Additive for bright nickel plating technology for permanent magnetic material
A permanent magnet material and additive technology, which is used in the surface treatment of permanent magnet materials and the additive field of bright nickel electroplating technology to achieve the effect of improving corrosion resistance.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0026] Weigh 3 kg of nickel sulfate, 500 g of nickel chloride, and 500 g of boric acid in 8 liters of pure water, adjust the pH, and finally dilute it to 10 liters, beat activated carbon, filter, and electrolyze with a small current. Add primary brightener BBI 3ml / L, secondary brightener PPS 1ml / L, impurity remover VS 1ml / L, wetting agent EHS 1ml / L, make a Huo's groove, add D22×5 bonded NdFeB sample 10 The sheet was plated for 10 minutes at a current of 0.5 amps and a temperature of 55°C. The surface of the coating is bright, and the crystal is fine and bright. The cross-file test shows that the coating does not peel off, does not peel off, and has a good bonding force.
Embodiment 2
[0028] Weigh 2.5 kg of nickel sulfate, 300 g of nickel chloride, and 400 g of boric acid in 8 liters of pure water, adjust the pH, and finally dilute it to 10 liters, beat activated carbon, filter, and electrolyze with a small current. Add primary brightener BSI 3ml / L, secondary brightener PPSOH 1ml / L, PPS1ml / L, impurity remover ALS 2ml / L, wetting agent AES 3ml / L, make a Huo's groove, add D22×5 sintered neodymium iron Ten boron samples were tested for 10 minutes at a current of 0.5 amps and a temperature of 55°C. The surface of the coating is bright, and the crystal is fine and bright. The cross-file test shows that the coating does not peel off, does not peel off, and has a good bonding force.
Embodiment 3
[0030] Weigh 3 kg of nickel sulfate, 500 g of nickel chloride, and 500 g of boric acid in 8 liters of pure water, adjust the pH, and finally dilute it to 10 liters, beat activated carbon, filter, and electrolyze with a small current. Add primary brightener BBI 1.5ml / L, BSI 1ml / L, PAP 1ml / L, secondary brightener PPS 1ml / L, impurity remover VS 1ml / L, wetting agent EHS 1ml / L, and play Huo's tank, Add 10 pieces of D22×5 sintered NdFeB samples and test plating for 10 minutes under the condition of 0.5A current and temperature 55℃. The surface of the coating is bright, and the crystal is fine and bright. The cross-file test shows that the coating does not peel off, does not peel off, and has a good bonding force.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com