Polyether type hyperbranched epoxy resin and preparation method thereof

A technology of epoxy resin and polyether type, which is applied in the field of polyether type hyperbranched epoxy resin and its preparation, can solve the problems of complicated preparation and purification process, difficulty in product purification, and limitation of promotion and application.

Active Publication Date: 2010-12-22
BEIJING UNIV OF CHEM TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chang and Frechet (Hang-Ting Chang; Jean M.J.Frechet.Journal of Chemical Society, 1999, 121, 2313) used proton transfer method to use 3,5-dimethylol diglycidyl ether phenol as AB2 monomer synthesized polyether type hyperbranched epoxy resin, then Caiguo Gong; / sub> monomer synthesized polyester-type hyperbranched epoxy resin, but the tedious preparation and purification process of AB2 monomer limited the promotion and application of this method
Frechet and his colleagues extended the proton transfer method to commercial multifunctional monomers (Todd Emrick; Hang-Ting Chang; Jean M.J.Frechet.acromolecules, 1999, 32, 6380) (Todd Emrick; Hang-Ting Chang; JeanM. J.Frechet.Journal of Polymer Science: Part A: Polymer Chemistry, 2000, 38, 4850), synthesized aliphatic in the form of A2+B3 monomer Polyether type hyperbranched epoxy resin, however, the similar solubility of monomers, polymers and catalysts in this system makes it difficult to purify the product, and the presence of catalysts greatly affects the storage stability of the resin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyether type hyperbranched epoxy resin and preparation method thereof
  • Polyether type hyperbranched epoxy resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Example 1: 4.56g (0.02mol) of bisphenol A, 6.62g (0.02mol) of trimethylolpropane triglycidyl ether, 0.6g of tetrabutylammonium chloride, and 40ml of N,N-dimethylformamide were added In the reaction kettle, react at 60°C for 15 hours under the protection of nitrogen, precipitate in ethanol after cooling, and dry to obtain a nearly colorless hyperbranched epoxy resin. The weight-average molecular weight of the product is 8452 and the molecular weight polydispersity index is 1.66 as measured by GPC.

[0022] figure 2 It is the nuclear magnetic hydrogen spectrogram of the hyperbranched epoxy resin that embodiment 1 obtains 1 HNMR (DMSO), δ: 0.765 (-CH 2 CH 3 ), 1.28 (-CH 2 CH 3 ), 1.541(-Φ-C(CH 3 ) 2 -Φ), 2.512 (epoxy, -CH 2 )2.625 (epoxy, -CH), 3.000 (epoxy, -OCH 2 ), 3.262-3.899 (-OCH 2 , -CH(OH)), 4.960, 5.029 (-OH), 6.631-7.068 (aromatic-H). From this spectrum, the polymer has both the structures of bisphenol A and trimethylolpropane triglycidyl ether. In ad...

Embodiment 2

[0023] Embodiment 2: Bisphenol F 6g (0.03mol), pentaerythritol triglycidyl ether 6.36g (0.02mol), tetrabutylammonium hydroxide 1.5g, N, N-dimethyl sulfoxide 40ml add in the reactor, nitrogen Under protection, react at 120°C for 96 hours, after cooling, precipitate in a mixture of methanol and water (volume ratio 1:1), and dry to obtain a nearly colorless hyperbranched epoxy resin. The weight-average molecular weight of the product measured by GPC is 87452, which is more The dispersion index was 2.15.

Embodiment 3

[0024] Example 3: Add 1 g (0.01 mol) of hydroquinone, 14.4 g (0.05 mol) of trimethylolethane triglycidyl ether, 0.725 g of potassium tert-butoxide, and 40 ml of tetrahydrofuran into the reactor, and react for 40 After reacting at ℃ for 80 hours, after cooling, it was precipitated in methanol and dried to obtain a nearly colorless hyperbranched epoxy resin. The weight-average molecular weight of the product was 50915 as measured by GPC, and the molecular weight polydispersity index was 1.96.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to polyether type hyperbranched epoxy resin and a preparation method thereof. The preparation method is as follows: the polyether type hyperbranched epoxy resin is synthesized bytaking commercial dihydric phenol and polylol glycidyl ether as raw materials through a proton translocation reaction under the protection of nitrogen. All reactants are added to a reaction unit onceduring reaction, and in the reaction process, the hyperbranched epoxy resin is obtained according to the following steps in sequence: catalyst catalyzes the epoxy groups of a plurality of epoxy monomers to open epoxy rings, a phenolic hydroxyl group and secondary oxygen anion are processed by proton transfer and phenoxy oxygen anion is processed by electrophilic substitution. The hyperbranched epoxy polymer can be used in the fields of modification of environment-friendly bond with less solvent or no solvent, painting, traditional epoxy resin, and the like.

Description

Technical field: [0001] The invention relates to a polyether hyperbranched epoxy resin and a preparation method thereof. Background technique: [0002] Hyperbranched polymers have a highly branched three-dimensional ellipsoidal structure and a large number of terminal groups. Compared with traditional linear polymers, hyperbranched polymers have the characteristics of good solubility, lower melt and solution viscosity, easy film formation, and a large number of terminal groups, and are one of the research hotspots in polymer science. [0003] Epoxy resin is an important thermosetting resin variety. Due to its excellent physical and mechanical properties, electrical insulation properties, chemical resistance, heat resistance and adhesive properties, it is widely used in chemical industry, light industry, water conservancy, transportation, machinery, electronics, home appliances, automobiles and aerospace industries. . New varieties of epoxy resins are also being introduced...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G59/02
Inventor 李效玉马丽杰王海侨何立凡
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com