Process for producing PET laser transfer membrane

A technology of laser transfer and manufacturing process, which is applied in printing process, process for producing decorative surface effect, decorative art, etc. It can solve the problems of easy deformation of base film, large trimming loss, low production efficiency, etc., and achieve simple process , reduce costs and improve production efficiency

Inactive Publication Date: 2009-09-23
上海宝绿包装材料科技有限公司
View PDF1 Cites 53 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the manufacturing process of BOPP laser composite film, there are problems such as easy deformation of the base film, large cutting edge loss, slow molding speed, low production efficiency, and the base film cannot be recycled after composite printing, which is not environmentally friendly; the secondary coating PET laser transfer film The advanced manufacturing process requires two coatings, that is, first coat a release layer and then coat an information layer to achieve the functions of peeling and molded imaging, so there are also problems such as low production efficiency and easy deformation of the base film.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for producing PET laser transfer membrane
  • Process for producing PET laser transfer membrane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] see figure 1 Be process flow chart of the present invention and figure 2 Shown in the structure schematic diagram of laser transfer film of the present invention, a kind of manufacturing process of PET laser transfer film, take PET film as transfer base film, be coated with laser transfer coating on it, mainly comprise coating, molding, aluminizing, Cutting and other several processes, including the following steps:

[0034] The first step: On the PET transfer base film (the surface dyne value is 38-42 dynes), use an anilox roller to coat the laser transfer coating once to form a coating. The coating viscosity of the laser transfer coating is 4# Cai En The cupping test is 7-9S, and the thinner is added to the paint several times. The thinner is a mixed solvent of butanone: n-propyl ester (mass ratio) of 4:1. The dry coating amount is: 1.0-1.2 for offset printing products. g / m 2 , gravure printing products are 1.2 ~ 1.4g / m 2 , the anilox roller is an anilox roller w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a process for producing a PET laser transfer membrane. A PET membrane is used as a basement transfer membrane, and laser transfer pigment is coated and spread on the PET membrane. The method includes the following steps: a laser transfer pigment is coated and spread on the PET basement transfer membrane by an anilox roll at one step to form a coating layer, and a precoating membrane can be formed after the operation of drying is carried out; the precoating membrane is processed by the operation of laser mould pressing, and interference figures on a laser slab are printed on the coating layer of the precoating membrane by heat pressing so as to form a mould pressing membrane; and aluminum is coated on the mould pressing membrane, an aluminum layer is formed on an information layer, and the PET laser transfer membrane can be prepared, wherein the pigment includes thermoplastic acroid resin and cellulose acetate. The process has the advantages that the special singly coated laser transfer pigment and the unique manufacture process control are selected, and the entire process is simple, novel, stable and reliable. As the laser mould pressing transfer coating layer has the properties of easy mould pressing, favorable stripping, and the like, the operation of coating just needs to be carried out for one time, and therefore the production efficiency can be greatly improved. After being transferred and stripped, the aluminum coated membrane can be recycled to be repeatedly used for many times, and therefore cost can be greatly reduced; and the PET laser transfer membrane is the environmentally friendly anti-counterfeit laser material for packaging and printing.

Description

technical field [0001] The invention relates to the technical field of packaging and printing, in particular to a manufacturing process of a PET laser transfer film for packaging and printing. Background technique [0002] The general laser film for packaging and printing is mainly BOPP laser composite film or secondary coated PET laser transfer film. Due to the manufacturing process of BOPP laser composite film, there are problems such as easy deformation of the base film, large cutting edge loss, slow molding speed, low production efficiency, and the base film cannot be recycled after composite printing, which is not environmentally friendly; the secondary coating PET laser transfer film The advanced manufacturing process requires two coatings, that is, coating a release layer first, and then coating an information layer, in order to achieve the functions of peeling and molding imaging, so there are also problems such as low production efficiency and easy deformation of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B41M5/025B41M3/12B05D7/24B05D3/02B05D3/12B44C1/24C09D133/00
Inventor 王宝金张雪飞
Owner 上海宝绿包装材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com