Low-temperature impact-resistant polypropylene composition, and preparation method and application thereof as decoration in automobile

A polypropylene composition and low-temperature-resistant technology, which is applied in the field of automotive interior parts, can solve the problems of not being able to obtain low-temperature-resistant and high-performance automotive instrument interior parts, not meeting automotive materials, and poor rigidity, etc., to achieve good cantilever Beam notched impact strength and multiaxial impact strength, the effect of overcoming poor low temperature performance, and good rigidity

Active Publication Date: 2012-07-11
KINGFA SCI & TECH CO LTD +1
View PDF12 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, while the current polypropylene material ensures low-temperature performance, its rigidity will deteriorate, which cannot meet the standards used in automotive materials, and it is impossible to obtain low-temperature resistant and high-performance automotive interior parts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-temperature impact-resistant polypropylene composition, and preparation method and application thereof as decoration in automobile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Example 1 Low temperature impact resistant polypropylene composition

[0036] The composition of the polypropylene composition of this embodiment is shown in Table 1.

[0037] Table 1 Raw materials and consumption of polypropylene composition

[0038] raw material name

Dosage%

(weight percent) Polypropylene copolymer: HHP6, Sinopec Maoming Petrochemical Branch 65.4 Talc powder: Heshan Chemical Group 22 Toughener: POE, density 0.868g / cm 3 , ExxonMobil Chemical 12 Antioxidant: tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid]

Pentaerythritol (Irganox1010), Ciba Fine Chemical Industry Co., Ltd. 0.2

Weather resistance agent: 4-benzoyloxy-2,2,6,6 tetramethylpiperidine (light stable 0.2

[0039] Agent 744), Ciba Fine Chemical Industry Co., Ltd. Calcium stearate 0.2

[0040] The polypropylene composition of the present embodiment, its preparation method is as follows:

[0041] The raw...

Embodiment 2

[0045] Example 2 Low temperature impact resistant polypropylene composition

[0046] The composition of the polypropylene composition of this embodiment is shown in Table 3.

[0047] Raw material and consumption of table 3 polypropylene composition

[0048] raw material name Dosage %

[0049] (weight percent) Polypropylene copolymer: SP179, Sinopec Qilu Petrochemical Company 67.4 Talc powder: Guangxi Hezhou Talc Powder Co., Ltd. 22 Toughener: POE, density 0.870g / cm 3 , ExxonMobil Chemical 10 Antioxidant: Tris(2,4-di-tert-butylphenyl)phosphite (Irganox

168), Ciba Fine Chemical Industry Co., Ltd. 0.2

Weather resistance agent: bis(1,2,2,6,6-pentamethyl-4-piperidinyl) sebacate

(Tinuvin292), Ciba Fine Chemical Industries Ltd. 0.2

Calcium stearate 0.2

[0050] The polypropylene composition of this embodiment, its preparation method is as embodiment 1.

[0051] The detection results of the polypropylen...

Embodiment 3

[0054] Example 3 Low temperature impact resistant polypropylene composition

[0055] The composition of the polypropylene composition for automotive interior parts of this embodiment is shown in Table 5.

[0056] Raw material and consumption of table 5 polypropylene composition

[0057] raw material name

Dosage%

(weight percent) Polypropylene copolymer: K7726, Sinopec Yanshan Petrochemical Branch 66.4 Talc powder: Heshan Chemical Group 25 Toughener: POE, density 0.868g / cm 3 , Dow Chemical 8 Antioxidant: tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl)propane

Acid] Pentaerythritol (Irganox1010), Ciba Fine Chemical Industry Co., Ltd.

limited company 0.2

Weather resistance agent: 4-benzoyloxy-2,2,6,6 tetramethylpiperidine (light

Stabilizer 744), Ciba Fine Chemical Industry Co., Ltd. 0.2

Calcium stearate 0.2

[0058] The polypropylene composition of this embodiment, its preparation method is as embodiment 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
impact strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a low-temperature impact-resistant polypropylene composition, and a preparation method and an application thereof as a decoration in an automobile. The polypropylene composition comprises the following components in percentage by weight: 40-79.8% of polypropylene resin, 15-35% of mineral filler, 5-30% of toughener, 0.1-1% of antioxidant and 0.1-1% of weather-proof agent. The polypropylene composition can be made into decorations in automobiles through injection molding. Various properties of the polypropylene composition meet the requirements for usage; and the polypropylene composition overcomes the effect of poor low temperature performance and especially has strong low temperature impact resistance at 0-40 DEG C.

Description

technical field [0001] The invention relates to automobile interior parts, in particular to a low-temperature impact-resistant polypropylene composition, a preparation method thereof and application as an automobile interior part. Background technique [0002] Due to its light weight, solvent resistance, easy processing, excellent mechanical properties, and easy recycling, polypropylene has been widely used, especially in the automotive industry, home appliances and machinery. In the future, the automobile industry will develop in the direction of energy saving, environmental protection and safety. This requires the materials used to be light in weight, simple to process, easy to recycle, etc., and polypropylene meets these requirements. However, polypropylene material has poor low-temperature resistance and low rigidity, and cannot meet the requirements for automotive interior parts. It must be modified to improve its low-temperature performance and rigidity to meet the re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/10C08L23/08C08L23/16C08L53/02C08K3/34C08K3/26B29B7/00B29B9/06B29L31/58B29K23/00
Inventor 李永华丁超黄达罗忠富周英辉陈广强
Owner KINGFA SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com