Electrolytic apparatus for regenerating waste acid produced by acid cleaning of stainless steel, regeneration method therefor

An electrolysis device, stainless steel technology, applied in the field of electrolysis devices for the regeneration of waste acid after pickling of stainless steel, can solve the problems of uncertain application prospects, waste of resources, secondary pollution, etc., to improve sample processing speed and efficiency, and reduce volume , The effect of easy disassembly

Inactive Publication Date: 2008-10-08
ANHUI UNIVERSITY OF TECHNOLOGY
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Obviously, these two treatment methods will cause serious pollution to the environment or cause serious waste of resources.
The literature "Review of the recovery process of cold-rolled stainless steel pickling waste acid roasting method" ("Baosteel Technology" supplementary publication in 2003) pointed out that the use of roasting method to treat waste acid is mature, but the process produces a lot of harmful gases and requires large-scale gas absorption. Equipment, there is secondary pollution, so the application prospect is not clear

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electrolytic apparatus for regenerating waste acid produced by acid cleaning of stainless steel, regeneration method therefor
  • Electrolytic apparatus for regenerating waste acid produced by acid cleaning of stainless steel, regeneration method therefor
  • Electrolytic apparatus for regenerating waste acid produced by acid cleaning of stainless steel, regeneration method therefor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Example 1: waste acid regeneration electrolysis device

[0024] Waste acid electrolysis treatment device such as figure 1 As shown, the power supply 1 is a multi-channel input and output constant voltage power supply. The negative output terminal 2 of the power supply is connected to the cathode access terminal 4 of the electrolytic cell with a wire 3, and connected to the cathode electrode 10 of the electrolytic cell. The electrode is columnar, increasing The electrolytic reaction area, the electrolytic cell 6 is a sealed cup-shaped container, with a sample inlet 7 and a sample outlet 8 at both ends, which is convenient for sample entry and product output. The access terminals 11 are connected, and the entire flow path is finally connected to the positive output terminal 13 of the power supply through a wire 12. The waste acid 9 after stainless steel pickling is added to the electrolytic cell, and the electrolytic treatment can be carried out, and the intermittent trea...

Embodiment 2

[0026] (1) if Figure 4 As shown, a single columnar graphite cathode and a filamentary platinum anode are used. The electrolyte is waste acid solution A after pickling in a large stainless steel factory in my country. The main ion concentrations are: iron ion concentration 62g / L, nickel ion concentration 1.5g / L , the concentration of chromium ion is 4g / L, the concentration of fluoride ion is 1.5mol / L, electrolyze at a constant voltage of 3.5V for 15 hours to obtain solution A1;

[0027] (2) Pass the solution A1 through a flame atomic absorption instrument, and measure the content of Fe, Ni, Cr and other ions therein by flame method or graphite furnace method; use a fluoride ion selective electrode to measure the fluoride ion content therein, and calculate the electrolytic ion removal efficiency.

Embodiment 3

[0029] (1) take by weighing 10g of anhydrous sodium sulfate, dissolve in water and dilute to 200mL, just make catalyst S;

[0030] (2) if Figure 4 As shown, a single columnar graphite cathode and a filamentary platinum anode were used to electrolyze spent acid solution A at a constant voltage of 3.5V, and catalyst S was added for 15 hours of electrolysis to obtain solution A2;

[0031] Step 3 is the same as step (2) in Example 2, and the electrolytic metal ion removal efficiency is calculated.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an electrolytic device for the waste acid regeneration after the acid etching of the stainless steel and a regeneration method, which belong to the technical field of the electrolysis process application. The electrolytic device is composed of a constant voltage and constant current power supply controlled by a computer and a plurality of electrolytic baths which are filled with waste acid after the acid etching of the stainless steel to be used as electrolyte solution, a plurality of electrodes are arranged in the electrolytic baths, a plurality of input / output constant voltage and constant current power supplies are used, a plurality of cathode electrodes and a plurality of anode electrodes in the electrolytic baths are connected in parallel or in series, the plurality of electrolytic baths are connected in series, the electrolysis is performed under the constant voltage of 3.5 V, the hydroxyl in the solution is reduced in an electrolysis way, to ensure the concentration of hydrogen ions in the solution to be increased, and simultaneously the electrolytic reduction of fluorions and nitrate ions in the solution to be avoided, thereby causing the waste acid regeneration. The electrolytic device can be used flexibly according to the physical circumstances, is easy to be cleaned, maintained and adjusted, and has wide applicability to the waste acid processing.

Description

Technical field: [0001] The invention belongs to the technical field of electrolysis technology application, and in particular relates to an electrolysis device and a regeneration method for regenerating waste acid after pickling of stainless steel. Background technique: [0002] At present, the method for treating stainless steel pickling waste liquid at home and abroad is a chemical method, that is, the method of acid and alkali neutralization is used to make fluoride ions generate some insoluble salts to precipitate, and the treated solution is directly discharged; or the vacuum distillation method is used. By adding concentrated sulfuric acid, the fluoride ions and nitrate ions in the waste acid are distilled out in the form of hydrogen fluoride and nitrogen dioxide, and then absorbed through the absorption pool. Obviously, these two treatment methods will cause serious pollution to the environment or cause serious waste of resources. The literature "Review of the recov...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23G1/36
Inventor 陈同云张王兵
Owner ANHUI UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap