High-property water-based emulsion cutting fluid composite

A composition and cutting fluid technology, applied in the directions of lubricating compositions, base materials, additives, etc., can solve the problem of not finding composite anti-rust agents, etc., and achieve widened anti-rust applicability, excellent lubricity, good anti-rust retardation. Erosion effect

Active Publication Date: 2009-12-30
BOER TECH WUHAN
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the relevant literature, no report on the use of composite antirust agents based on synthetic amides has been found.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] (1), prepare pentaerythritol octadecyl fatty acid ester by known method;

[0049](2), prepare composite amide antirust agent of the present invention;

[0050] 1) Preparation of component A: polycarboxylate alkanamide

[0051] According to weight ratio, drop into 1 part of terpolymeric acid (molecular weight is about 470) and 1 part of 2,2 / ,2 / / Aminotriethanol, under stirring, at 55±5°C, reacted for about 2 hours to obtain polycarboxylated alkanamide;

[0052] 2) Preparation of component B: a mixed solution of benzotriazole and diethylene glycol butyl ether

[0053] According to the weight ratio, add 1 part of benzotriazole and 2 parts of diethylene glycol butyl ether into the container, mix and stir at room temperature until completely dissolved and become transparent;

[0054] 3) Prepare compound antirust agent

[0055] Add 10% of the mixed solution of component B benzotriazole and diethylene glycol butyl ether to 90% component A polycarboxylated alkanol amide...

Embodiment 2

[0074] (1), prepare pentaerythritol octadecyl fatty acid ester by known method;

[0075] (2), prepare composite antirust agent of the present invention;

[0076] 1) Preparation of component A: polycarboxylate alkanamide

[0077] According to the specified ratio, put 1 part of terpolymeric acid (molecular weight about 470) and 1.5 parts of 2,2 into the normal pressure steel reactor. / ,2 / / Aminotriethanol, under stirring, at 55±5°C, reacted for about 2 hours to obtain polycarboxylated alkanamide;

[0078] 2) Preparation of component B: a mixture of benzotriazole and cosolvent diethylene glycol butyl ether

[0079] According to the specified ratio, add 1 part of benzotriazole and 3 parts of diethylene glycol butyl ether into the container, mix and stir at room temperature until it is completely dissolved and becomes transparent;

[0080] 3) Prepare compound antirust agent

[0081] Add 12% of component B to 88% of component A by weight percentage, and mix and stir for 30-40...

Embodiment 3

[0098] (1), prepare pentaerythritol octadecyl fatty acid ester by known method;

[0099] (2), prepare composite antirust agent of the present invention;

[0100] 1) Preparation of component A: polycarboxylate alkanamide

[0101] Put 1 part of terpolymeric acid (molecular weight) and 2 parts of 2, 2`, 2`` amino triethanol into the normal pressure steel reaction kettle according to the specified ratio, and under stirring, at 55±5℃, the reaction is about In 2 hours, polycarboxylated alcohol amine amide was obtained;

[0102] 2) Preparation of component B: a mixture of benzotriazole and diethylene glycol butyl ether

[0103] According to the prescribed ratio, add 1 part of benzotriazole and 4 parts of diethylene glycol butyl ether into the container, mix and stir at room temperature until it is completely dissolved and becomes transparent;

[0104] 3) Preparation of composite amide antirust agent

[0105] By weight percentage, add 15% of the mixture of component B benzotriazol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a high-property water-based emulsion cutting fluid composite, belonging to the field of metalworking fluid products. The composite is a water soluble product and comprises mineral oil, pentaerythritol fatty acid synthetic esters, a compound acidamide anti-rusting agent, an emulsifier, a corrosion inhibitor, a sulfide aliphatic acid ester extreme pressure lubricant, a bactericide and a defoamer; wherein, the compound acidamide anti-rusting agent is the composite of a component A, namely polycarboxylic acid hydramine acidamide and a component B, namely a mixture of triazole and a cosolvent butyl ether diglycol, thereby obviously improving the anti-rusting property of the product and broadening the anti-rusting applicability of diverse metals. The components of the composite product of the invention are scientific and reasonable in selection and use and balanced and harmonious in proportioning, thus achieving the effects of complementary action and synergy, therefore, the water-based emulsion cutting fluid of the invention not only enjoys high lubricating property, high anti-rusting property, high emulsibility, high antibacterial ability and high stability and has long service life, but also produces no pollution to the environment, does no harm to human bodies and satisfies the requirements of high-difficulty machining on the cutting fluid.

Description

technical field [0001] The invention discloses a high-performance water-based emulsified cutting fluid composition, which belongs to the field of metal processing fluid products, and in particular relates to machine tool cutting fluid products. Background technique [0002] Cutting fluids in the traditional sense mainly include oil-based cutting fluids and water-based cutting fluids. Starting from the use of water and animal and vegetable oils, they have a long history of development in machining and are widely used. Water-based cutting fluid is characterized by fast heat dissipation and low cost. Water-based cutting fluid is divided into three categories: emulsion (Solubleoil), synthetic cutting fluid (Synthetics) and semi-synthetic cutting fluid (Semi-synthetics). [0003] The classic emulsified cutting fluid is composed of emulsified oil, emulsifier, antirust agent and water. The emulsified oil used is mineral oil with a content of up to 80%. Sodium nitrate, this kind o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C10M169/04C10M111/02C10M167/00C10M101/02C10M105/38C10M141/08C10M149/18C10M141/06C10M133/44C10M129/16C10M129/28C10M135/10C10M133/08C10M129/40C10M135/06C10M133/42C10M155/02C10N40/22C10N30/06C10N30/12C10N30/16
Inventor 胡金霞
Owner BOER TECH WUHAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More