UV curing high wear-resistant low luster coating and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A high wear-resistant, ultraviolet light technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of non-abrasion, coating loss, non-scratch, etc., to achieve the surface not easy to shine, construction simplicity, The effect of good adhesion
Inactive Publication Date: 2010-02-10
DONGGUAN JIAZHUOCHENG CHEM TECH
View PDF0 Cites 8 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] With the popularization of computers, the keyboard has become the most contacted product in our daily life and work, but the current keyboard is mainly plastic or a small amount of conventional matte UV-cured coating, due to the plastic itself a
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides a UV curing high wear-resistant low luster coating and a preparation method thereof. The coating comprises the following components in percentage by weight: primer and a curingagent, wherein, the primer comprises 55-60 of hydroxyl acrylic resins, 10-13 of solution containing 20% of cellulose acetate butyrate resins, 4-6 of methyl isobutyl ketone, 0.1-0.2 of flow agent, 5-7of aluminum paste and 17-19 of ethyl acetate; the curing agent comprises 55-60 of hexamethylene diisocyanate, 10-15 of unsaturated aliphatic polyurethane acrylate and 26-32 of butyl acetate. The invention has the advantages as follows: the invention has low VOC discharge when being used for construction under common coating conditions; the invention can achieve the effects of high wear resistanceand difficult surface shining by using the common plastics coating method; the invention features simplicity and commonality of construction and has very good adhesion on the plastics and aluminum; the invention features thin film thickness and has cost lower than that of the common UV coatings.
Description
technical field [0001] The invention relates to an ultraviolet light-cured high-wear-resistant matte coating and a preparation method thereof. The coating is suitable for plastic keyboards, such as ABS+PC keycaps or aluminum keyboards. Background technique [0002] With the popularization of computers, the keyboard has become the most contacted product in our daily life and work, but the current keyboard is mainly plastic or a small amount of conventional matte UV-cured coating, due to the plastic itself and ordinary UV light The defects in the design of the cured coating itself lead to its non-scratch resistance, non-abrasion resistance, surface shine or coating loss after long-term use, which affects the appearance of the keyboard and reduces its protection. Contents of the invention [0003] The purpose of the present invention is to overcome the above-mentioned defects and provide a UV-cured high wear-resistant matte coating, which has the characteristics of thinner co...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.