Production technology of plasterboard modified starch
A paper-faced gypsum board and modified starch technology, which is applied in the field of production technology of paper-faced gypsum board modified starch, can solve the problems of weak market competitiveness of products, increased cost of production enterprises, small scale of modified starch, etc., and achieves good elasticity. , low cost and energy consumption, good water absorption effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0019] Add 1,000 parts of raw starch into the mixer, start the stirring motor, spray 25 parts of diluted hydrochloric acid with a concentration of 10% and 20 parts of hydrogen peroxide with a concentration of 10% to 27.5%, stir at room temperature for 10 to 15 minutes, and then After being fully mixed by a high-speed mixer, it is sent to the material inlet of the microwave far-infrared equipment. Adjust the thickness of the material layer to 3-6cm, turn on the microwave far-infrared equipment, adjust the temperature of the material at 50-150°C, and keep it for 10-30 minutes. After the index of 10-12% and viscosity of 2-5mpa.s reaches the required value, put the material into the cooling compounding machine and wait for the temperature to drop below 40°C, spray the concentration at 4%-10% 10 parts of potassium hydroxide solution (containing 5 parts of methanol) are mixed evenly, and then 5-10 parts of microcrystalline cellulose are added, mixed thoroughly for 10-20 minutes, then...
Embodiment 2
[0021] Add 1000 parts of raw starch into the mixer, start the stirring motor, spray 18 parts of diluted hydrochloric acid with a concentration of 12%, 10 parts of ammonium persulfate with a concentration of 12%, stir at room temperature for 10 to 15 minutes, and follow-up procedures are the same as in Example 1 , and finally spray 5-10 parts of sodium hydroxide solution with a concentration of 10% (containing 5 parts of methanol) and mix evenly, then add 6-12 parts of silicon dioxide, mix thoroughly for 10-20 minutes, and then sieve and pack. Obtain the product of the present invention.
Embodiment 3
[0023] Add 1000 parts of raw starch into the mixer, start the stirring motor, then spray 15 parts of diluted sulfuric acid with a concentration of 5%, and 10 parts of hydrogen peroxide with a concentration of 10%, stir at room temperature for 10 to 15 minutes, follow-up procedures and Example 1 Similarly, spray 15 parts of sodium silicate solution with a concentration of 9% at the end, add 12 parts of silicon dioxide after mixing evenly, mix thoroughly for 10 to 20 minutes, then sieve and pack to obtain the product of the present invention.
[0024] The modified starch obtained in the above examples is mainly used in the addition of paper-faced gypsum boards, and its main properties are shown in the table (taking the product standard of a well-known domestic paper-making enterprise as an example)
[0025]
[0026] The results show that the main properties of the gypsum board starch of the present invention meet or exceed the standards and performance requirements specified b...
PUM
![No PUM](https://static-eureka-patsnap-com.libproxy1.nus.edu.sg/ssr/23.2.0/_nuxt/noPUMSmall.5c5f49c7.png)
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka-patsnap-com.libproxy1.nus.edu.sg/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com