Method of preparing manganese oxide hollow nano-sphere with large-specific surface area

A large specific surface area, hollow nano technology, applied in the field of materials, can solve the problems of limiting the application of preparation materials and small specific surface area, and achieve the effects of low production cost, large specific surface area and simple process steps

Inactive Publication Date: 2009-01-14
SHAANXI NORMAL UNIV
View PDF0 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the prepared birnessite-type manganese oxide crystals all have the disadvantage of small specific surface area, generally 20-30m2 2 / g, up to 150m 2 / g, which largely limits the application of prepared materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method of preparing manganese oxide hollow nano-sphere with large-specific surface area
  • Method of preparing manganese oxide hollow nano-sphere with large-specific surface area
  • Method of preparing manganese oxide hollow nano-sphere with large-specific surface area

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] 1. Preparation of silica nanospheres

[0035] Mix 6.0mL of ammonia water with a mass concentration of 30% and 50.0mL of absolute ethanol, control the temperature at 40°C, use a power of 240W and ultrasonic generator frequency of 40KHz for 10 minutes, and then dissolve 3.0mL of tetraethylsilane in 8 Add drops / min to the above mixed solution. The volume ratio of tetraethylsilane to ammonia water and ethanol with a mass concentration of 30% is 1:2:17. Ultrasonic treatment for 10 minutes, centrifugation at 8000 rpm for 10 minutes, the precipitate was washed with deionized water until the pH of the supernatant was 8-9, and prepared into silica nanospheres.

[0036] 2. Preparation of manganese oxide-coated silica composite nanospheres

[0037] Disperse 0.83 g of silica nanospheres in 12 mL of potassium permanganate solution with a concentration of 0.38 mol / L, the molar ratio of potassium permanganate to silica nanospheres is 1:3, and generate ultrasonic waves with a power of...

Embodiment 2

[0042]In the process step 2 of preparing manganese oxide-coated silica composite nanospheres in Example 1, 1.05 g of silica nanospheres were dispersed in 12 mL of potassium permanganate solution with a concentration of 0.38 mol / L, so that the permanganese The molar ratio of potassium phosphate and silicon dioxide nanospheres is 1:3.8, and the ultrasonic wave with a power of 240W is used for 30 minutes at a generator frequency of 40KHz, and the resulting suspension is placed in a pressure container, and the pressure container is In a homogeneous reactor, hydrothermal reaction was carried out at 130° C. for 48 hours, and the other steps of this process were the same as in Example 1. In step 3 of the process for preparing manganese oxide hollow nanospheres, 0.5 g of manganese oxide-coated silica composite nanospheres is mixed with 62.5 g of aqueous sodium hydroxide solution with a mass concentration of 20%, and the manganese oxide-coated silica composite The mass ratio of nanosph...

Embodiment 3

[0044] In the process step 2 of preparing manganese oxide-coated silica composite nanospheres in Example 1, 1.24 g of silica nanospheres were dispersed in 12 mL of potassium permanganate solution with a concentration of 0.38 mol / L, and the permanganate The molar ratio of potassium to silicon dioxide nanospheres is 1: 4.5, and with an ultrasonic generator with a power of 240W, after ultrasonic treatment at a frequency of 40KHz for 30 minutes, the resulting suspension is placed in a pressure bomb, and the pressure bomb is placed in In a homogeneous reactor, hydrothermal reaction was carried out at 200° C. for 48 hours. The other steps of this process step were the same as in Example 1. In step 3 of the process for preparing manganese oxide hollow nanospheres, 0.5 g of manganese oxide-coated silica composite nanospheres is mixed with 125 g of sodium hydroxide aqueous solution with a mass concentration of 20%, and the manganese oxide-coated silica composite nanospheres Ball and ma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

Disclosed is a preparation method of a hollow manganese oxide nanosphere of large specific surface area, comprising steps of preparing a silicon dioxide nanosphere, preparing a silicon dioxide composite nanosphere covered by manganese dioxide and preparing hollow manganese oxide nanosphere. Because the preparation method adopts the process steps, which are simple, the production cost is low; the prepared hollow manganese oxide nanosphere is tested by an X-ray diffraction instrument, a scanning electron microscope, a transmission electron microscope, a Fourier transform infrared spectrometer and a physisorption instrument; the hollow manganese oxide nanosphere belongs to natrium-manganese crystal phase and is characterized by spherical morphology, having particle sizes ranging from 300 to 450nm and large specific surface area, and can be used as electrode materials to produce electrochemical capacitors.

Description

technical field [0001] The invention belongs to the technical field of materials, and in particular relates to manganese oxide hollow nanosphere materials. Background technique [0002] The birnessite-type layered manganese oxide crystal is a kind of porous manganese oxide crystal family, which is composed of the basic unit MnO 6 The octahedron is formed by sharing edges, and the interlayer region is occupied by exchangeable cations and water molecules. Its general chemical formula is A x MnO 2 ·H 2 O (where A represents H + or metal ions, including K + 、Na + , Ca 2+ Wait). Due to its good ion exchange, catalytic and electrochemical properties, birnessite-type manganese oxide has broad application prospects in the fields of ion exchange, selective adsorption, catalysis and electrochemistry. Since the morphology of manganese oxide material affects its properties to a great extent, in recent years, the research on controlling the different morphology of layered mangane...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01G45/02
Inventor 刘宗怀唐秀花
Owner SHAANXI NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap