Natural rubber composite with electromagnetic shielding property and preparation method thereof

A technology of natural rubber and composite materials, applied in the field of electromagnetic shielding materials, can solve problems such as unsuitable for large-scale popularization and application, high manufacturing cost, complicated process, etc., and achieve excellent electromagnetic wave absorption performance, low manufacturing cost, and simple preparation method.

Inactive Publication Date: 2011-08-03
QINGDAO UNIV OF SCI & TECH
View PDF5 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, there are generally problems such as high manufacturing cost, complicated process, and easy pollution, which are not suitable for large-scale promotion and application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Fully disperse the chopped carbon fiber in a beater, filter the dispersion and fully dry it to obtain a chopped and dispersed carbon fiber monofilament with a fiber diameter of 3 μm and a length of 1 mm; in an internal mixer or an open mixer, first 100 parts by weight of natural rubber were masticated for 5 minutes, then 2 parts of stearic acid, 5 parts of zinc oxide, 1 part of antioxidant, 60 parts of carbon black, 3 parts of chopped carbon fiber, 3 parts of paraffin oil, 1 part of part of accelerator and 2.5 parts of sulfur, and then mixed for 8 minutes, and then pressed into tablets after mixing evenly to obtain the mixed rubber; the mixed rubber was parked at room temperature for 24 hours, and then vulcanized and formed on a 50T flat vulcanizing machine, and the vulcanized condition was 140 °C×30min to obtain the finished product.

[0019] According to the performance test, the tensile strength of the electromagnetic shielding natural rubber composite material is 14...

Embodiment 2

[0021] Fully disperse the chopped carbon fiber in a beater, filter the dispersion and fully dry it to obtain a chopped and dispersed carbon fiber monofilament with a fiber diameter of 6 μm and a length of 3 mm; in an internal mixer or an open mixer, first 100 parts by weight of natural rubber were masticated for 5 minutes, then 2 parts of stearic acid, 5 parts of zinc oxide, 1 part of antioxidant, 60 parts of carbon black, 7 parts of chopped carbon fiber, 3 parts of paraffin oil, 1 part of part of accelerator and 2.5 parts of sulfur, and then mixed for 8 minutes, and then pressed into tablets after mixing evenly to obtain the mixed rubber; the mixed rubber was parked at room temperature for 24 hours, and then vulcanized and formed on a 50T flat vulcanizing machine, and the vulcanized condition was 140 °C×30min to obtain the finished product.

[0022] According to the performance test, the tensile strength of the electromagnetic shielding natural rubber composite material is 15...

Embodiment 3

[0024] Fully disperse the chopped carbon fiber in a beater, filter the dispersion and fully dry it to obtain a chopped and dispersed carbon fiber monofilament with a fiber diameter of 10 μm and a length of 5 mm; in an internal mixer or an open mixer, first 100 parts by weight of natural rubber were masticated for 5 minutes, then 2 parts of stearic acid, 5 parts of zinc oxide, 1 part of antioxidant, 60 parts of carbon black, 11 parts of chopped carbon fiber, 3 parts of paraffin oil, 1 part of part of accelerator and 2.5 parts of sulfur, and then mixed for 8 minutes, and then pressed into tablets after mixing evenly to obtain the mixed rubber; the mixed rubber was parked at room temperature for 24 hours, and then vulcanized and formed on a 50T flat vulcanizing machine, and the vulcanized condition was 140 °C×30min to obtain the finished product.

[0025] According to the performance test, the tensile strength of the electromagnetic shielding natural rubber composite material is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Electromagnetic shielding effectivenessaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a natural rubber composite with an electromagnetic shielding property. The composite comprises natural rubber, a short carbon fiber and a compounding agent, wherein the diameter of the short carbon fiber is 3-10 mu m, the length of the short carbon fiber is 1-5 mm, and the weight ratio of the natural rubber to the short carbon fiber at room temperature is 100:(0.5-11). Because the physical and mechanical properties of the natural rubber and the short carbon fiber are fully used for preparing the composite with the electromagnetic shielding property, the composite has the good electromagnetic wave absorption property of the short carbon fiber and the good physical and mechanical properties of the rubber material, and can be adaptive to the requirement on various environments. The composite has the advantages that the electromagnetic shielding property is high, the preparation method is simple, the preparation cost is low, and the energy consumption is reduced.

Description

technical field [0001] The invention belongs to the field of electromagnetic shielding materials, specifically a natural rubber composite material with electromagnetic shielding performance and a preparation method thereof Background technique [0002] The electromagnetic interference generated by electromagnetic wave radiation will not only affect the normal operation of various electronic equipment, but also cause serious damage to the physical and mental health of people who have been exposed to electromagnetic wave radiation for a long time. Because polymer materials have good physical and mechanical properties, it is very necessary to develop electromagnetic shielding polymer materials with high electromagnetic shielding performance, low manufacturing cost, and simple preparation methods. The metal thin composite layer or coating of the surface conductive electromagnetic shielding polymer material is easy to peel off during use and processing, and its mechanical propert...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L7/00C08K7/06C08K3/04
Inventor 曾宪奎汪传生边慧光
Owner QINGDAO UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com