Composite fabric with heat-accumulation temperature-adjustment phase-change materials as well as preparation method and application thereof

A phase change material, heat storage and temperature regulation technology, applied in applications, clothing, clothing, etc., can solve the problems of phase change material leakage, reduced human comfort, and inability to uniformly regulate temperature.

Inactive Publication Date: 2012-09-26
汕头市雅培妇幼用品有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The defect of the above technology is that the phase change fiber is woven into a fabric, and the point contact combination of each thin fiber cannot be uniformly adjusted in temperature; the rupture of the microcapsule and the infiltration of the hole are very easy to cause the leakage of the phase change material; resulting in human body comfort. The feeling is greatly reduced; wrapped or impregnated phase change materials are organic polymers that are spun into chemical fibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Phase change material PEG powder intrinsic viscosity index 0.45, antioxidant 1010 or antioxidant 680 (produced by Shanghai Reagent Factory), the mixing weight ratio of the two is 100:0.6; phase change material PEG powder and high melt index PE material ( MFI: 32) The mixing weight ratio is 100:0.3; the stirring speed is 20 rpm, the screw melting temperature: 185°C, the diaphragm pressure: 60MPa, the hot roller setting temperature is 115°C, the molecular weight of the PE film raw material is 1.2 million, and the thickness 25um, composite hot pressing speed 60 m / min, hot roller pressing temperature 115 ℃, embossed film trimming width 8mm, laminated with cotton knitted fabric. Application products: suits for infants and young children, nursing clothes for the elderly and weak patients.

Embodiment 2

[0023] The intrinsic viscosity index of phase change material PEG powder particles is 0.48, antioxidant 1010 or antioxidant 680 (produced by Shanghai Reagent Factory, commercially available), the mixing weight ratio of the two is 100:0.8; PEG powder particles and high melt index PE powder mixing weight ratio 100:0.2, MFI: 40, stirring speed 25 rpm, screw melting temperature: 190°C, diaphragm pressure: 75MPa, heat setting temperature: 125°C, PE film raw material molecular weight 1.3 million, thickness 30mm , Composite hot pressing speed; 55 m / min, hot roller pressing temperature 120°C, film trimming width: 12mm, laminated with cotton woven fabric. Application products: bed sheets, quilt covers, outerwear.

Embodiment 3

[0025] The intrinsic viscosity index of phase change material PEG powder particles is 0.50, and the antioxidant 1010 (produced by Shanghai Reagent Factory), the mixing weight ratio of the two is 100:0.9; the mixing weight ratio of PEG powder particles and high melt index PE powder is 100: 0.3, MFI: 52, stirring speed: 28 rpm; screw melting temperature: 205°C; diaphragm pressure: 80MPa; heat setting temperature: 135°C; PE film raw material molecular weight: 1.25 million, thickness: 28mm; compound hot pressing speed : 50 rev / min, hot roller pressing temperature: 115°C; film trimming width: 10mm, laminated cotton knitted fabric: application products: casual wear, home wear.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a compound fabric with heat-accumulation temperature-adjustment phase-change materials as well as a preparation method and the application thereof. The composite fabric consists of three layer, phase-change materials PEG are extruded into a thin film by a threaded rod, then two PE films are compounded on and under the thin film to be extruded into a three-layer compound film, and then both ends of the three-layer compound film are cut to seal edges according to different needs of bedclothes or clothes packing courses. The compound fabric has the heat-accumulation temperature-adjustment effect of the phase-change materials, thereby having functions such as absorption, storage and release of heat energy; and in addition, the compound fabric is a novel compound fabricand is especially suitable for being used as the bedclothes and constant temperature clothes for babies and old and weak patients.

Description

technical field [0001] The present invention relates to a multi-layer polymer film and fabric composite fabric and its preparation method and application, more particularly, to a composite fabric with heat storage and temperature adjustment phase change material and its preparation method and application. Background technique [0002] The phase change fiber material suitable for bedding and clothing, the existing technology mainly includes: the phase change material is encapsulated by microcapsules, and then blended or glued into the polymer for spinning and stretching into a phase change fiber (such as Chinese patent 01817825.1); adopt composite spinning forming, the cortex is a fiber-forming high polymer, the core layer is a phase change material or a blend of phase change material and polymer, and the phase change fiber of the composite skin-core structure is spun (such as China Patent 01819240.8); Spinning porous structure fibers, impregnating the phase change liquid in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A41D31/02A47G9/02
Inventor 薛长华
Owner 汕头市雅培妇幼用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com