A kind of nano-silica sol modified exterior wall latex paint and preparation method thereof

A nano-silica sol and latex paint technology, applied in latex paint, coating, etc., can solve the problems of poor adhesion, weather resistance, and burst aging of latex paint on exterior walls, and achieve enhanced weather resistance, strong adhesion, and extremely low Effect of VOC emissions

Active Publication Date: 2011-12-07
SHENYANG SHUNFENG NEW MATERIAL CO LTD
View PDF3 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The main problem to be solved by the invention is that the exterior wall latex paint has poor adhesion and weather resistance, and is susceptible to cracking and aging caused by climate change.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of nano-silica sol modified exterior wall latex paint and preparation method thereof
  • A kind of nano-silica sol modified exterior wall latex paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The invention is a water-based latex paint for exterior walls with good performance, which can be applied by brushing, ordinary spraying, airless spraying and the like. Specific description below in conjunction with embodiment:

[0024] The formulation of nano-silica sol modified exterior wall latex paint is as follows in parts by weight:

[0025] pulping stage

[0026] water 220kg Wetting agent X-405 1 kg Modulator AMP-95 1.5 kg Dispersant SN-5040 5kg Defoamer NXZ 1.5 kg Coalescing agent TEXANOL 15kg Propylene Glycol 15kg TiO 2 150kg heavy calcium 150kg talcum powder 30kg Thickener PE-66 5kg water 25kg

[0027] High-speed dispersion sanding, enter the paint mixing stage

[0028] Styrene acrylic emulsion 296D-S 320kg Defoamer NXZ 1 kg Nano silica sol 50kg Thickener PE-667 5kg water 10kg total 1000kg

[0029] In this example,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a nanometer silica sol modified exterior wall emulsion paint. The emulsion paint comprises, by mass, 10-30% of water, 15-30% of an emulsion, 5-10% of a nanometer silica sol, 5-15% of heavy calcium, 1-3% of talc, 0.5-1.5% of propylene glycol, 5-25% of titanium dioxide, 0.05-2% of a wetting agent, 0.5-1% of an antifoaming agent, 0.1-0.5% of a dispersant, 1-2% of a thickening agent, and 0.5-2% of a film forming assistant. The preparation method comprises the following steps: dispersion grinding: adding water, powders and early assistants to a dispenser, grinding, and filtering; and post-treating: adding the emulsion, the nanometer silica sol, later water and later assistants to a dispersed slurry, and adjusting the PH value and the viscosity to prepare the emulsion paint. According to the invention, the exterior wall emulsion paint, which is prepared by completing simple technologies of dispersing, sand milling, filtering and the like, has the advantages of no pollution, low VOC (volatile organic compound) discharge, environmental protection, strong adhesion, and good storage stability, washing resistance, contamination resistance and weather resistance.

Description

technical field [0001] The invention relates to an exterior wall latex paint and a preparation method thereof, in particular to a nano-silica sol modified exterior wall latex paint with good adhesion and weather resistance and a preparation method thereof. technical background [0002] At present, there are many types of latex paints for exterior walls in the market, which generally have the characteristics of high strength, low pollution, and good film-forming properties, but there are also many problems. If there is a lack of toughness and adhesion, peeling and cracks will appear on the wall painted with ordinary exterior paint after one year. Poor erosion resistance, severe discoloration, poor oil stain resistance, especially poor weather resistance, prone to cracking in warm and cold climates. [0003] Silica sol has high activity and can react with certain salts of the substrate to form a silicate polymer compound and harden to form a film; fine particles can penetrate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D133/04C09D7/12C09D5/02
Inventor 刘春峰吕会勇陈栋杜晓宁王杨松刘佳高爱民
Owner SHENYANG SHUNFENG NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products