Non-cyanide copper plating solution

A cyanide-free copper pre-plating and solution technology, applied in the field of cyanide-free copper pre-plating solution and copper pre-plating, can solve the problems of unpublished formula and composition, damage to the ecological environment, cumbersome operation and maintenance, etc., and achieve reliable coating bonding and solution Stable performance and the effect of eliminating serious pollution

Active Publication Date: 2010-10-06
江南工业集团有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the cyanide pre-plating copper electrolyte will release highly toxic cyanide in a high-temperature working environment, which is harmful to the human body and causes serious damage to the ecological environment. The national "Clean Production Promotion Law" clearly stipulates that "cyanide-containing electroplating "
At present, China is actively exploring and researching new cyanide-free electroplating processes, such as SurTec864 imported from abroad, BH580 of Guangzhou Erqing Institute, and JH-250A of Guangzhou Jinhui Company. The process range is narrow, the operation and maintenance are cumbersome, and the formula and composition are basically not published. In view of this situation, we have developed a cyanide-free pre-plating copper solution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] Recipe one

[0016] Chemical Name

[0017] Recipe two

[0018] Chemical Name

[0019] Recipe Three

[0020] Chemical Name

[0021] Formula four

[0022] Chemical Name

[0023] Chemical Name

[0024] When using the above-mentioned hydroxyorganic phosphonic acid, it must be treated with hydrogen peroxide at 1~2ml / 100g first, and then neutralized with 30%~40% chemically pure potassium hydroxide to a pH of 10, and then added in order by volume concentration. Each component constitutes the non-cyanide pre-copper plating solution of the present invention.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Cyanogen-free preplated copper solution belongs to the technical field of surface treatment electroplating. The solution adopts a nontoxic organic phosphine compound to replace cyanide as a complexing agent for the preplated copper, and is particularly suitable for preplated copper used to electroplate steel, aluminum, magnesium, zinc, titanium and titanium alloy. The cyanogen-free preplated copper solution has the following main technical characteristic that the solution consists of (a) one sort of copper sulphate, basic cupric carbonate or copper nitrate with the volume concentration of between 30 and 60 g / L; (b) one sort or two sorts of compounds selected from methylene diphosphonic acid, 1-hydroxyethylidene 1.1 diphosphonic acid and 1-hydroxybutyleneidene 1.1 diphosphonic acid with the volume concentration of between 120 and 160 g / L; (c) one sort or two sorts of compounds selected from methylamino dimethylene diphosphonic acid, hexamethylene diamine tetramethylene phosphonic acid and ethylenediamine tetramethylene phosphonic acid with the volume concentration of between 2 and 5 g / L; (d) one sort of potassium citrate, amine citrate or seignette salt with the volume concentration of between 6 and 12 g / L, and (e) polyethyleneimine alkyl slat or aliphatic amine ethoxy sulfonated substance (AESS) with the volume concentration of between 0.02 and 0.05 g / L. The cyanogen-free preplated copper solution has the characteristics of stable service performance, simple solution compositions, convenient maintenance, high safety, environmental protection, reliable plating coat binding and the like.

Description

Technical field [0001] The invention relates to a cyanide-free pre-copper plating solution, which belongs to the technical field of surface treatment electroplating. It uses a non-toxic organic phosphine compound instead of cyanide as a complexing agent for pre-plating copper, and is particularly suitable for treating steel, aluminum, magnesium, and zinc. , Pre-plated copper for titanium and its alloys for electroplating. Background technique [0002] In the background art, cyanide pre-copper plating electrolyte uses sodium cyanide or potassium cyanide as the complexing agent of copper ions, and the CN in the electrolyte - It forms a stable complex with monovalent copper ions for electrodeposition. The composition of the plating solution is simple, the maintenance is convenient, the plating adhesion is good, and there is no replacement of copper. Therefore, the cyanide pre-plating copper electrolyte is widely used in China Pre-plated copper for steel, aluminum, magnesium, zinc, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C25D3/38
Inventor 胡德意袁艳伟刘友良刘保许自强曾垂海李职模王海云徐劼钟建武张奇峰
Owner 江南工业集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products