Five-layer co-extrusion laminated board for sanitary ware and preparation method thereof

A composite board and sanitary ware technology, applied in the direction of chemical instruments and methods, lamination, layered products, etc., can solve the problems of structural incompatibility, board crack resistance, chemical corrosion resistance and poor hot water circulation resistance, etc., to achieve Not easy to fade, good hot water cycle resistance, stable color effect

Inactive Publication Date: 2010-03-17
CHANGZHOU BOSHUANG PLASTICS
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Acrylic composite panels are widely used in the sanitary ware industry such as bathtubs and bathtubs. At present, the raw materials for preparing such panels are mostly acrylonitrile-butadiene-polystyrene copolymer (ABS) and polymethyl methacrylate (PMMA). , but from the perspective of chemical mechanism, ABS and PMMA are not structurally compatible, which leads to the disadvantages of poor crack resistance, chemical corrosion resistance and hot water cycle resistance of the board produced by extrusion.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] a. Stir the raw materials with a ratio of 0.1% of benzotriazole ultraviolet absorber (UV) and polymethyl methacrylate (PMMA) as the balance in the mixing hopper, and carry out the process at a temperature of 80°C at the same time. After 3 hours of drying, the resin is melted and plasticized at 200-250°C by one of the extruders, and extruded into the first and fifth flow channels of the distributor;

[0033] b. Stir the raw materials with a ratio of benzotriazole ultraviolet absorber (UV) 0.1%, titanium dioxide color masterbatch 4%, PMMA 40, and ABS in the mixing hopper evenly in a mixing hopper at a temperature of 80° C. Dry for 3 hours within the range, melt and plasticize the resin at 200-240°C by the second rod extruder, and extrude it into the second and fourth flow channels of the distributor;

[0034] c. Mix the raw materials with a ratio of 5% titanium dioxide color masterbatch and ABS as the balance, and stir them evenly in the mixing hopper, and at the same tim...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a five-layer co-extrusion laminated board for sanitary ware and a preparation method thereof, wherein the first layer and the fifth layer are made from PMMA and UV; the secondlayer and the fourth layer are made from the PMMA, ABS, the UV and a titanium dioxide color master batch; and the third layer is made from the ABS and the titanium dioxide color master batch. The preparation method of the board comprises the following steps: uniformly mixing and stirring the raw materials of each layer in respective mixing hoppers; drying the raw materials and then plasticizing, melting and extruding the raw materials into corresponding flow channels of a distributor at a certain temperature by three extruders; and extruding the raw materials by a T-shaped die head and flattening the raw materials through a flattening system to prepare the board. The invention has the advantages that after long-term uneven cold and hot changes, the board is not easy to generate delamination to crack, has good hot water circulation resistance and the function of ultraviolet ray resistance, can be guaranteed to be not easy to fade during use and have cracking resistance, chemical corrosion resistance, hot water circulation resistance, stable color, difficult fading after being exposed to the sun and the rain for a long term, and the like. The invention is also widely suitable for other fields such as indoor and outdoor decoration, and the like.

Description

technical field [0001] The invention relates to a five-layer co-extruded composite board for sanitary ware and a preparation method thereof. Background technique [0002] Acrylic composite panels are widely used in the sanitary ware industry such as bathtubs and bathtubs. At present, the raw materials for preparing such panels are mostly acrylonitrile-butadiene-polystyrene copolymer (ABS) and polymethyl methacrylate (PMMA). , but from the perspective of chemical mechanism, ABS and PMMA are not structurally compatible, which leads to the disadvantages of poor crack resistance, chemical corrosion resistance and hot water cycle resistance of the board produced by extrusion. Contents of the invention [0003] One of the purposes of the present invention is to provide a five-layer co-extruded composite board for sanitary ware: [0004] The five-layer co-extruded composite board for sanitary ware consists of five layers: [0005] The first layer: benzotriazole ultraviolet abso...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/08B32B27/18B32B27/20B32B27/28B32B37/15B32B27/30B29C47/06B29C47/92B29B13/06B29C48/08B29C48/92
CPCB29C48/92B29C2948/92704B29C48/08B29C2948/92895
Inventor 金惠良贺国华
Owner CHANGZHOU BOSHUANG PLASTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products