Dyeing method for wool/cupro blended fabrics

A technology of cupro ammonia fiber and blended fabrics, applied in the field of fiber dyeing, which can solve the problems of reducing dye fixing ability, reducing dyeing uniformity, and affecting the difference between large and small samples, so as to achieve good dyeing effect, shorten dyeing time, and reduce damage.

Inactive Publication Date: 2011-11-30
HEILAN HOME
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Conventional reactive dyes are highly reactive dyes with poor penetration during dyeing. In the dyeing of blended fabrics, poor penetration reduces the uniformity of dyeing
Most reactive dyes have a tendency to hydrolyze, especially when dyeing at high temperature, but in comparison, high reactive dyes are easier to hydrolyze than medium and low reactive dyes. The hydrolysis of reactive groups will reduce the color fixing ability of dyes, thus affecting The size and sample difference after fabric dyeing, as well as the stability of fabric dyeing and the reproducibility of dyeing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] 1. Preparation:

[0021] Dye: 0.2% (fabric weight percentage) Lanersol Red CE

[0022] 0.4% (fabric weight percentage) Lannasol Yellow CE

[0023] 0.1% (fabric weight percentage) Lanners blue CE.

[0024] 2. Dyeing

[0025]Put the wool / cupro blended fabric into the overflow dyeing machine, run it for 10 minutes, add glacial acetic acid of 0.1% by weight of the fabric, make the pH of the dyeing bath 6.5, run it for 5 minutes, add 0.5g / L Abexil FFC- 01, run for 5 minutes, add 2g / L Dye Yubao C, run for 5 minutes, add 15g / L Yuan Mingfen, run for 10 minutes, add Lannasol dye, run for 5 minutes, start to heat up, and keep the heating rate at 1°C / min, keep warm at 90°C for 30 minutes, then cool down to 70°C, add 3g / L soda ash, keep warm for 60 minutes. Bath ratio: 1:15.

[0026] 3. Post-processing

[0027] Place the dyed wool / cupro ammonia fiber blended fabric in 2% fabric weight percentage soap solution 209, add 2% fabric weight percentage soda ash, treat a...

Embodiment 2

[0029] 1. Preparation:

[0030] Dye: 0.3% (fabric weight percent) Lanersol Red CE

[0031] 3.8% (fabric weight percentage) Lanner black CE-R.

[0032] 2. Dyeing

[0033] Put the wool / cupro blended fabric into the overflow dyeing machine, run it for 10 minutes, add glacial acetic acid of 0.2% by weight of the fabric, make the pH of the dyeing bath 6.0, run it for 5 minutes, add 0.5g / L Abexil FFC- 01, run for 5 minutes, add 2g / L Abai Run C, run for 5 minutes, add 20g / L Yuan Mingfen, run for 10 minutes, add Lannasol dye, run for 5 minutes, start to heat up, and keep the heating rate at 1°C / Minutes, keep warm at 90°C for 30 minutes, then cool down to 70°C, add 4g / L soda ash, keep warm for 60 minutes. Bath ratio: 1:15.

[0034] 3. Post-processing

[0035] Place the dyed wool / cupro ammonia fiber blended fabric in 3% fabric weight percentage soap solution 209, add 3% fabric weight percentage soda ash, treat at 90°C for 30min, rinse and then place it in 1% fabric weight percenta...

Embodiment 3

[0037] 1. Preparation:

[0038] Dye: 6.5% (fabric weight percentage) Lanner black CE-R

[0039] 2. Dyeing

[0040] Put the wool / cupro blended fabric into the overflow dyeing machine, run it for 10 minutes, add 0.3% glacial acetic acid by weight of the fabric, make the pH of the dyeing bath 5.5, run it for 5 minutes, add 1g / L Avaxol FFC-01 , run for 5 minutes, add 2g / L Dyeyubao C, run for 5 minutes, add 30g / L Yuan Mingfen, run for 10 minutes, add Lannasol dye, run for 5 minutes, start to heat up, and keep the heating rate at 1°C / Minutes, keep warm at 90°C for 30 minutes, then cool down to 70°C, add 3g / L soda ash, keep warm for 60 minutes. Bath ratio: 1:15.

[0041] 3. Post-processing

[0042] Place the dyed wool / cupro ammonia fiber blended fabric in 5% fabric weight percentage of soaping solution 209, add 3% soda ash, treat at 90°C for 30 minutes, rinse and then place it in 1% fabric weight percentage of glacial acetic acid Medium, 40 ° C for 10 min. Bath ratio: 1:15.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a kind of dyeing method of wool / cupro ammonia fiber blended fabric, selects Lannasol dye produced by American Huntsman Textile Dyeing Chemical (China) Co., Ltd. to carry out one-bath dyeing; Add Abai Run C as the dyeing method during the dyeing process Anti-wrinkle lubricant, adding penetration enhancer Abuchlor FFC-01, the method includes dyeing and aftertreatment: 1. Dyeing: the wool / cupro ammonia fiber blended fabric is loaded into the overflow dyeing machine, adding glacial acetic acid, Abusil FFC-01, Abai Run C, Yuan Mingfen and Lannasol dyes, keep warm at 90°C±2°C for 20-30 minutes, then cool down to 70°C±2°C, add soda ash, keep warm for 50-70 minutes, liquor ratio: 1:15-20; 2. Post-treatment process: first place the dyed wool / cupro fiber blended fabric in soap solution 209, add soda ash, treat at 80-90°C for 20-30 minutes, rinse and then place on ice In acetic acid, treat at 40°C±2°C for 10 minutes, bath ratio: 1:15-1:20. The invention has good dyeing effect and good color fastness. Moreover, there is little damage to the fabric during the dyeing process.

Description

(1) Technical field [0001] The invention relates to the selection of dyes for dyeing wool / cupro ammonia fiber blended fabrics, the selection of auxiliary agents corresponding to dyeing in the dyeing process, and the matching dyeing and post-treatment processes. It belongs to the technical field of fiber dyeing. (2) Background technology [0002] Wool / cupro blended fabric is a blended fabric produced with high-count untwisted cupro filament as warp and worsted wool single yarn as weft. The fabric has the characteristics of smooth hand feeling, charming luster, elegant color, good drapability and unique style. [0003] Cupro ammonia fiber is a kind of regenerated cellulose fiber. It is made of spinning solution by dissolving loose cotton linters and other natural cellulose raw materials in concentrated ammonia solution of copper hydroxide or alkaline copper salt. After soaking, it is coagulated and shaped in a spinning bath of water or dilute alkali solution, and then decomp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06P1/38D06P3/852D06P1/44D06P5/02
Inventor 赵国英胡晓峰张新龙杨自治周月琴
Owner HEILAN HOME
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com