Dielectric ceramic composition and multilayer ceramic capacitor

A technology of dielectric ceramics and components, applied in the field of multilayer ceramic capacitors, can solve problems such as insufficient resistivity and unstable operation, and achieve the effects of stable characteristics, high resistivity, and high permittivity

Active Publication Date: 2010-01-20
MURATA MFG CO LTD
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] However, KSr of Patent Document 1 2 Nb 5 o 15 The ceramic composition has high permittivity ε but insufficient resistivity ρ
Therefore, operation may be unstable in an environment with high driving voltage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dielectric ceramic composition and multilayer ceramic capacitor

Examples

Experimental program
Comparison scheme
Effect test

experiment example 1

[0036] In this experiment example, the investigation is that, relative to the principal component (KSr 2 Nb 5 o 15 ), changing the element type and content of R and M in the subcomponents, thereby affecting the electrical characteristics. The sample numbers of the prepared samples are 1 to 35, and Table 1 shows the composition of each sample and the measurement results of electrical characteristics. It will be described in detail below.

[0037] First, as the raw material of the main component, prepare K 2CO 3 , SrCO 3 , Nb 2 o 5 , weigh these raw materials to make it a composition formula: KSr 2 Nb 5 o 15 The composition shown is mixed in a solvent with a ball mill and dried, and then synthesized by heat treatment at 1000 ° C for 2 hours, thus obtaining KSr 2 Nb 5 o 15 Composition of the main ingredient powder.

[0038] For example, with respect to 100 mole parts of the main component, the molar parts of R contained in sample numbers 1 to 35 in Table 1, the deta...

experiment example 2

[0049] In this experiment example, the investigation is that, relative to the principal component (KSr 2 Nb 5 o 15 ), in the composition of R and M containing subcomponents, a part of the K site is replaced by Na, which affects the electrical characteristics. The sample numbers of the prepared samples are 101 to 123, and Table 2 shows the composition of each sample and the measurement results of electrical characteristics. It will be described in detail below.

[0050] First, make the composition formula: (K 1-x Na x )Sr 2 Nb 5 o 15 The value of x in Table 2 is the value of x shown in sample numbers 101 to 123 in Table 2, so as the raw material of the main component, weigh K 2 CO 3 、Na 2 CO 3 , SrCO 3 , Nb 2 o 5 , mixed these raw materials with a ball mill in a solvent, dried them, and then carried out 2 hours of heat treatment synthesis at 1000 ° C, thus obtaining (K 1-x Na x )Sr 2 Nb 5 o 15 main ingredient powder.

[0051] For example, with respect to 100...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
areaaaaaaaaaaa
Login to View More

Abstract

Disclosed is a dielectric ceramic material used for a multilayer ceramic capacitor, namely a dielectric ceramic composition having a high resistivity which can be fired together with an internal electrode mainly composed of Ni at a temperature not more than 1200 DEG C. This dielectric ceramic composition mainly contains a tungsten bronze type complex oxide represented by the chemical composition:(K1-xNax)Sr2Nb5O15 (wherein 0 <= x < 0.2), while containing, as minor components, 0.05-20 parts by mole of R (R is at least one element selected from the group consisting of Y, La, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb and Lu) and 0.05-40 parts by mole of M (M is at least one element selected from the group consisting of Mn, V, Li, Si, Ni, Cr, Co, Fe, Zn, Mg and Zr) per 100 parts by mole of the main component.

Description

technical field [0001] The present invention relates generally to dielectric ceramic compositions and laminated ceramic capacitors, and in particular to KSr with tungsten bronze (tungsten bronze) type structure 2 Nb 5 o 15 A dielectric ceramic composition as a basic component, and a multilayer ceramic capacitor using the dielectric ceramic composition. Background technique [0002] A multilayer ceramic capacitor, which is the main application of the present invention, is generally manufactured as follows. [0003] First, a ceramic substrate containing a dielectric ceramic raw material is prepared, and a conductive material constituting internal electrodes is applied to the surface in a desired pattern. [0004] Next, a plurality of ceramic substrates containing the ceramic substrates added with the above-mentioned conductive material are stacked and bonded by thermocompression, whereby an integrated green layered body is produced. [0005] Next, this green layered body i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/00H01B3/12H01G4/12H01G4/30
CPCC04B2235/3239C04B2235/768H01B3/12C04B2235/3206H01G4/30C04B2235/3201C04B2235/6582C04B2235/3213C04B35/495C04B2235/3279C04B2235/6584C04B2235/3203C04B35/62685C04B2235/3262C04B2235/3272C04B2235/3224C04B2235/652C04B2235/3418H01G4/1254C04B2235/3284C04B2235/3251C04B2235/3227C04B2235/6588C04B2235/3241C04B2235/3255C04B2235/3225C04B2235/3275C04B2235/3244C04B35/00H01G4/12
Inventor 竹田敏和
Owner MURATA MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com