Method for preparing vanadium redox battery negative pole electrolyte

A negative electrode electrolyte, vanadium battery technology, applied in the field of battery manufacturing, can solve the problems affecting the performance of vanadium batteries, poor electrolyte stability, difficult to control the ratio, etc., to achieve electrochemical reaction activity and good reversibility, good stability, anti- The effect of improving low temperature environment capability

Active Publication Date: 2010-06-09
承德新新钒钛储能科技有限公司
View PDF0 Cites 34 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The process cost of this type of method is high, and the vanadium in the obtained positive and negative electrolytes is in a mixed valence state, and the ratio is not easy to control; and because of the requirements of the electrolysis process, there are many restrictions on the use of additives, so the stability of the prepared electrolyte is relatively high. Poor, seriously affecting the performance of vanadium batteries, limiting its popularization and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing vanadium redox battery negative pole electrolyte
  • Method for preparing vanadium redox battery negative pole electrolyte

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Prepare vanadium battery negative electrode electrolyte according to the following steps:

[0028] (1) to 1:1 dilute H 2 SO 4 Add 450g of industrial high-purity V to 1000mL of the solution 2 o 3 (total vanadium content is greater than 67%), in the solution, continuous feeding purity is 99.999% (O 2 ≤0.001%) of high-purity nitrogen, the solution is heated to 80 ℃ ~ 150 ℃, then add 90g additive Na 2 SO 4 , filter the insoluble matter, and get V 2 (SO 4 ) 3 solution;

[0029] (2) to 1:1 dilute H 2 SO 4 Add 450g of industrial high-purity V to 1000mL of the solution 2 o 3 (total vanadium content greater than 67%) and 240g reducing agent Na 2 S, the continuous feeding of the solution has a purity of 99.999% (O 2 ≤0.001%) of high-purity nitrogen, the solution is heated to 80 ℃ ~ 150 ℃, add 90g additive Na 2 SO 4 , filter the insoluble matter, and get VSO 4 solution;

[0030] (3)VSO 4 solution and V 2 (SO 4 ) 3 The solution is mixed according to the molar ...

Embodiment 2

[0035] Prepare vanadium battery negative electrode electrolyte according to the following steps:

[0036] (1) to 1:1 dilute H 2 SO 4 Add 450g of industrial high-purity V to 1000mL of the solution 2 o 3 (total vanadium content is greater than 67%), in the solution, continuous feeding purity is 99.999% (O 2 ≤0.001%) of high-purity nitrogen, the solution is heated to 80 ℃ ~ 150 ℃, then add 90g additive Na 2 SO 4 , filter the insoluble matter, get V 2 (SO 4 ) 3 solution;

[0037] (2) Take the above V 2 (SO 4 ) 3 Solution 500mL, to which continuous feeding purity is 99.999% (O 2 ≤0.001%) of high-purity nitrogen, the solution is heated to 80 ℃ ~ 150 ℃, then add 220g of reducing agent Na 2 SO 3 , filter the insoluble matter to get VSO 4 solution;

[0038] (3)V 2 (SO 4 ) 3 solution and VSO 4 The solution is mixed according to the molar ratio of 1:2, that is, it is prepared by V 2 (SO 4 ) 3 、VSO 4 , water and additive Na 2 SO 4 A mixed solution consisting of, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of battery manufacturing, in particular to a method for preparing vanadium redox battery negative pole electrolyte, which is characterized in that industrial high purity V2O3 is adopted as raw material, proper additive and reducing agent are added into the raw material, and the vanadium redox battery negative pole electrolyte is directly prepared by a chemical method under the protection of high purity nitrogen. The method has the advantages of easily obtained raw material, low cost, simple reaction condition as well as simple and convenient operation; the prepared electrolyte is high in total vanadium concentration and good in stability, and has the using performance to be obviously improved in the low temperature environment; and the method is suitable for industrialized production.

Description

technical field [0001] The invention relates to the field of battery manufacturing, in particular to a method for preparing a vanadium battery negative electrode electrolyte. Background technique [0002] Vanadium battery is a very promising green energy storage battery, its positive and negative electrodes are VO 2+ / VO 2 + and V 2+ / V 3+ . Compared with the traditional solid-phase battery, it has the advantages of small concentration polarization, large battery capacity and easy adjustment, long service life, high current charge and discharge resistance, active solution can be regenerated and recycled, and it is safe during manufacture, use and disposal. There are many advantages such as no harmful substances that pollute the environment. At present, the electrolyte solution for vanadium batteries mainly uses V 2 o 5 It is prepared by dissolving in sulfuric acid, reducing with a reducing agent, adjusting the concentration of vanadium after the reaction is complete,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M8/18H01M10/38
CPCY02E60/12Y02E60/528Y02E60/10Y02E60/50Y02P70/50
Inventor 张群赞孙爱玲扈显琦
Owner 承德新新钒钛储能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com