Production method of superfine glass wool product

A production method and ultra-fine glass technology, applied in the direction of manufacturing tools, ceramic molding machines, etc., can solve the problems of uneven thickness of glass wool layer, affecting the quality of glass wool products, and uneven diameter of glass wool, so as to achieve good elasticity and protection Environment, the effect of uniform thickness

Active Publication Date: 2010-10-13
许立江
View PDF2 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, the production method adopted by ultra-fine glass wool on the market is very complicated, and due to the uneven diameter of the produced glass wool, the glass wool after curing has poor elasticity and the thickness of the glass wool layer is uneven; it seriously affects the quality of glass wool products. The quality, and the yield of glass wool products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A method for producing ultrafine yellow glass wool products, wherein the diameter of the yellow ultrafine glass wool is 2.5 μm to 4 μm, and the steps of the production method are as follows:

[0039] (a) Recover cullet, clean and break it; the diameter of broken glass is less than 30mm

[0040] (b) Prepare raw materials: feldspar, dolomite, soda ash, borax, and analyze the composition of raw materials;

[0041] (c) According to the requirements: 11.3% feldspar, 3.15% soda ash, 10% borax, and 75.55% glass to calculate the amount of various raw materials, and then weigh and mix the raw materials and cullet to make a batch; the compound in the batch The required ratio is, SiO 2 : 64.7%; AL 2 o 3 with Fe 2 o 3 Sum: 2.7%; B 2 C 3 4.9%; the sum of CaO and MgO: 10.8%; Na 2 O and K 2 The sum of O is 15.9%, and other impurities are 1%.

[0042] (d) melting the batch materials to obtain uniform, pure and transparent molten glass;

[0043] This step has five stages: sil...

Embodiment 2

[0068] A method for producing ultrafine white glass wool products, wherein the diameter of the ultrafine white glass wool is 2.5 μm to 4 μm, the steps of the production method are as follows:

[0069] (a) Recover cullet, clean and break it; the diameter of broken glass is less than 30mm

[0070] (b) Prepare raw materials: feldspar, dolomite, soda ash, borax, and analyze the composition of raw materials;

[0071] (c) According to the requirements: 10% feldspar, 3.5% soda ash, 9% borax, and 77.5% glass to calculate the amount of various raw materials, and then weigh and mix the raw materials and cullet to make a batch; the compound in the batch The required ratio is, SiO 2 : 65.2%; AL 2 o 3 with Fe 2 o 3 Sum: 2.6%; B 2 C 3 4.8%; the sum of CaO and MgO: 10.6%; Na 2 O and K 2 The sum of O is 15.8%, and other impurities are 1%.

[0072] (d) melting the batch materials to obtain uniform, pure and transparent molten glass;

[0073] This step has five stages: silicate forma...

Embodiment 3

[0098] A kind of production method of ultra-white fine glass wool product, its glass wool diameter is 2 μm~2.5 μm, the steps of this production method are as follows:

[0099] (a) Recover cullet, clean and break it; the diameter of broken glass is less than 30mm

[0100] (b) Prepare raw materials: feldspar, dolomite, soda ash, borax, and analyze the composition of raw materials;

[0101] (c) According to the requirements: 14.5% feldspar, 4% soda ash, 9.5% borax, and 72% glass to calculate the amount of various raw materials, then weigh and mix the raw materials and cullet to make a batch; the compound in the batch The required ratio is, SiO 2 : 64.1%; AL 2 o 3 with Fe 2 o 3 Sum: 2.9%; B 2 C 3 5%; the sum of CaO and MgO: 11%; Na 2 O and K 2 The sum of O is 16%, and other impurities are 1%.

[0102] (d) melting the batch materials to obtain uniform, pure and transparent molten glass;

[0103] This step has five stages: silicate formation stage, glass formation stage, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a production method of a superfine glass wool product. The production method comprises the following steps of: recovering shattered glass, cleaning and crushing; preparing raw materials including feldspar, dolomite, sodium carbonate and borax, and testing and analyzing the components of the raw materials; calculating the use levels of the raw materials according to the required proportion of the compound in a batch mixture, and weighting and mixing the raw materials and the shattered glass to prepare the batch mixture; founding the batch mixture to obtain uniform, purified and transparent molten glass; preparing a binder; fiberizing the molten glass to obtain glass wool, and spraying the binder into the glass wool; solidifying and sizing and the glass wool; and carrying out aftertreatment on the glass wool product. In the invention, the water soluble resin binder is used so that the produced glass wool product has good elasticity and is uniform. Since the recovered waste glass is adopted as the main raw material, the recycle of resource is realized, the environment is protected, and the cost is saved. In addition, the production method of the superfine glass wool product has simple operation.

Description

technical field [0001] The invention relates to a production method of glass wool products, in particular to a production method of ultrafine glass wool products. Background technique [0002] Ultra-fine glass wool, as a new type of fibrous receiving material, has excellent properties such as light weight, heat preservation, fire prevention, sound absorption, moth resistance, and corrosion resistance. It is widely used in chemical industry, metallurgy, light industry, electric power, petroleum and construction industries. However, at present, the production method adopted by ultra-fine glass wool on the market is very complicated, and due to the uneven diameter of the produced glass wool, the glass wool after curing has poor elasticity and the thickness of the glass wool layer is uneven; it seriously affects the quality of glass wool products. The quality, and the yield of glass wool products. Contents of the invention [0003] Purpose of the invention: The purpose of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B26/12C04B14/42C03C13/00C03C6/02B28B1/52
Inventor 周介明
Owner 许立江
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com