Preparation method of estrogen specific nanometer silica gel surface molecule imprinting material

A nano-silica gel and molecular imprinting technology, which is applied in the preparation of microspheres, microcapsule preparations, chemical instruments and methods, etc., can solve the problem of the decrease of the specific adsorption capacity of the target molecule, the change of the shape and the movement of the recognition site, and the influence of the adsorption amount of MIPs, etc. problems, to achieve the effect of simple and easy-to-obtain experimental equipment, easy to repeat, save time and reagents

Inactive Publication Date: 2012-08-01
NANJING MEDICAL UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the study of molecularly imprinted polymers, due to the lack of rigidity of the organic cross-linked polymer materials used, the imprinted "holes" are prone to morphological changes and recognition site movement under the action of temperature and solvents, resulting in MIPs' inability to target molecules. Decreased specific adsorption capacity
On the other hand, in the synthesis process of molecularly imprinted polymers, because the template molecules are inside the polymer material, the removal of the template molecules is not complete, and there is generally a problem of 3-5% residues, which not only affects the adsorption capacity of MIPs, but also affects the adsorption capacity of MIPs. Severe interferences in trace analysis

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of estrogen specific nanometer silica gel surface molecule imprinting material
  • Preparation method of estrogen specific nanometer silica gel surface molecule imprinting material
  • Preparation method of estrogen specific nanometer silica gel surface molecule imprinting material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] At room temperature, 2ml of mass concentration of 25% ammonia and 2ml of double distilled water were dissolved in 50ml of absolute ethanol, and 2.5ml of tetraethyl orthosilicate (TEOS) was added dropwise to the above mixture at a rate of 0.025ml. min -1 , 200r·min -1 The reaction was stirred for 24h. The obtained silica sol nanospheres were washed with absolute ethanol until neutral for later use.

[0029] Disperse 100mg of silica sol nanospheres with a particle size of 150nm in 50ml of toluene, add 2ml of γ-methacryloxypropyltrimethoxysilane, and react under nitrogen protection at 120°C for 16 hours. Toluene was washed 4 times by ultrasonic centrifugation at 16500r / min to obtain modified silica sol nanospheres;

[0030] Functional monomer methacrylic acid, template molecule estradiol, crosslinking agent ethylene glycol dimethacrylate and initiator azobisisobutyronitrile are dissolved in 50 milliliters of porogen toluene to make the above functional monomer The mola...

Embodiment 2

[0033] At room temperature, 2ml of mass concentration of 25% ammonia and 2ml of double-distilled water were dissolved in 50ml of absolute ethanol, and 2.5ml of tetraethyl orthosilicate (TEOS) was added dropwise to the above mixture at a rate of 0.025ml. min -1 , 200r·min -1 The reaction was stirred for 24h. The obtained silica sol nanospheres were washed with absolute ethanol until neutral for later use.

[0034] Disperse 50mg of silica sol nanospheres with a particle size of 150nm in 50ml of toluene, add 1ml of γ-methacryloxypropyl trimethoxysilane, and react under nitrogen protection at 120°C for 12 hours. Acetonitrile was ultrasonically washed three times at 16500r / min to obtain modified silica sol nanospheres;

[0035] Dissolve functional monomer methyl methacrylate, template molecule estradiol, crosslinking agent ethylene glycol dimethacrylate and initiator azobisisobutyronitrile in 50 milliliters of porogen acetone to make the above functional The molar concentration...

Embodiment 3

[0038] At room temperature, 2ml of mass concentration of 25% ammonia and 2ml of double-distilled water were dissolved in 50ml of absolute ethanol, and 2.5ml of tetraethyl orthosilicate (TEOS) was added dropwise to the above mixture at a rate of 0.025ml. min -1 , 200r·min -1 The reaction was stirred for 24h. Gained silica sol nanospheres were washed with absolute ethanol until neutral for later use.

[0039] Disperse 150mg of silica sol nanospheres with a particle size of 150nm in 50ml of toluene, add 2ml of γ-methacryloxypropyl trimethoxysilane, nitrogen protection, 120°C high temperature reaction for 12 hours, the reaction product is water, acetone Ultrasonic centrifugation and washing at 16500r / min respectively for 5 times to obtain modified silica sol nanospheres;

[0040] Functional monomer acrylamide, template molecule estradiol, crosslinking agent ethylene glycol dimethacrylate and initiator azobisisobutyronitrile are dissolved in 50 milliliters of porogen acetonitril...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a preparation method of an estrogen specific nanometer silica gel surface molecule marking material, mainly comprising three steps of surface modification of a colloidal silica sol nanosphere, polyreaction and template molecule elution. The preparation method is easy to control, required experimental facilities are simple, and a prepared nanometer colloidal silica gel molecule marking polymer has the advantages of big specific surface, high molecule binding capacity, many recognition sites, favorable molecular recognition performance and the like. An estrogen molecule marking polymer material prepared by the invention not only can be used for various ideal adsorbents or coating materials of a solid-phase extraction technology, but also can be used for preparing molecule marking sensors and chips. The invention adopting the technology is of great importance in analyzing and researching various environmental pollutant residues.

Description

1. Technical field [0001] The invention belongs to the field of new material science, and particularly relates to a preparation method of a core-shell type estrogen-specific nano silica gel surface molecular imprinting material. 2. Background technology [0002] The problem of estrogen (ES) residues is currently the focus of attention and research by governments around the world. With the rapid development of the breeding industry, the abuse of estrogen in agricultural inputs (feed and feed additives, etc.) to promote animal growth is very common. The problem of estrogen residues in aquatic products, meat, eggs and milk is becoming more and more serious. Because ES has strong physiological activity, even at extremely low concentrations (mostly at the ppt-ppb level or lower) it will have a great impact on organisms. They interfere with the normal endocrine function of human beings, change the signal transmission process in the body during development and adulthood, and thus ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/281B01J20/286B01J20/28B01J20/30B01J13/02C07J1/00
Inventor 周学敏马静袁丽华丁美娟王舒徐金慧吴晓丽李芸
Owner NANJING MEDICAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap