A technology of alloy materials and edge banding, which is applied in the field of alloy material edge banding, can solve problems such as insufficient rigidity of edge banding, damage to human health, damage to brain cells, etc., and achieve superior product performance, low cost, and low cost of materials. little effect

Inactive Publication Date: 2010-11-03
XIONG YI PLASTIC PROD CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The edge bands commonly used in home decoration are generally divided into log edge bands and traditional polyvinyl chloride (PVC) edge bands. The log edge bands are simple to make, but the cost is expensive. In order to protect forest resources, countries restrict the felling of trees, which limits the source of raw wood edge banding; for this reason, PVC is used instead of log skin as the main raw material for making edge banding; due to the defects of the PVC material itself, the edge banding The rigidity of the product is not good enough; and most of them use heavy metal salt stabilizers, especially lead-based stabilizers; heavy metals such as lead can damage human brain cells, cause cancer and mutation, and have serious damage to human health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] An alloy material edge banding, which comprises the following components in parts by weight:

[0046] 100 parts polyvinyl chloride

[0047] ABS 50 parts

[0048] Calcium carbonate 10 parts

[0049] Calcium stearate 5.6 parts

[0050] Zinc stearate 2.4 parts

[0051] Dioctyl phthalate 6 parts

[0052] Chlorinated polyethylene 4 parts

[0053] 2.5 parts of stearic acid

[0054] 2 parts styrene

[0055] 2 parts polyacrylate

[0056] The preparation method of this embodiment is: the above-mentioned amount of polyvinyl chloride, ABS, calcium carbonate, calcium stearate and zinc stearate composite stabilizer, chlorinated polyethylene reinforcing agent, stearic acid lubricant, styrene Modifier, polyacrylate processing aid, put into the mixing equipment and stir, the stirring speed is kept at 150 rpm, the stirring time is controlled at 15 minutes, and the temperature is kept at 50°C; add the above-mentioned amount of phthalic acid di For octyl ester plasticizer, perfor...

Embodiment 2

[0058] An alloy material edge banding, which comprises the following components in parts by weight:

[0059] PVC 200 parts

[0060] ABS 80 parts

[0061] Calcium carbonate 60 parts

[0062] 7 parts calcium stearate

[0063] 3 parts zinc stearate

[0064] Dioctyl phthalate 20 parts

[0065] Chlorinated polyethylene 16 parts

[0066] Stearic acid 5 parts

[0067] Styrene 10 parts

[0068] Polyacrylate 5 parts

[0069] The concrete preparation method of this embodiment is the same as embodiment 1.

Embodiment 3

[0071] An alloy material edge banding, which comprises the following components in parts by weight:

[0072] 100 parts polyvinyl chloride

[0073] ABS 20 parts

[0074]Calcium carbonate 10 parts

[0075] 3 parts calcium stearate

[0076] Zinc stearate 2 parts

[0077] Dioctyl phthalate 1 part

[0078] Chlorinated polyethylene 2 parts

[0079] 1 part stearic acid

[0080] 1 part styrene

[0081] 1 part polyacrylate

[0082] The concrete preparation method of this embodiment is the same as embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of composite material, in particular to a formulation of an alloy material edge banding. The formulation is to prepare PVC materials with different hardness by adding a complex calcium-zinc stabilizing agent, a strengthening agent, a lubricant, a styrene modifying agent, a processing addition agent and other substances into polyvinyl chloride. An ABS material is added into the PVC materials to improve the rigidity of the alloy material edge banding without affecting mechanical property, fire resistance, high-strength weather fastness and other physical performances of PVC, and the processing aid is added to reduce processing temperature and improve planeness of a product. The formulation has the advantages of small usage of the polyvinyl chloride, low cost and excellent product performance of the edge banding; and the product does not contain a heavy metallic salt stabilizing agent, and can protect human health from being hurt, thereby being an environment friendly product.

Description

Technical field: [0001] The invention relates to the technical field of composite materials, in particular to an alloy material edge banding strip. Background technique: [0002] The edge bands commonly used in home decoration are generally divided into log edge bands and traditional polyvinyl chloride (PVC) edge bands. The log edge bands are simple to make, but the cost is expensive. In order to protect forest resources, countries restrict the felling of trees, which limits the source of raw wood edge banding; for this reason, PVC is used instead of log skin as the main raw material for making edge banding; due to the defects of the PVC material itself, the edge banding The rigidity of the product is not good enough; and most of them use heavy metal salt stabilizers, especially lead-based stabilizers; heavy metals such as lead can damage human brain cells, cause cancer and mutagenesis, and have serious damage to human health. Invention content: [0003] The purpose of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08L55/02C08K13/02C08K5/098
Inventor 罗新勇
Owner XIONG YI PLASTIC PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap