) Conductive carbon black 20%;

[0047] (5) Graphite 15%;

[0048] (6) Ethylene-octene copolymer 8%

[0049] Among them, the content of octene accounts for 20%~25% of the mass of the copolymer;

[0050] (7) Sodium alkylaryl sulfonate 5%;

[0051] (8) Polyoxyethylene fatty alcohol ether 2%;

[0052] (9) Stearic acid 3%.

[0053] On the basis of above-me...

Embodiment 2

[0074] Embodiment 2: A kind of raw material formulation and preparation method of vanadium battery non-metallic electrode material

[0075] The raw material formula is composed of the following substances in mass percentage:

[0076] (1) High-density polyethylene 25%

[0077] Among them, the melt index of high-density polyethylene is 2~4;

[0078] (2) Low-density polyethylene 20%

[0079] Among them, the melt index of low density polyethylene is 4~8;

[0080] (3) Mixture of calcium stearate and zinc stearate 3%

[0081] Among them, the mass mixing ratio of calcium stearate and zinc stearate is 1:0.25~1:0.5;

[0082] (4) Conductive carbon black 22%;

[0083] (5) Graphite 12%;

[0084] (6) Ethylene-octene copolymer 10%

[0085] Among them, the content of octene accounts for 20%~25% of the mass of the copolymer;

[0086] (7) Sodium alkylaryl sulfonate 3%;

[0087] (8) Polyoxyethylene fatty alcohol ether 3%;

[0088] (9) Stearic acid 2%.

[0089] The preparation method ...

Embodiment 3

[0090] Embodiment 3: A kind of raw material formulation and preparation method of vanadium battery non-metallic electrode material

[0091] The raw material formula is composed of the following substances in mass percentage:

[0092] (1) High-density polyethylene 12%

[0093] Among them, the melt index of high-density polyethylene is 2~4;

[0094] (2) Low-density polyethylene 25%

[0095] Among them, the melt index of low density polyethylene is 4~8;

[0096] (3) Mixture of calcium stearate and zinc stearate 1%

[0097] Among them, the mass mixing ratio of calcium stearate and zinc stearate is 1:0.25~1:0.5;

[0098] (4) Conductive carbon black 32%;

[0099] (5) Graphite 10%;

[0100] (6) Ethylene-octene copolymer 12%

[0101] Among them, the content of octene accounts for 20%~25% of the mass of the copolymer;

[0102] (7) Sodium alkylaryl sulfonate 2%;

[0103] (8) Polyoxyethylene fatty alcohol ether 5%;

[0104] (9) Stearic acid 1%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a nonmetal electrode material of a vanadium redox battery and a preparation method thereof. The nonmetal electrode material comprises the following raw materials in a prescription: 10-30% of high-density polyethylene, 20-40% of low-density polyethylene, 1-3% of a mixture of calcium stearate and zinc stearate, 20-40% of electroconductive carbon black, 10-30% of graphite, 8-12% of ethylene-octylene copolymer, 2-5% of sodium alkylarysulfonate, 2-5% of polyoxyethylene fatty alcohol ether and 1-3% of stearic acid. A preparation process comprises the step of uniform mixing and milling to prepare the electrode material. The nonmetal electrode material disclosed by the invention has the advantages of compacter material structure, no falling-off, no pollution to electrolyte, good machine-shaping performance, breakdown difficulty, long service life, easily obtainable raw materials, low price, simple preparation method, no toxicity, no pollution, and suitability to mass popularization and application.

Description

technical field [0001] The invention relates to the technical field of vanadium batteries, in particular to a non-metallic electrode material for a vanadium battery and a preparation method thereof. Background technique [0002] The vanadium battery is called a vanadium redox flow battery (Vanadium Redox Battery, abbreviated as VRB), which is a redox battery in which the active material is in a circulating liquid state. In work, vanadium battery is a secondary energy system that utilizes redox reactions between vanadium ions in different valence states for energy storage and conversion. Its characteristics are: no emission pollution, adjustable capacity, long cycle life, deep high current density discharge, fast charging, and high energy conversion rate. Therefore, it is widely used in systems such as power station peak regulation, large-scale photoelectric conversion, energy storage for wind power generation, uninterruptible power supply, and emergency power supply. [00...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/86H01M4/88
CPCY02E60/50
Inventor 陶淞祥
Owner 陶淞祥
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap